Effect of platinum on the oxide-to-metal adhesion in thermal barrier coating systems
An investigation was conducted to determine the role of Pt in a thermal barrier coating system deposited on a nickel-base superalloy. Three coating systems were included in the study using a layer of yttria-st...
-
Article
Failure of ethylene furnace outlet transfer line due to overheating
An outlet transfer line tube of an ethylene-cracking furnace failed after five years of service. The tube, made from Incoloy alloy 800H, developed cracks that penetrated the entire thickness. Optical and scann...
-
Article
Stabilization of Laves phase by silicon in a heat-resistant steel casting and its effect on creep-rupture life
-
Article
Effect of superalloy substrate composition on the performance of a thermal barrier coating system
An investigation was carried out to determine the performance of a thermal barrier coating system consisting of (ZrO2-8% Y2O3)/(Pt) on two single-crystal Ni-base superalloys. Coating/alloy behavior was studied wi...
-
Article
Comparative performance of selected bond coats in advanced thermal barrier coating systems
An investigation was carried out to determine the comparative performance of selected bond coats representing the diffusion aluminides and overlays in thermal barrier coating systems. Emphasis was placed upon ...
-
Article
Failure mechanism of a thermal barrier coating system on a nickel-base superalloy
An investigation was carried out to determine the failure mechanism of a thermal barrier coating system on an Ni-base superalloy. The coating system consisted of an outer layer of yttria-stabilized zirconia (t...
-
Article
Thermal stability of advanced Ni-base superalloys
Exposures consisting of 1 to 900 h at 1000 and 1100 °C after an ageing treatment of 16 h at 870 °C were used to study the thermal stability of selected γ′-strengthened Ni-based superalloys representing convent...
-
Article
Thermal stability of a platinum aluminide coating on nickel-based superalloys
An investigation was carried out to determine the thermal stability of a platinum aluminide coating on the directionally solidified alloy MAR M 002 and its single-crystal version alloy, SRR 99, at 800, 1000 an...
-
Article
Mechanism of carburization of high-temperature alloys
An investigation of the mechanism of gaseous carburization in a reducing environment was conducted for selected Fe- and Ni-base alloys. Carburization kinetics were measured as functions of temperature in the r...
-
Article
Energy dispersive X-ray fluorescence analysis of chloride in reforming catalysts
A relatively less expensive Phillips PV 9500/SY 585 automatic energy dispersive X-ray fluorescence (EDXFR) spectrometer with rhodium target, was modified using a commercial kitchen aluminium wrap** foil filt...
-
Article
Effect of Ni3Nb precipitation on the corrosion resistance of Inconel alloy 625
-
Article
Effect of long-range ordering on the corrosion properties of an Ni-Mo alloy
A correlation was made between long-range ordering to Ni4Mo (A4 → D1a superlattice) in a Ni-28wt % Mo alloy and its corrosion properties. Emphasis was placed upon the effects of ordering on: (i) microchemical com...
-
Article
Ageing characteristics of a duplex stainless steel