Open AccessStress relaxation cracking susceptibility evaluation in 347H stainless steel welds
Stress relaxation cracking (SRC) has been reported as a dominant failure mechanism for 347H stainless steel welds at elevated service temperatures, occurring in either the heat-affected zone (HAZ) or fusion zo...