Article
The corrosion of welded joints of 16GS + 08Kh13 bimetal, made of the specimens cut out from a column after the long-term operation
Corrosion-electrochemical investigations into bimetals are conventionally carried out on samples with the carrying layer preliminarily removed. In this work, the liability of welded joints to HSC without remov...
-
Article
Weldability and changes in the physicomechanical properties of welded joints
The new definition of weldability takes into account its dependence on the degree of degradation of the material, and this characteristic can be calculated as an integral parameter. We give examples of the deg...
-
Article
Effect of heat treatment on the resistance of a dispersion hardening nickel alloy to hydrogen embrittlement
-
Prolonged immersion of the alloy in an atmosphere of hydrogen and the magnitude of loading both influence the...
-
-
Article
Corrosion-resistant nickelless steel 04Kh19AFT
-
Article
Features of the structure and properties of high-silicon corrosion-resistant steels and their weld joints
-
Intergranular corrosion in austenitic high-silicon steels is caused by the precipitation in tempering at the ...
-
-
Article
Effect of the dimensions of the specimens on the accuracy of determination of the cracking resistance of high-alloy steels
-
Article
Fracture toughness of two-phase joints at 77°K
-
Article
Low-temperature cyclic crack resistance of weld joints of Fe-Cr-Ni and Fe-Cr-Mn steels
-
Article
Temperature relationship of the retarded fracture process of VNS-2 maraging steel
-
Article
Effect of the structure of steel 03Kh13AG19 on propagation of fatigue cracks at normal and low temperatures
-
Article
Effect of alloying of the seam metal on the properties of weldments in invar alloys
-
Alloys of iron with 36–42% Ni have good weldability and high physicomechanical properties at 4.2–293°K.
...
-
-
Article
Mechanical properties of weld seams in austenitic steels at +20 to −296°C
The ultimate tensile strength and proof stress at Iow temperatures are lower in the weld seam than in the base metal of austenitic stainless steels. The differences were particularly large in steels Kh21N5AG7 ...
-
Article
Corrosion resistance of steels with a low concentration of nickel in aggressive media
-
We have shown that the resistance of homogeneous ferritic—austenitic stainless steels to pitting corrosion is...
-
-
Article
Corrosion resistance of welded joints of 0Kh21N6M2T steel
-
Direct x-ray spectral microanalysis showed that the main alloyed elements are distributed between the α- and ...
-