Abstract
The value of the diffusion coefficient in the liquid (D l ) is generally obtained from the measurement of composition profiles ahead of a quenched planar interface. The experimental results show significant scatter. The main reason for this scatter will be shown to be due to the presence of fluid flow in the liquid. Directional-solidification studies in the Al-Cu system have been carried out to first establish the experimental conditions required for diffusive growth. The composition profiles are then measured to obtain the values of D l for alloy compositions ranging from 4.0 to 24.0 wt pct Cu. The value of D l =2.4×10−3 mm2/s was obtained along the liquidus line, and this result is significantly smaller than the values reported in the literature, which vary from 3.0 to 5.5 × 10−3 mm2/s. It is shown that the scatter in the reported values can be correlated with the diameter of the sample used and, thus, with the fluid flow present in their experiments. Detailed experimental procedures to obtain and verify diffusive-growth conditions are outlined, and appropriate analyses of the data are discussed.
Similar content being viewed by others
References
K. Niwa, M. Shimoji, S. Kado, Y. Watanabe, and T. Yokokawa: J. Met., 1957, vol. 6, pp. 96–101.
T. Ejima, T. Yamamura, N. Uchida, Y. Matsuzaki, and M. Nikaido: J. Jpn. Inst. Met., 1980, vol. 44, p. 316.
M.P. Watson and J.D. Hunt: Metall. Trans. A, 1977, vol. 8A, pp. 1793–98.
B.N. Bhat: J. Cryst. Growth, 1975, vol. 28, pp. 68–76.
J.D. Verhoeven, E.D. Gibson, and R.I. Griffith: Metall. Trans. B, 1975, vol. 6B, pp. 475–80.
M.D. Rinaldi, R.M. Sharp, and M.C. Flemings: Metall. Trans., 1972, vol. 3, pp. 3133–38.
R.M. Jordan and J.D. Hunt: Metall. Trans., 1971, vol. 2, pp. 3401–10.
R.M. Sharp and A. Hellawell: J. Cryst. Growth, 1969, vol. 5, pp. 155–61.
D. Froschhammer, H.M. Tensi, H. Zoller, and U. Feurer: Metall. Trans. B, 1980, vol. 11B, pp. 169–71.
T. Sato and G. Ohira: J. Cryst. Growth, 1977, vol. 40, pp. 78–89.
T. Sato, K. Ito, and G. Ohira: Trans. Jpn. Inst. Met., 1980, vol. 21, pp. 441–48.
J.B. Edwards, E.E. Hucke, and J.J. Martin: Int. Metall. Rev., 1968, vol. 13, pp. 1–28.
J.D. Verhoeven: Trans. AIME, 1968, vol. 242, pp. 1937–42.
R. Trivedi, S. Liu, P. Mazumder, and E. Simsek: Sci. Technol. Adv. Mater., 2001, vol. 2, pp. 309–20.
N.A. El-Mahallawy and M.M. Farag: J. Cryst. Growth, 1978, vol. 44, pp. 252–58.
D.H. Kim and R.A. Brown: J. Cryst. Growth, 1991, vol. 114, pp. 411–34.
R.J. Schaefer and S.R. Coriell: Metall. Trans. A, 1984, vol. 15A, pp. 2109–15.
R. Trivedi, P. Mazumder, and S.N. Tewari: Metall. Mater. Trans. A, 2002, vol. 33A, pp. 3763–75.
Shan Liu, P. Mazumder, and R. Trivedi: J. Cryst. Growth, 2002, vol. 240, pp. 560–68.
R. Trivedi, H. Miyahara, P. Mazumder, and E. Simsek: J. Cryst. Growth, 2001, vol. 222, pp. 365–79.
F.R. Mollard and M.C. Flemings: Trans. AIME, 1967, vol. 239, pp. 1526–46.
W.A. Tiller, K.A. Jackson, J.W. Rutter, and B. Chalmers: Acta Metall., 1953, vol. 1, pp. 428–37.
S.R. Coriell, R.F. Boisvert, G.B. McFadden, L.N. Brush, and J.J. Favier: J. Cryst. Growth, 1994, vol. 140, pp. 139–47.
B. Caroli, C. Caroli, and L. Ramirez-Piscina: J. Cryst. Growth, 1993, vol. 132, pp. 377–88.
J.A. Warren and J.S. Langer: Phys. Rev. E, 1993, vol. 47, pp. 2702–12.
Y. Miyata: J. Jpn. Inst. Met., 1983, vol. 11, pp. 1004–09.
H.M. Tensi and C. Mackrodt: Zeit. fur Metall., 1990, vol. 81, pp. 367–72.
R. Trivedi and G.M. Pound: J. Appl. Phys., 1967, vol. 39, pp. 3569–76.
D.D. Pearson and J.D. Verhoeven: Metall. Trans. A, 1984, vol. 15A, pp. 1037–1145.
R. Trivedi and W. Kurz: in Solidification Processing of Eutectic Alloys, D.M. Stefanescu, G.J. Abbaschian, and R.J. Bayuzick, eds., AIME, Warrendale, PA, 1988, pp. 3–34.
J.D. Hunt and S.-Z. Lu: in Handbook of Crystal Growth, D.T.J. Hurle, ed., Elsevier Science, New York, NY, 1994, vol. 2, pp. 1113–66.
M.H. Burden and J.D. Hunt: J. Cryst. Growth, 1974, vol. 22, pp. 109–116.
S.R. Coriell, M.R. Cordes, W.J. Boettinger, and R.F. Sekerka: J. Cryst. Growth, 1980, vol. 49, pp. 13–28.
C. Le Marek, R. Guerin, and P. Haldenwag: J. Cryst. Growth, 1996, vol. 169, pp. 147–56.
R. Trivedi and Shan Liu: Proc. Int. Conf. on Solidification Science and Processing, B.K. Dhindaw, B.S. Murty, and S. Sen, eds., Science Publishers, Inc., Enfield, NH, USA, 2001, pp. 12–24.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Lee, J.H., Liu, S., Miyahara, H. et al. Diffusion-coefficient measurements in liquid metallic alloys. Metall Mater Trans B 35, 909–917 (2004). https://doi.org/10.1007/s11663-004-0085-6
Received:
Issue Date:
DOI: https://doi.org/10.1007/s11663-004-0085-6