Abstract
BiFeO3 (BFO), Ti-doped BFO (BFTO), and Zn-doped BFO (BFZO) thin films were deposited on Pt(111)/Ti/SiO2/Si(100) substrates by using a pulsed laser deposition method. The effects of the substitution of Zn and Ti were investigated. Increased remnant polarization (P r ) and reduced coercive electric field (2E c ) were observed in the BFZO thin film capacitor. The values of 2P r and 2E c of the BFO, BFZO, and BFTO films were 100 µC/cm2 and 678 kV/cm, 107 µC/cm2 and 540 kV/cm, and 100 µC/cm2 and 720 kV/cm, respectively. The measured leakage current density of the BFZO thin film was approximately two orders of magnitude lower than that of the BFO thin film.
Similar content being viewed by others
References
J. Wang et al., Science 299, 1719 (2003).
W. Eerenstein, F. D. Morrison, J. Dho, M. G. Blamire, J. F. Scott and N. D. Mathur, Science 307, 1230a (2005).
V. R. Palkar, J. John and R. Pinto, Appl. Phys. Lett. 80, 1628 (2002).
Y. H. Lee, J. M. Wu and C. H. Lai, Appl. Phys. Lett. 88, 042903 (2006).
J. B. Neaton, C. Ederer, U. V. Waghmare, N. A. Spaldin and K. M. Rabe, Phys. Rev. B. 71, 014113 (2005).
A. J. Jacobson and B. E. F. Fender, J. Phys. C: Solid State Phys. 8, 844 (1975).
S. V. Kiselev, R. P. Ozerov and G. S. Zhdanov, Sov. Phys. Dokl. 7, 742 (1963).
T. Zhao et al., Nature 5, 823 (2006).
J. Li, J. Wang, M. Wuttig, R. Ramesh, N. Wang and B. Ruette, Appl. Phys. Lett. 84, 5261 (2004).
F. Huang, X. Lu, W. Lin, X. Wu, Y. Kan and J. Zhu, Appl. Phys. Lett. 89, 242914 (2006).
S. R. Das, P. Bhattacharya, R. N. P. Choudhary and R. S. Katiyar, J. Appl. Phys. 99, 066107 (2006).
M. H. Lee, S. C. Lee, Y. S. Sung, M-H. Kim, W-J. Kim, D. Do, S. S. Kim, J. H. Cho, B. C. Choi and T. K. Song, J. Korean Phys. Soc. 57, 1901 (2010).
J. K. Kim, S. S. Kim, W-J. Kim, A. S. Bhalla and R. Guo, Appl. Phys. Lett. 88, 132901 (2006).
D. Do, J. W. Kim, S. S. Kim, W-J. Kim, M. H. Lee and T. K. Song, J. Korean Phys. Soc. 57, 1875 (2010).
S. J. Kim, S. H. Han, H. G. Kim, A. Y. Kim, J. S. Kim and C. I. Cheon, J. Korean Phys. Soc. 56, 439 (2010).
R. D. Shannon, Acta Crystallogr., Sect. A: Found. Crystallogr. 32, 751 (1976).
K. Saito, I. Yamaji, T. Akai, M. Mitsuya and H. Funakubo, Jpn. J. Appl. Phys. 42, 539 (2003).
X. G. Tang, J. Wang, Y. W. Zhang and H. L. W. Chan, J. Appl. Phys. 94, 5163 (2003).
P. Mills and J. L. Sullivan, J. Phys. D 16, 723 (1983).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Lee, M.H., Park, J.S., Cho, H.J. et al. Ferroelectric properties of Zn- and Ti-doped BiFeO3 thin films. Journal of the Korean Physical Society 60, 272–275 (2012). https://doi.org/10.3938/jkps.60.272
Received:
Published:
Issue Date:
DOI: https://doi.org/10.3938/jkps.60.272