Article
Effects of Hydrogen Charging Time and Pressure on the Hydrogen Embrittlement Susceptibility of X52 Pipeline Steel Material
The effects of hydrogen charging time and pressure on the hydrogen embrittlement (HE) susceptibility of X52 pipeline steel material are studied by slow strain rate tensile tests. The fracture morphologies of t...
-
Article
Effects of Temperature on Fretting Corrosion Between Alloy 690TT and 405 Stainless Steel in Pure Water
In pressurized water reactor, fretting corrosion has become the main reason for the failure of 690TT heat exchanger tubes. The effect of temperature on the fretting corrosion behavior between 690TT tube and 40...
-
Article
Microstructure, Residual Strain and Stress Corrosion Cracking Behavior in 316L Heat-Affected Zone
Austenitic stainless steels are usually chosen to make many components of nuclear power plants (NPPs). However, their microstructure in the heat-affected zone (HAZ) will change during the welding process. Some...
-
Article
Oxidation and Electrochemical Behavior of Monolayer-Graphene-Coated Copper in Simulated Primary Water
In high-temperature and high-pressure water, traditional anticorrosion approaches are not suitable to be used to protect structural materials from oxidation and corrosion. In this study, monolayer graphene was...