Abstract
A composite plastic scintillator is prepared by uniform dispersion of organic fluorophores 2-(4-Biphenylyl)-5-(4-tert-butylphenyl)-1,3,4-oxadiazole (b-PBD) and 1,4-bis(2-methylstyryl) benzene (Bis-MSB) in epoxy resin followed by curing at room temperature. The developed scintillator is strong blue emitter (425 nm), confirmed by 365 nm UV excited Photo luminescence and beta particle (90Sr-90Y) excited Radio-luminescence characterizations. The developed scintillator is highly transparent (~ 70%) to emitted light wavelength. Moreover, the scintillator’s blue emission is appropriate for photomultiplier tube (PMT) based scintillation measurement due to its maximum peak spectral response in blue region. Alpha, beta and gamma radiation detection were performed on PMT coupled scintillators of sizes Ø50 mm × 1 mm, Ø50 mm × 5 mm and Ø50 mm × 25 mm respectively. Pulse height spectra were recorded using 1 k Multichannel analyser (MCA) using various reference radiation sources. All scintillators demonstrated promising response to the respective radiations. Absolute detection efficiency of alpha scintillator is obtained as 32% (241Am), 86% of that of standard plastic scintillator EJ-212. Beta endpoint energy and gamma Compton edges showed linear variation w.r.t. corresponding channel numbers. Detection efficiency of beta and gamma scintillator is found to be 35.7% (90Sr-90Y) and 6.7% (136Cs) respectively. The developed scintillator has potential to be used for radioactivity contamination & gamma dose rate measurement applications.
Similar content being viewed by others
Introduction
Scintillators are energy converting luminescent materials that emit ultraviolet or visible light pulses when excited by high energy particles (alpha & beta particle, protons or neutrons) or high energy photons (X-ray and Gamma radiation). A scintillation detector is realized by coupling it to a photo-detector that produces electrical pulses on absorption of these light pulses, which can be processed and correlated with incident radiation intensity and energy1. Scintillation detectors have various applications such as radiation spectrometry2, medical imaging, positron emission tomography(PET)3, Industrial radiography4, high energy physics experiments5, radioisotope identification6, homeland security7 and nuclear & radiological emergency management8. Scintillators are broadly categorized in two types (i) Inorganic scintillators and Organic scintillators. Inorganic scintillators are characterized by high stop** power due their high density (3.3 to 9.4 g/cc), high light yield and good energy resolution9,10. Single crystals11, transparent ceramics12, composites13,14 and glasses15 are the various forms of inorganic scintillators. Various inorganic single crystals of halides, oxides, silicates, aluminates and germinate single crystals are being used for radiation detection and measurement application among which NaI:Tl, CsI:Tl, LaBr3:Ce, BGO, CLYC:Ce are popular scintillators16. GYGG:Ce transparent ceramic scintillator has been emerged as alternative to single crystal due to its ease of fabrication and cost effectiveness of process17. Inorganic Ce doped silicate glass scintillator along with 6Li are used for thermal neutron detection in high temperature environment18,19.
Organic Scintillators consist of fluorescent aromatic molecules and are characterized by low density (1.03–1.2 g/cc), fast decay times (0.7–3.3 ns)20 and excellent pulse shape discrimination (PSD) capability making it highly suitable for gamma-neutron discrimination21. These scintillators can be fabricated as single crystals, liquid scintillator or plastic scintillator. Naphthalene, stilbene, anthracene are important organic single crystal scintillators. Organic liquid scintillator is solution of fluorophores such as p-terphnyl, PPO etc., in organic solvents such as benzene, xylene etc., used for low energy beta measurement22. Plastic scintillator is a solid scintillator having transparent polymer as base with primary and secondary fluorophores dissolved in it. The polymer base primarily absorbs radiation energy and subsequently transfers it to primary fluorophore molecules having emission UV range. The emitted UV light wavelength is shifted to visible range by a secondary fluorophore as wavelength shifter23 for making it suitable for PMTs. The advantage of plastic scintillator lies in its flexibility to cast in different shapes and sizes for gross counting24 and radioactive contamination monitoring applications25,26. Plastic scintillators have been modified by using multiple combinations of polymers and fluorophores as per the applications. Various plastic scintillators have been developed utilizing different polymer bases such as polyvinyl toluene (PVT)27, polystyrene (PS)28, Polymethyl Methacrylate (PMMA)29, poly(9-vinylcarbazole) (PVK)30, Polysixloxane31, Polyethylene Naphthalate (PEN)32 and Others. Generally, plastic scintillator is fabricated by starting from a monomer in which the fluorophores are dissolved and subjected to heat cycles for polymerization to obtain solid scintillator. This process of develo** plastic scintillator is time consuming and may take several days. Among resin systems, epoxy resins are transparent in nature and it can be easily cured at room temperature conditions, significantly reducing working time and temperatures requirements. Further epoxy based scintillator are more resistant to temperature and chemicals and can be casted easily in multiple forms33.
In this paper, development of epoxy based composite plastic scintillator consisting of Butyl-PBD (bPBD) as primary fluorophore (λem ~ 364 nm) and Bis-MSB as wavelength shifter or secondary fluorophore (λem ~ 425 nm)34 is presented. The developed scintillators of sizes Ø50mm × 1 mm, Ø50 mm × 5 mm and Ø50 mm × 25 mm showed promising response to alpha, beta and gamma radiation respectively.
Material and methods
Preparation of epoxy composite plastic scintillator
Fluorophores 2-(4-Biphenylyl)-5-(4-tert-butylphenyl)-1,3,4-oxadiazole (b-PBD) and 1,4-bis(2-methylstyryl) benzene (Bis-MSB) were taken in ratio 10:1, mixed and grinded using a mortar and pestle to obtain a uniform mixture. 1.1% w/w of fluorophore mixture was then added to epoxy resin in a plastic container and subsequently resin hardener was added. The solution was then stirred mechanically to disperse fluorophores uniformly in epoxy resin-hardener solution. After uniform dispersion of the fluorophores in the solution, it was then poured in Ø50 mm cylindrical moulds and for casting of 1 mm, 5 mm and 25 mm thick scintillators by controlling the volume of solution. The solution was left at room temperature for 24 h for curing to get solid composite plastic scintillators. Step wise preparation process is schematically shown in Fig. 1.
Material characterization
Photoluminescence measurements were performed using JASCO 6000 Spectro-fluorometer utilizing 150W Xe-tube UV light source. Radio-luminescence was measured by replacing UV light by 90Sr-90Y (7.74 kBq) beta radiation source as excitation source. Transmittance was investigated by using Analytical Jena Specord-900 photodiode array spectrophotometer.
Detector preparation
For detection of alpha, beta and gamma radiation, prepared scintillators of sizes Ø50mmx1mm, Ø50 mm × 5 mm and Ø50 mm × 25 mm were coupled to three Hamamatsu R-550 multi-alkali PMT using optical grade silicon grease to match the refractive index of PMT glass with epoxy composite plastic scintillator. An aluminium foil of thickness ~ 10 µm was wrapped on Beta and Gamma scintillators as reflector material for efficient collection of scintillation light. No aluminium foil is wrapped on alpha scintillator to avoid significant loss of alpha particle energy during its passage through the foil. Experimental setup used for detection of alpha, beta and gamma radiation is shown in Fig. 2 is quite similar to that of our earlier work35. Scintillator coupled PMT is connected to 1 k Multi channel analyser (MCA) (Make: Para Electronics, Model-GSpec-USB) for recording of radiation induced scintillation pulse height. MCA consists of inbuilt voltage divider of PMT, HV circuit, preamplifier and spectroscopy amplifier. The detector part was fitted in a stainless steel (SS) light tight box to prevent external light entrance during the measurement. The emitted scintillation photons, due to interaction of radiation with scintillator, were converted into electrical pulses by photo-multiplier tube. The generated pulses were further amplified by preamplifier & linear amplifier inbuilt in MCA. The amplified signals were converted to digital pulses by ADC and further plotted with respect to channel no. on a PC. The MCA was powered and controlled by the PC (Fig. 2).
Radiation measurement
Reference radiation source of various activities and energies were used for radiation measurement experiments. For alpha radiation measurement 241Am + 239Pu (13 Bq), 241Am (3700 Bq) and 239Pu (22,200 Bq) reference sources were used. For beta radiation measurement 147Pm (1.495 kBq), 60Co (17.74 kBq), 204Tl (4.32 kBq) and 90Sr-90Y (5.09 kBq) were used and for gamma measurement, 133Ba (63.63 kBq), 137Cs(48.76 kBq), 60 Co (17.487 kBq) and 22Na (23.38 kBq) were used. Scintillation pulse height spectra using alpha, beta and gamma sources were recorded for duration of 300 s at closest source to detector distance (1 mm) and analysed. All measurements were performed in ambient conditions and no vacuum was used during the measurement. Ionizing radiations primarily interact with host polymer matrix (Epoxy) and deposit their energy by ionization and excitation of host polymer molecules. Alpha and beta particles being the charged particles, directly excite the host polymer molecules whereas gamma radiation being photon, indirectly deposit its energy by generating recoiled electrons through Compton scattering, which in-turn excites the host polymer molecules. The excitation energy is subsequently transferred to primary fluorophore Butyl-PBD (b-PBD), a broad UV emitter peaked at ~ 364 nm. Due to overlap** of excitation spectra of the wavelength shifter Bis MSB and emission spectra of b-PBD, Bis-MSB absorbs UV emission from b-PBD and coverts it into visible photons of 425 nm through fluorescence process34. These visible photons finally come out of the scintillator and reach to photocathode of PMT, generating photoelectrons which get multiplied in subsequent stages of dynodes before reaching to anode to constitute an electrical pulse. The electrical pulse in amplified and processed to get a pulse height distribution with help of MCA and displayed on PC.
Results and discussions
The developed scintillator along with bare epoxy is shown in Fig. 3a in natural light and UV lamp light (365 nm). It is evident that in natural light, developed scintillator is highly transparent and in contrast with bare epoxy, strong blue emission is clearly visible in UV light, confirming the luminescent nature of the scintillator. Photoluminescence excitation and emission spectra of developed scintillator and bare epoxy are shown in Fig. 3b. Broad emission of scintillator in visible range with peak at ~ 425 nm, obtained with 365 nm UV excitation, further substantiate the blue emission shown is Fig. 3a. Further, In order to be scintillator, the developed composite must show the property of radio-luminescence i.e. to emit visible light on excitation with ionizing radiation source. 90Sr-90Y (beta radiation source) is used to excite the developed plastic scintillator and Radio-luminescence (RL) generated is measured. The RL measurement also showed the emission peaked at ~ 425 nm, which confirms the developed scintillator is responding to ionizing radiation (Fig. 3c). Transmittance measurement showed that the scintillator is transparent to visible light and transmittance to RL emitted light wavelength (425 nm) is ~ 70% (Fig. 3d).
Alpha, beta and gamma detection
Alpha radiation detection
Figure 4 shows the pulse height spectra acquired for duration of 300 s with Ø50mmx1mm epoxy composite plastic scintillator using various activity alpha sources. Pulse height spectra obtained in absence of radiation source i.e. background is also shown for comparison. Pulse height intensities are found increasing with the activity of sources. Alpha detector is sensitive enough to distinguish the pulse height intensity obtained using low activity 241Am + 239Pu source (~ 13 Bq) in contrast of the background (shown in the inset). Mono-energetic alpha particles, deposit their energy in very short range and due to transparency of the scintillator the obtained alpha pulse height distribution is narrow compared to that of beta and gamma radiation. The pulse height distribution is nearly Gaussian. Peak centroids (xc) of pulse height spectra were obtained by Gaussian fit. 239Pu and 241Am spectra peak centroid were obtained at channel no. 90 and 98 which corresponds to alpha energies 5.15 and 5.49 MeV marked for each peak on on Fig. 4. The energies mentioned on Fig. 4 are standard energies of the sources. While passing through 1 mm of air between source and detector, 88.2 keV energy is lost which is 16% of initial energy36. The difference in peaks is attributed to dependence of total number photon generated due to deposited energy of alpha particles.
Alpha particle response of epoxy composite scintillator was compared with commercial thin plastic scintillator EJ-212. Figure 5 shows the pulse height spectra obtained using EJ-212 plastic scintillator (Ø50 mmx0.25 mm) along with pulse height spectra using Ø50 mmx1mm epoxy plastic scintillator shown for comparison. Peak centroid of spectra with EJ-212 was obtained at higher channel no. ~ 394 compared to that of epoxy scintillator (channel no. ~ 98). This is attributed to higher light yield (10,000 ph/MeV) of EJ-212, that results in higher pulse amplitude and lesser thickness allows the higher transmission of generated scintillation photons. The full width at half maximum (FWHM) obtained by Gaussian fitting, found to be ~ 45.3 for epoxy plastic scintillator which is comparable to FWHM ~ 47.5 of EJ-212 (Fig. 5). The absolute detection efficiency calculated from the expression
where \({N}_{A}\) is count rate in cps due to source of activity A and \({N}_{B}\) is background count rate in cps. Count rate is obtained by integrating area under the pulse height spectrum divided by counting time t. Absolute detection efficiency obtained for epoxy plastic scintillator is ~ 32% for 241Am source (Table 1) which is 86% of EJ-212 detection efficiency ~ 37%. The thickness of epoxy scintillator is four time higher than that of EJ-212. Reduction is thickness can improve the pulse height amplitude of epoxy scintillator pulse height spectra. Preparing a scintillator of thickness less than 1 mm by casting is slightly difficult because of high viscosity of epoxy used here. However organic solvents can be used to reduce the epoxy’s viscosity making it suitable for casting ultrathin scintillator.
Beta radiation detection
Pulse height spectra acquired for duration of 300 s with Ø50 mm × 5 mm scintillator using different beta sources are shown in Fig. 6. For comparative view, spectra of low activity sources (147Pm, 204Tl) are enhanced to ten and three times respectively and that of high activity source (60Co) is reduced to half of originally acquired spectra. 147Pm pulse height spectra terminating at channel no. ~ 71, corresponds to end point energy (Eβ = 224.5 keV). 60Co (Eβ = 317 keV) has wider beta pulse height distribution and is terminating at channel no. ~ 107 along with distribution of low intensity pulses extending from channel no. 318 to 410 is observed. These pulses are due to Compton interaction of 60Co gamma radiation emitted post beta decay. As the beta end point energies are further increasing, the pulse height distributions get broadened. 204Tl (Eβ = 760 keV) and 90Sr-90Y (Eβ = 2.28 MeV) spectra terminate at channel no. 245 and 700 respectively. Unlike alpha particles, emitted beta particles are not mono-energetic but have distribution of energies with maximum possible energy as end point energy. Because of poly energetic nature of beta particles emitted from source, the pulse height spectra are broad and vary proportionally w.r.t. to end point energies of beta sources. Beta end point energies when plotted w.r.t. channel no. corresponding to beta end point energies, a straight line is obtained showing a relation between end point energy and channel no.. The slope of line ~ 3.23 keV/Channel is obtained as end point energy calibration factor (Fig. 7). The detection efficiency calculated for standard beta source 90Sr-90Y is found to be ~ 35.7% (Table 1). The effect of aluminium reflector foil on the beta energies was also studied. Energy loss of beta particles is calculated using ESTAR programme37 and tabulated in Table 2. Energy loss varies from 2.5% (241Pm) to 0.18% (90Sr-90Y).
Gamma radiation detection
Since epoxy’s (C21H25ClO5) effective atomic number is low (Z = 8.5) and gamma energies involved here are ranging from 356 to 1275 keV, Compton scattering is dominant mechanism of interaction due to high Compton cross-section38. The generated Compton electrons have range of energies depending on scattering angle of gamma photon from electrons in epoxy molecule. The maximum energy \({E}_{e}\) transferred to Compton electron by gamma photon of energy \({E}_{\gamma }\) is referred as ‘Compton edge’ which corresponds to gamma scattering at an angle of 1800. The Compton edge is given by equation
where \({m}_{0}{c}^{2}\) is electron’s rest mass. The Compton electrons excite epoxy molecules which in- turn excite the fluorophore molecules, generating the scintillations. Figure 8 shows the pulse height spectra obtained with Ø50 mm × 25 mm scintillator using various gamma sources such as 133Ba (Eγ = 356 keV), 137Cs (Eγ = 662 keV), 60Co (Av.Eγ = 1250 keV) and 22Na (Eγ = 512 keV and 1275 keV).The pulse height spectra intensity of 133Ba is reduced to half for better comparative view. Gamma Compton edge is characterized by a hump in pulse height spectra, which is proportional to energy of gamma photon as per Eq. (2). Compton edges of respective sources are clearly visible in Fig. 8, confirming the dominant Compton interaction occurring in the scintillator. The counts obtained beyond Compton edge corresponds to multiple Compton interaction and photoelectric interaction which are relatively lesser intensity compared to that of Compton edge. The calculated Compton edge energy (Table 3) is marked for each source on the pulse height spectra in Fig. 8. Figure 9 shows plot of Compton edge energy with respect to corresponding channel numbers obtained from Fig. 8. The obtained straight line shows the relation between the channel no. and Compton edge energy and slope ~ 1.92 keV/channel gives the Compton energy calibration factor. The absolute detection efficiency is obtained to be ~ 6.7% for 137Cs (Table 1).
Conclusion
Epoxy-bPBD-BisMSB composite plastic scintillator is prepared in different sizes using a cost effective solution mixing method for efficient detection of alpha, beta and gamma radiations. Radiation detectors were realized by coupling the prepared scintillators with PMT and MCA. Radiation response studies for alpha, beta and gamma radiations were performed on these detectors. Alpha pulse height spectra showed distinct peaks corresponding to different alpha energies with FWHM and detection efficiency comparable to a standard commercial scintillator EJ-212. Beta scintillator showed distinguishable beta spectra for different energies ranging from 224.5 keV to 2.28 MeV. The end point energies have linear variation with the corresponding channels, validating the spectroscopic measurement capability of the prepared detectors. Detection efficiencies ~ 32% (alpha) and ~ 35.7% (beta) enable these scintillators to be used for efficient detection of low level radioactive contaminations. Gamma spectra are broad due to low Z of epoxy base and ‘Compton edges’ obtained in pulse height spectra, validate the occurrence of dominant Compton interactions in scintillator. This Compton kinematics can be used for gamma spectroscopic applications. Also, gamma detection efficiency ~ 6.7% allows it to be used for radioactivity and dose rate measurements applications. The ease of preparation makes this suitable for large area scintillator fabrication without requirement of sophisticated infrastructure. Also these detectors combined with suitable converter material can be used for (n,α) and (n,γ) reaction based neutron detection.
Data availability
All data generated or analysed which support the finding of this study are available within the article.
References
Knoll, G. F. Radiation Detection and Measurement (Wiley, 2010).
Moszyński, M. Inorganic scintillation detectors in γ-ray spectrometry. Nucl. Instrum. Methods Phys. Res. Sect. A Accel. Spectrom. Detect. Assoc. Equip. 505, 101–110 (2003).
Lecoq, P. Development of new scintillators for medical applications. Nucl. Instrum. Methods Phys. Res. Sect. A Accel. Spectrom. Detect. Assoc. Equip. 809, 130–139 (2016).
Franco, L., Gomez, F., Iglesias, A., Vidal, F. & Ameneiro, R. Industrial radiography and tomography based on scanning linear scintillator array. Int. J. Mater. Prod. Technol. 41, 61 (2011).
Kharzheev, Y. N. Scintillation counters in modern high-energy physics experiments. Phys. Part. Nucl. 46, 678–728 (2015).
Milbrath, B. D. et al. Comparison of LaBr 3: Ce and NAI(Tl) scintillators for radio-isotope identification devices. Nucl. Instrum. Methods Phys. Res. Sect. A Accel. Spectrom. Detect. Assoc. Equip. 572, 774–784 (2007).
Corre, G., Boudergui, K., Sannie, G. & Kondrasovs, V. Neutron detection with large plastic scintillators for RPM applications. 2015 4th Int. Conf. Adv. Nucl. Instrum. Meas. Methods Appl. ANIMMA 2015 33, 1–4 (2015).
Marques, L., Vale, A. & Vaz, P. State-of-the-art mobile radiation detection systems for different scenarios. Sensors (Switzerland) 21, 1–67 (2021).
Yanagida, T. Inorganic scintillating materials and scintillation detectors. Proc. Jpn. Acad. 94, 75–97 (2018).
Van Eijk, C. W. E. Inorganic scintillators in medical imaging. Phys. Med. Biol. 47, 85–106 (2002).
Nikl, M., Vedda, A. & Laguta, V. V. Single-crystal scintillation materials. In Springer Handbook of Crystal Growth (eds Dhanaraj, G. et al.) 1663–1700 (Springer Berlin Heidelberg, 2010). https://doi.org/10.1007/978-3-540-74761-1_50.
Greskovich, C. & Duclos, S. Ceramic scintillators. Annu. Rev. Mater. Sci. 27, 69–88 (1997).
Sahani, R. M., Pandya, A. & Dixit, A. Zinc oxide/polystyrene composite based scintillator for alpha particle monitoring. Mater. Sci. Semicond. Process. 127, 105692 (2021).
Sahani, R. M., Pandya, A. & Dixit, A. ZnO- 6 LiF/polystyrene composite scintillator for thermal neutron radiation detection. Rev. Sci. Instrum. 94, 024101 (2023).
Liu, J. et al. All inorganic glass scintillators: Scintillation mechanism, materials, and applications. Laser Photonics Rev. 17, 2300006 (2023).
McGregor, D. S. Materials for gamma-ray spectrometers: Inorganic scintillators. Annu. Rev. Mater. Res. 48, 245–277 (2018).
Cherepy, N. J. et al. Transparent ceramic scintillators for gamma spectroscopy and imaging. 2017 IEEE Nucl. Sci. Symp. Med. Imaging Conf. NSS/MIC 2017 Conf. Proc. https://doi.org/10.1109/NSSMIC.2017.8533003 (2018).
Nikitin, A., Fedorov, A. & Korjik, M. Novel glass ceramic Scintillator for detection of slow neutrons in well logging applications. IEEE Trans. Nucl. Sci. 60, 1044–1048 (2013).
Guizhen, S. et al. The preparation and properties of cerium-activated lithium glass scintillators. J. Non Cryst. Solids 80, 594–599 (1986).
ELJEN Technology, Plastic scintillator products. https://eljentechnology.com/products/plastic-scintillators (2021).
Birks, J. B. & Firk, F. W. K. The theory and practice of scintillation counting. Phys. Today 18, 60 (1965).
Ling, A. C. Applications of liquid scintillation counting (Horrocks, Donald L.). J. Chem. Educ. 52, A360 (1975).
Dujardin, C. & Hamel, M. Introduction—Overview on plastic and inorganic scintillators. In Plastic Scintillator Chemistry and Applications (ed. Hamel, M.) 3–34 (Springer Nature, 2021). https://doi.org/10.1007/978-3-030-73488-6_11.
Chaudhary, H. S. et al. Indigenous plastic scintillator. Radiat. Prot. Environ. 31, 215–217 (2008).
Sahani, R. M., Chaudhary, H. S., Mahala, V. K., Senwar, K. R. & Meena, J. P. Evaluation of indigenously developed plastic scintillator sheet detector for surface radioactive contamination monitoring application. In Thirty third IARP International Conference on Development towards Improvement of radiological Survillance at Nuclear Facilities and Environment: Book of Abstracts (2018).
Parihar, A., Sahani, R. M., Mahala, V. K. & Vaijapurkar, S. G. Development of plastic scintillator based food radioactivity contamination monitoring system. In Proc. of the International Conference on Radiological Safety in Workplace, Nuclear Facilities and Environment: Book of Abstracts (2016).
Zaitseva, N. et al. Plastic scintillators with efficient neutron/gamma pulse shape discrimination. Nucl. Instrum. Methods Phys. Res. Sect. A Accel. Spectrom. Detect. Assoc. Equip. 668, 88–93 (2012).
Pla-Dalmau, A., Bross, A. D. & Mellott, K. L. Low-cost extruded plastic scintillator. Nucl. Instrum. Methods Phys. Res. Sect. A Accel. Spectrom. Detect. Assoc. Equip. 466, 482–491 (2001).
Salimgareeva, V. N. & Kolesov, S. V. Plastic scintillators based on polymethyl methacrylate: A review. Instrum. Exp. Tech. 48, 273–282 (2005).
Sato, A. et al. Photoluminescence and scintillation characteristics of Bi-loaded PVK-based plastic scintillators for the high counting-rate measurement of high-energy X-rays. RSC Adv. 11, 15581–15589 (2021).
Feygelman, V. M., Walker, J. K. & Hamon, J. P. Polysiloxane-based scintillators: 1,1,4,4-tetraphenylbutadiene as a secondary fluor. Nucl. Instrum. Methods Phys. Res. Sect. A Accel. Spectrom. Detect. Assoc. Equip. 295, 94–98 (1990).
Flühs, D., Flühs, A., Ebenau, M. & Eichmann, M. Polyethylene naphthalate scintillator: A novel detector for the dosimetry of radioactive ophthalmic applicators. Ocul. Oncol. Pathol. 2, 5–12 (2016).
Markley, F. W. Plastic scintillators from cross-linked epoxy resins. Mol. Cryst. 4, 303–317 (1968).
Berlman, I. B. Handbook of fluorescence spectra of aromatic molecules. Handb. Fluoresc. Spectra Aromat. Mol. https://doi.org/10.1016/b978-0-12-092656-5.x5001-1 (1971).
Sahani, R. M., Kumari, C., Pandya, A. & Dixit, A. Efficient alpha radiation detector using low temperature hydrothermally grown ZnO : Ga nanorod scintillator. Sci. Rep. https://doi.org/10.1038/s41598-019-47732-1 (2019).
Tarasov, O. B. & Bazin, D. LISE++: Radioactive beam production with in-flight separators. Nucl. Instrum. Methods Phys. Res. Sect B Beam Interact. Mater. Atoms 266, 4657–4664 (2008).
Berger, M. J., Coursey, J. S., Zucker, M. A. & Chang, J. Stop**-power & range tables for electrons, protons, and helium ions. NIST Stand. Ref. Database https://doi.org/10.18434/T4NC7P (2017).
Parks, J. E. The compton effect-compton scattering and gamma ray spectroscopy (2015).
Acknowledgements
Authors are grateful to Sh. R.V. Hara Prasad, OS and Director Defence Laboratory for his guidance and support during this work. Authors are thankful to Sh. A.S. Rathore, Sc ’G’, Technology Director, NRMA division for providing the necessary facilities for radiation measurement; Dr. M.K. Patra, Sc ‘F’, Group Head, MD Group for facilitating photo-luminescence measurement and Dr. Narottam Prasad, TO ‘C’ for transmittance measurement.
Author information
Authors and Affiliations
Contributions
R.M.S. conceptualized, fabricated scintillators and carried out experiments for radiation detection and prepared original manuscript and A.P. facilitated the experimental work, analysed data and reviewed the manuscript. All authors discussed the results and contributed in finalizing the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Sahani, R.M., Pandya, A. Novel epoxy-bPBD-BisMSB composite plastic scintillator for alpha, beta and gamma radiation detection. Sci Rep 14, 6531 (2024). https://doi.org/10.1038/s41598-023-45501-9
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-023-45501-9
- Springer Nature Limited