Localized corrosion process of Al-Zn-Mg-Cu-Zr alloy: Transitions from pitting corrosion to intergranular corrosion
The localized corrosion mode and process dependence on ageing conditions for Al-7.82Zn-1.99Mg-2.41Cu-0.12Zr alloy were investigated. Intergranular...
-
Understanding and probing progression of localized corrosion on inner walls of steel pipelines: an overview
Corrosion poses a major threat to the safety of transportation pipelines. Therefore, it is crucial to have an in-depth understanding of corrosion...
-
The Influence of Global Corrosion Degradation on Localized Damage Detection Using Guided Waves
This paper presents the results of a numerical analysis of the influence of corrosion degradation of metal plates on the wave propagation phenomenon.... -
Correlations Between Localized Pitting Corrosion and Deflection in Reinforced Concrete Beams Subjected to Accelerated Corrosion
Corrosion is one of the main deterioration phenomena in reinforced concrete structures. This paper investigates the correlations between localized... -
Corrosion
Very few events, if any, have such a devastating effect from the point of view of structural, economical and human casualties as corrosion. Virtually... -
Localized Corrosion Damage Study and Strengthening Strategies on Orthogonal Concrete Filled Steel Tubular Column
Concrete-filled steel tubular (CFST) columns are widely used in the construction industry due to their high strength and durability. However,... -
Natural Localized Corrosion of Steel Bar in 44-Years Old Cracked RC Beam Structures Exposed to Marine Tidal Environment
The chloride-induced corrosion processes of exposed structures are very complex. Locally isolated anodically and cathodically active steel surface... -
Corrosion Theory
The corrosion of steel in concrete is a significant concern in infrastructure and construction industries. This chapter discusses the theories,... -
Localized Corrosion in Additively Manufactured Stainless Steel and Aluminum Alloys
Localized corrosion susceptibility represents a risk to the long-term performance of all materials, additively manufactured (AM) alloys included....
-
Effect of Volatile Corrosion Inhibitor Dosage Towards Top and Bottom of the Line Corrosion
The objectives of this work are to determine the emulsion tendency of VCI at varying concentrations, and the effect of VCI dosage on corrosion of X65... -
Corrosion Studies on AA7075-T7352 Alloys Under Adverse Environments
The stress corrosion cracking (SCC) resistance of AA7075-T7352 aluminum alloy is critically examined in this study to analyze its failure under... -
Pipeline Corrosion Management
Corrosion is one of the most important threats for pipeline integrity. This chapter presents methods to control external and internal corrosion that... -
Mechanisms of Corrosion of Pipelines
This chapter presents fundamental concepts regarding corrosion, from thermodynamics to kinetics issues, and showcases techniques used to determine... -
Fracture Mechanics Approach to Stress Corrosion
Stress corrosion cracking (SCC) is used as a generic term to describe any behavior in which a combination of a static load and an aggressive... -
Stress Corrosion of AA2024 Aluminium Alloy: Effects of Shot Peening in Sodium Chloride Solution
Aluminum alloy 2024 is a high-strength aluminum alloy commonly used in aerospace applications. However, it is known to be susceptible to stress... -
Time-Dependent Prediction on the Localized Corrosion of Steel Structure Using Spatial Statistical Simulation
The structural failure induced by the localized corrosion of steel members frequently occurred. In this study, a spatial statistical technique was...
-
Modelling Salt Film During Localized Corrosion of Steel in Aqueous Chloride Solution
Salt film formation is an occurrence that happens during pit growth. A new perspective on pitting corrosion has been proposed which involves salt... -
Corrosion behavior of additive-manufactured NiFeCrMo alloys in various corrosion media
To understand the corrosion performance of additive-manufactured Ni-based in various corrosion media during the actual engineering application...
-
-