Phase Transformations in Co-Ni-Cr-W Alloys During High Temperature Exposure to Steam Environment
Three model alloys, Co-10Ni-20Cr-15W, Co-30Ni-20Cr-15W and Ni-20Cr-15W (all in wt.%) were investigated in Ar-50%H2O at 700 and 750 °C for up to 3000 h reaction. The results showed the formation of thin chromia sc...
-
Article
Predicting Oxidation-Limited Lifetime of Thin-Walled Components of NiCrW Alloy 230
Using alloy 230 as an example, a generalized oxidation lifetime model for chromia-forming Ni-base wrought alloys is proposed, which captures the most important damaging oxidation effects relevant for component...
-
Article
Effect of SO2 Addition on Air Oxidation Behavior of CM247 and CMSX-4 at 1050°C
In the present work, the oxidation behavior of two commercial Ni-base superalloys, CMSX-4 and CM247, in synthetic air with and without 2 vol.% SO2 at 1050°C has been studied. The corrosion reactions in the presen...
-
Article
Effect of Specimen Thickness on Microstructural Changes During Oxidation of the NiCrW Alloy 230 at 950–1050°C
An accurate procedure for predicting oxidation-induced damage and lifetime limits is crucial for the reliable operation of high-temperature metallic components in practical applications. In order to develop a ...
-
Article
Boron Depletion in a Nickel Base Superalloy Induced by High Temperature Oxidation
The conventionally cast Ni-base superalloy Rene 80 containing 90 wt ppm boron was oxidized in synthetic air at 850–1,050 °C for times up to 100 h. Extensive microstructural studies using GD-OES and SEM/WDX/EBS...