Abstract
Defect scattering is well known to suppress thermal transport. In this study, however, we perform both molecular dynamics and Boltzmann transport equation calculations, to demonstrate that introducing defect scattering in nanoscale heating zone could surprisingly enhance thermal conductance of the system by up to 75%. We further reveal that the heating zone without defects yields directional nonequilibrium with overpopulated oblique-propagating phonons which suppress thermal transport, while introducing defects redirect phonons randomly to restore directional equilibrium, thereby enhancing thermal conductance. We demonstrate that defect scattering can enable such thermal transport enhancement in a wide range of temperatures, materials, and sizes, and offer an unconventional strategy for enhancing thermal transport via the manipulation of phonon directional nonequilibrium.
Similar content being viewed by others
Introduction
Engineering thermal transport has long been an important scientific endeavor with fundamental and practical interests1. Defects in materials are well known to introduce excessive scattering and suppress thermal transport2,3,4. Defect engineering is thus widely applied for develo** low thermal conductivity materials5,6. On the other hand, when seeking high thermal conductivity materials, reducing defect scattering is sought, usually by growing high-quality crystalline structures or through isotope purification7,8.
In this study, we find that, counterintuitively, defect scattering could enhance thermal conductivity at nanoscale. We first adopt molecular dynamics (MD) simulations to demonstrate that introducing defect scattering in the heating zone can enhance thermal transport in the ballistic regime, i.e., when the characteristic length is smaller than the phonon mean free path. With an analysis based on the phonon Boltzmann transport equation (BTE), we show that the defect-free volumetric heating zone overpopulates oblique-propagating phonons, while introducing defects would redirect phonons randomly to restore directional equilibrium, thereby enhancing thermal conductance. Such a mechanism exists for a wide range of temperatures, sizes, and materials. Such findings provide new insights into directional nonequilibrium phonon transport and can extend our current strategies for manipulating thermal transport.
Results and discussion
Defect scattering leads to enhanced phonon transport
In this study, we consider a typical one-dimensional system where a thin film is sandwiched between an adiabatic boundary and a heat sink, as shown in Fig. 1a. Heat generation occurs in a thin heating zone near the adiabatic boundary. Note that such a system is quite similar to a transistor9, in which heat is generated in a nanometer-thin channel region by electron scattering. To model such a system, we first adopt the MD simulation. The advantage of MD is that it includes almost all the nanoscale thermal transport physics, except for its classical nature10,11. Figure 1b illustrates the simulation cell of the system in MD simulations. The phonons gain energy from the heating zone and then carry the energy to the heat sink. The regions from the top to the bottom are the fixed atoms (preventing sublimating), heating zone, substrate, fixed temperature heat sink, and fixed atoms, respectively. For demonstration purposes, the substrate is pure Si and the heating zone is Si with Ge impurities occupying random sites. The interatomic potential is the Tersoff potential12. After a convergence test (see Supplementary Note S1), a cross-sectional area of 8 × 8 -unit cells is considered and periodic boundary conditions are applied in lateral directions. In the previous study, we have demonstrated that the Nose-Hoover chain thermostat behaves like a spatially uniform heat generation and the Langevin thermostat behaves like a fixed temperature reservoir13. Therefore, we model the heat generation in the heating zone using a Nose-Hoover chain thermostat and the fixed temperature heat sink using a Langevin thermostat. The length of the heating zone Lheat and substrate Lsub are set as 10 nm and 40 nm, respectively. The cases with other lengths will be discussed later. The length of the heat sink does not affect thermal transport and is set as 2 nm, which is sufficient to avoid nonphysical behavior13,14. We also try a system without fixed atoms by using periodic boundaries and find the negligible influence of fixed atoms (see Supplementary Note S1). Sufficient time is run to achieve steady-state. All the MD simulations are performed using the Large-scale Atomic/Molecular Massively Parallel Simulator (LAMMPS) package15 (see Methods for more details).
We show the temperature profiles along the z direction in Fig. 2a, b for different concentrations of Ge in the heating zone. We test the cases around two temperatures: 300 K (Fig. 2a) and 100 K (Fig. 2b), where the heat sink temperatures are fixed at 290 K and 90 K. For all cases, the deposited power in the heating zone is fixed at 5 eV/ps. Based on common understanding, heat dissipation of pure Si system should be better than the doped system due to the excessive scattering induced by defects2. This can also be seen by our equilibrium MD (EMD) simulation results of bulk thermal conductivity of Si systems with Ge impurities: as shown in Fig. 2c, with 1% Ge, the bulk thermal conductivity is less than 10% of that of the pure Si. Hence, we would expect the temperature rise of the pure Si system should be the lowest with the fixed deposited power. Figure 2a, b, however, show unexpected trends: either around 300 K or 100 K, with the increase in defect concentration, the temperature rise in the heating zone first decreases and reaches the lowest at 1% concentration, and then increases with higher Ge concentration. This phenomenon shows that the heat dissipation of the system with 1% Ge is better than that of the pure Si system for the present problem. To quantify the performance of the heat dissipation, we define the thermal conductance \(G={q}_{z}/({T}_{heat}-{T}_{sink})\) for this system, where \({q}_{z}\) is the heat flux along the z direction in the substrate and Theat is the average temperature in the heating zone16. The definition of this thermal conductance is similar to the widely used thermal resistance in the heat dissipation of transistors, representing that, under the same heat generation, the lower the device temperature rise, the smaller the thermal resistance, and the greater the thermal conductance17,18,19. As shown in Fig. 2d, for either 300 K or 100 K, the thermal conductance first increases and then decreases with increasing defect concentrations. The maximum enhancement in thermal conductance reaches 13% with 1% Ge at 300 K and reaches 30% with 1% Ge at 100 K. This significant increase in thermal conductance largely contradicts the drastic decrease of the bulk thermal conductivity as shown in Fig. 2c.
Phonon transport mechanism
Because MD simulations study random atomic vibrations in real space, it is difficult to directly extract phonon transport physics20. In contrast, the phonon BTE based on the phonon gas model has been widely adopted for understanding thermal transport mechanisms21,22,23,24. In our previous studies, we have unified the two methods for thermal transport simulations13. Therefore, we adopt the phonon BTE to understand the mechanism behind thermal transport enhancement in this study.
At steady state, the energy-based phonon BTE with relaxation time approximation can be expressed as25:
where \(e\) is the phonon energy density25 and \({e}^{0}\) is the corresponding equilibrium energy density. \(\omega\), p, \({{{{{\bf{s}}}}}}\) represent the phonon frequency, polarization, and propagation direction, respectively. Here phonon energy density is defined as \({e}_{\omega,p,s}=\hslash \omega D(\omega,p)( {f}_{\omega,p,s}-{f}^{0}({T}_{{{{{{\rm{sink}}}}}}}))\), where \(f\) is the phonon distribution function and \({f}^{0}\) is the equilibrium distribution function. The energy-based phonon BTE can be directly derived from the distribution function-based phonon BTE25 (see Methods). The temperature of the system can be obtained from the summation of energy density over all phonon modes according to \(T=\frac{1}{4\pi }\mathop{\sum}\limits_{p}{\int }_{4\pi }{\int }_{\omega }{e}_{\omega,p,s}d\varOmega d\omega /\mathop{\sum}\limits_{p}\int {C}_{\omega,p}d\omega+{T}_{{{{{{\rm{sink}}}}}}}\)25. The heat flux of the system can be obtained from the summation of energy flux \({{{{{{\bf{e}}}}}}}_{\omega,p,{{{{{\bf{s}}}}}}}={e}_{\omega,p,{{{{{\bf{s}}}}}}}{{{{{\bf{s}}}}}}\) over all phonon modes according to \({{{{{\bf{q}}}}}}={\int }_{4\pi }\mathop{\sum}\limits_{p}{\int }_{\omega }{v}_{\omega,p}{{{{{{\bf{e}}}}}}}_{\omega,p,{{{{{\bf{s}}}}}}}d\omega d\varOmega\)25. \(\dot{Q}\) is the volumetric heat generation. \({{{{{\bf{v}}}}}}\), \(\tau\), and C are phonon group velocity, relaxation time, and heat capacity, respectively. The relaxation time in this study considers two scattering mechanisms: phonon–phonon scattering and phonon-defect scattering. According to the Matthiessen’s rule, \(1/\tau=1/{\tau }_{{{{{{\rm{ph}}}}}}-{{{{{\rm{ph}}}}}}}+1/{\tau }_{{{{{{\rm{ph}}}}}}-{{{{{\rm{defect}}}}}}}\)26,27. Using the relaxation time implies that the phonon scattering processes are isotropic, i.e., no anisotropic scattering is induced artificially. We make the following simplifications in phonon BTE calculations. (i) We adopt the gray model for phonon properties, i.e., all phonons have the same properties including group velocity, heat capacity, and relaxation time. (ii) We assume that group velocity is the speed of sound (5500 m/s for Tersoff Si)28,29. Heat capacity is the total heat capacity 2.06 \(J/{m}^{3}K\)11. (iii) In the heating zone, the relaxation time of the phonon–phonon scattering is obtained according to \({\tau }_{{{{{{\rm{ph}}}}}}-{{{{{\rm{ph}}}}}}}=3{k}_{{{{{{\rm{bulk}}}}}}}/C{v}^{2}\), where \({k}_{{{{{{\rm{bulk}}}}}}}\) is the bulk thermal conductivity. The values of phonon–phonon relaxation time are \(3.93\times {10}^{-11}\) s and \(1.30\times {10}^{-11}\) s for 100 K and 300 K, respectively. The relaxation time of phonon-defect scattering varies in a range from \({10}^{-9}\) to \({10}^{-12}\) s. (iv) All scatterings in the substrate are neglected. These simplifications can help better reveal the underlying mechanisms. The rigorous calculations that consider the mode-level phonon properties and defect scattering will be discussed later. Based on the assumptions above, the phonon BTE can be numerically solved to obtain the temperature profile and heat flux (see Methods for numerical details).
The computational domain of the phonon BTE is shown in Fig. 3a. The upper boundary is set as the specularly reflecting boundary (see Methods), a type of adiabatic boundary condition in BTE, which has been proven to be equivalent to the fixed layer of atoms in the MD simulation13. Uniform heat generation is set in a heating zone with the length of 10 nm next to the specularly reflecting boundary. The volumetric heat generation rate is fixed at 2\(\times {10}^{17}W/{m}^{3}\) for all cases; thus the heat flux in \(z\) directions is fixed at \(2\times {10}^{9}W/{m}^{2}\) according to the energy balance \(\int \dot{Q}dV=\int {{{{{\bf{q}}}}}}\cdot {{{{{\bf{n}}}}}}dA\). The substrate has a length of \({L}_{{{{{{\rm{sub}}}}}}}=\)40 nm. The bottom boundary is set as the thermalizing boundary condition, which is equivalent to the Langevin thermostat13. The thermalizing boundary condition emits phonons in their equilibrium state with a fixed temperature and absorbs all injected phonons (Fig. 3a). Such a computational domain is equivalent to the MD simulation domain as Fig. 1b. The thermal conductance results obtained using the phonon BTE are shown in Fig. 3b. In phonon BTE calculations, we find similar trends of thermal conductance as in MD simulations (Fig. 2d): the thermal conductance first increases and then decreases with decreasing phonon-defect relaxation time (increasing defect concentration), at both 100 K and 300 K.
Both MD and BTE show that introducing defect scattering can lead to enhanced thermal transport. As will be shown later, with consideration of the mode-level phonon properties, the two methods can be quantitatively matched, providing robust evidence for the accuracy of our calculations and supporting the credibility of our findings. To uncover the mechanism of this intriguing phenomenon, we first analyze how the temperature distribution varies with the phonon-defect relaxation time. Figure 4a shows the temperature distribution at 100 K for pure Si and systems with phonon-defect relaxation time of 5\(\times {10}^{-12}\) s and \({10}^{-12}\) s at 100 K. For these three cases, there is a temperature drop inside the heating zone and another temperature drop from the heating zone-substrate interface to the bottom boundary. Note that the temperature inside the substrate is constant since the scattering inside the substrate is neglected30. The temperature drop from the heating zone-substrate interface to the bottom boundary is equal to the temperature jump at the boundary in present cases. We divide the total temperature drop into two parts: the temperature drop inside the heating zone \(\varDelta {T}_{{{{{{\rm{heat}}}}}}}\) and the temperature drop from the heating zone-substrate interface to the bottom boundary \(\varDelta {T}_{{{{{{\rm{sub}}}}}}}\), i.e., temperature jump at the boundary (Fig. 4a). Figure 4b shows how these two temperature drops vary with phonon-defect relaxation time. With decreasing phonon-defect relaxation time, the temperature drop inside the heating zone \(\varDelta {T}_{{{{{{\rm{heat}}}}}}}\) increases but \(\varDelta {T}_{{{{{{\rm{sub}}}}}}}\) decreases. Therefore, the overall thermal conductance G ((\(G={q}_{z}/(\overline{\varDelta {T}_{{{{{{\rm{heat}}}}}}}}+\varDelta {T}_{{{{{{\rm{sub}}}}}}})\), where \(\overline{\varDelta {T}_{{{{{{\rm{heat}}}}}}}}\) denotes the average temperature drop inside the heating zone relative to the heating zone-substrate interface, with the calculation expressed as \({T}_{heat}-{T}_{cold}-\varDelta {T}_{{{{{{\rm{sub}}}}}}}\)) first increases due to the decreasing \(\varDelta {T}_{{{{{{\rm{sub}}}}}}}\) when phonon-defect relaxation time is large and then decreases due to the increasing \(\varDelta {T}_{{{{{{\rm{heat}}}}}}}\) when phonon-defect relaxation time becomes too small. The increase of \(\varDelta {T}_{{{{{{\rm{heat}}}}}}}\) is consistent with the previous understanding that the scattering impedes phonon transport30,31. The decreasing \(\varDelta {T}_{{{{{{\rm{sub}}}}}}}\) leads to the unexpected increase of the thermal conductance. To understand the decreasing \(\varDelta {T}_{{{{{{\rm{sub}}}}}}}\), we further examine the directional phonon energy flux.
We calculate the directional phonon energy flux distribution for pure Si and systems with phonon-defect relaxation time of 5\(\times {10}^{-12}\) s and \({10}^{-12}\) s at 100 K, as shown in Fig. 4c. One can see that for pure Si systems, phonons propagating in different directions exhibit large nonequilibrium. When the phonon defect scattering increases, the directional phonon nonequilibrium significantly reduces, leading to a more isotropic phonon energy flux distribution. To understand why this directional nonequilibrium exists and how it affects thermal transport, the transport mechanism is illustrated in Fig. 4d, e. When the scattering is rare (i.e., in the ballistic regime) inside the uniform volumetric heating zone (Fig. 4d), the phonon mode propagating oblique to the z direction (mode 2) travels a much longer distance in the heating zone than the mode propagating along the z direction (mode 1), and thus receives a much larger amount of energy. Therefore, the phonons propagating in different directions exhibit large directional nonequilibrium (Fig. 4d). Based on the definition of temperature under such directional nonequilibrium, the over-populated mode 2 will have a larger contribution to the local temperature than mode 1. On the other hand, the local heat flux is only contributed by the energy flux projected along z directions, hence mode 2 only has a small contribution to the local heat flux (Fig. 4d). If sufficient scattering is present in the heating zone (i.e., in the diffusive regime), scattering can randomly redirect phonons and restore the equilibrium directional distribution, as depicted in Fig. 4e. Now we compare the cases of Fig. 4d, e. If the heat fluxes in both cases are the same, the case in Fig. 4d will have a higher temperature than the one in Fig. 4e. This directional nonequilibrium phonon transport explains why the temperature drop in the substrate \(\varDelta {T}_{{{{{{\rm{sub}}}}}}}\) decreases with decreasing phonon-defect relaxation time. In other words, the defect-free heating zone overpopulates the oblique-propagating phonons and leads to lower thermal conductance than the equilibrium situation. Introducing defects redirects phonons randomly to restore directional equilibrium and thereby enhances thermal conductance. At 300 K, due to the smaller phonon–phonon relaxation time32, the phonon transport for pure Si is more diffusive than that at 100 K, and the directional phonon nonequilibrium is smaller for pure Si (see Supplementary Note S2). As a result, the thermal conductance enhancement is smaller at 300 K than that of 100 K (Fig. 3b). Note that ref. 33. recently utilized defects to redirect phonons and assist phonon transport through kinked nanowires, which differs in principle from this study that focused on reducing directional nonequilibrium through defect scattering. Meanwhile, previous discussions of phonon local nonequilibrium focused mainly on spectral nonequilibrium, i.e., different phonon modes are in nonequilibrium29,34,35,36. This work introduces a different type of local nonequilibrium, i.e., directional nonequilibrium, to the family of phonon local nonequilibrium transport.
Mode-level phonon BTE calculations
From the simplified BTE analysis, we reveal that the enhancement of thermal conductance is due to the manipulation of directional nonequilibrium by defect scattering. To further validate the simplified BTE analysis, we conduct rigorous mode-level phonon BTE calculations without the simplifications. The input phonon properties, including the group velocity, heat capacity, and relaxation time, are obtained using the standard anharmonic lattice dynamics considering up to three-phonon scattering37. To consider the defect scattering by Ge atoms, we adopt the Tamura model38, which considers scattering caused by mass difference and is proven to be quite accurate4,26. All the lattice dynamics calculations are performed on the ALAMODE package39. To quantitatively compare the phonon BTE and MD results, we first extract phonon properties from Tersoff potential12 and assume the phonon population to be classical. Mode-level heat generation is distributed over the phonon mode according to its heat capacity13. Thermal conductance obtained from this mode-level phonon BTE calculation is compared with MD results and shown in Fig. 5a. It can be clearly seen that with rigorous calculations, quantitative agreement in conductance can be achieved between BTE and MD results (differences are less than 10%). Since the MD simulation adopts the empirical Tersoff potentials12 and takes the classical distribution of the phonon population11, it is still different from the real situation. We further obtain phonon properties from first-principles calculations and consider quantum phonon population (Bose-Einstein distribution). The obtained thermal conductance results for Si with different Ge impurity concentrations are shown in Fig. 5b. One can see that the overall trend of thermal conductance with the Ge impurity concentrations is the same as that in MD simulations and simplified BTE calculations. Therefore, we can conclude that defect scattering in this case reduces the unfavored directional nonequilibrium, hence leads to enhanced thermal transport in the system in Fig. 1 (\({L}_{{{{{{\rm{heat}}}}}}}\) = 10 nm and \({L}_{{{{{{\rm{sub}}}}}}}\)= 40 nm).
Influence factor
In the above discussions, we focus on the Si systems with fixed temperatures and sizes. To further examine the generality of directional phonon nonequilibrium, we study systems with different temperatures, sizes, and materials. We first investigate the Si systems with fixed sizes at four temperatures (400 K, 300 K, 100 K, and 50 K) and observe the thermal conductance enhancement at all temperatures (Fig. 5b). Especially, the maximum enhancement of thermal conductance reaches 61% for 50 K. The enhancement at low temperatures is important for cryogenic transistors in quantum computation and radio astronomy23,40. Figure 5c shows the thermal conductance for three different lengths of substrates (10 nm, 100 nm and 1 \(\mu\) m) with a fixed length of heating zone (10 nm) at 100 K. For all these lengths, thermal conductance enhancement by introducing defects is observed. The maximum enhancement of thermal conductance reaches 75% with a 100 nm substrate. In Fig. 5d, we fix the length of substrate (1 \(\mu\) m) and compute the thermal conductance at 100 K for three lengths of heating zone (10 nm, 100 nm and 1 \(\mu\) m). With the increasing lengths of the heating zone, the increase in thermal conductance gradually decreases and eventually disappears. The reason is that with increasing size, the phonon transport in the heating zone becomes more diffusive due to the intrinsic phonon–phonon scattering and the directional phonon nonequilibrium gradually reduces. We also investigate the thermal conductance of SiC and GaN systems, which serve as channel materials for power transistors41,42, as illustrated in Fig. 6. In SiC systems, we introduce defect scattering by randomly replacing C atoms with 14C atoms. For GaN systems, defect scattering is induced by randomly replacing Ga atoms with 71Ga atoms. Additionally, we explore the impact of 24Mg impurities in GaN and 10B impurities in SiC, as detailed in Supplementary Notes S5 and S6. Phonon properties are obtained from first-principles calculations (see Supplementary Notes S5 and S6). Our investigation encompasses varying temperatures (Fig. 6a, d), substrate lengths (Fig. 6b, e), and heating zone lengths (Fig. 6c, f). We observe thermal conductance enhancement by introducing defect scattering across different temperatures and sizes. As such, in a wide range of temperatures, sizes, and materials, directional nonequilibrium exists and can be mitigated by defect scattering to enhance thermal transport. The only requirement for the existence of this directional nonequilibrium is that the phonon transport in the heating zone is in the ballistic regime, i.e., the length of the heating zone is smaller than the phonon mean free path.
Previous studies of phonon local nonequilibrium focused mainly on spectral nonequilibrium29,34,35,36. Some studies found that in transistors or Raman measurements, optical phonons are over-populated which leads to lower thermal conductance34,35,36. Our analysis so far has assumed that mode-level heat generation is proportional to the modal heat capacity (spectral equilibrium). However, we also investigate the thermal conductance with considering the over-population of optical phonons (spectral nonequilibrium). We conduct a rigorous electron–phonon coupling calculation for Si to determine the mode-level heat generation (see Supplementary Note S7). As shown in Fig. 7a, compared with cases for heat generation with spectral equilibrium, we actually find more significant thermal conductance enhancement by introducing defect scattering for heat generation with spectral nonequilibrium. At 100 K, the maximum thermal conductance enhancement reaches 338%. The underlying mechanism is that defect scattering not only manipulates the directional nonequilibrium but also the spectral nonequilibrium (see Supplementary Note S7).
In all the aforementioned discussions, we consistently applied a specular reflection boundary condition to the upper boundary across all systems. To show the robustness of our findings, we also explored systems with diffuse reflection boundary conditions (see Methods). As illustrated in Fig. 7b, a decrease in thermal conductance enhancement is observed when compared to cases with specular boundaries. This is expected as diffuse boundary conditions are similar to defect scattering and tend to randomize the phonon directions, thereby contributing to the reduction of directional nonequilibrium. It is noteworthy that both specular and diffuse reflection boundaries can be experimentally implemented43,44, and the boundary in reality is most likely partially specular and partially diffuse. Consequently, our research offers valuable insights into optimizing thermal conductance enhancement through impurity scattering in experimental settings, with a preference for the utilization of more specular boundaries.
We have noticed another work by ref. 45. published during the peer review process of this study, which doped oxygen atoms in van der Waals crystal \({{{{{{\rm{TiS}}}}}}}_{3}\) nanoribbons to induce lattice contraction and increase Young’s modulus, leading to enhanced thermal conductivity. Distinct from inducing defects to migrate directional nonequilibrium in this study that reveals a general mechanism to enhance thermal transport, the strategy provided by ref. 45 is available for limited material systems. Nevertheless, the potential coexistence of these effects provides further viable approaches for manipulating heat transfer at the micro- and nanoscale. The observed phenomenon in this study also holds promise for experimental validation. Our system has real-world counterparts, where the volumetric heating method aligns with optical and electrical heating in experiments36,41. The corresponding heat sink corresponds to the thermal reservoir in the heat bridge method46,47. Our discussions on the influencing factors also provide guidance on maximizing the enhancement of thermal conductance through defect scattering in experiments (at lower temperatures, with smaller sizes, and with a specular upper surface).
In summary, we demonstrate that defect scattering could enhance phonon transport at the nanoscale and reveal the underlying mechanism of this phenomenon. To achieve a phonon transport enhancement by introducing defect scattering, the only requirement is that the phonon transport in the heating zone is in the ballistic regime, i.e., the length of the heating zone is smaller than the phonon mean free path. Our further and comprehensive analysis shows that the defect-free volumetric heating zone overpopulates oblique-propagating phonons, while introducing defects would redirect phonons randomly to restore directional equilibrium, thereby enhancing thermal conductance. Such a mechanism exists in a wide range of temperatures (from cryogenic temperature to above room temperature), materials (Si, SiC, GaN), and sizes (up to microns). For the cases we studied, the enhancement in thermal conduction via introducing defect scattering can be up to 75%. This work introduces a different type of local nonequilibrium, i.e., directional nonequilibrium, to the family of phonon local nonequilibrium transport, and extends our current strategies for enhancing thermal transport. Moreover, introducing defect scattering into heating region can be a simple and effective strategy to further overcome heat dissipation bottlenecks for a variety of transistors including computational architectures, power transistors, and cryogenic transistors.
Methods
Molecular dynamics simulations
All the MD simulations are performed using the Large-scale Atomic/Molecular Massively Parallel Simulator (LAMMPS) package15. In the simulation, the time step is set as 1 fs for 300 K and 0.1 fs for 100 K, respectively. The whole system is first relaxed under the NPT (constant mass, pressure, and temperature) ensemble for 3,000,000 steps, after which we build the heating zone and heat sink (the Nose-Hoover chain thermostat and the Langevin thermostat). The simulations are then run for 20,000,000 steps, while the steady state can be well achieved with the first 5,000,000 steps for all our simulated systems. We use the data recorded within the last 15,000,000 steps to determine the temperature profile and the heat flux. The heat flux values in the substrate are obtained by energy conservation48. The deposited power in the heating zone is fixed as 5 eV/ps. Since the Nose-Hoover thermostat can only control average temperature, we actually modify the target average temperature of the Nose-Hoover thermostat for different cases to ensure the fixed deposited power. In both the Langevin and Nose-Hoover chain thermostats, the re-scaling time constant is 1/100 of the time step, as recommended by a previous work14.
Phonon Boltzmann transport equation
The phonon Boltzmann transport equation is expressed as30:
where f is the phonon distribution function, f 0 is the equilibrium distribution, and \(\dot{s}\) is the source term. By defining a phonon energy density as \({e}_{\omega,p,s}=\hslash \omega D(\omega,p)({f}_{\omega,p,s}-{f}^{0}({T}_{\sin {{{{{\rm{k}}}}}}}))\), the energy-based phonon BTE can be derived as25:
\({e}^{0}\) is the corresponding equilibrium energy density, which is corresponding energy density of the equilibrium distribution f 0, which is obtained according to energy conservation25:
The temperature of the system is obtained according to (consistent with the temperature definition in MD simulation)13
The heat flux of the system is obtained according to
The specularly reflecting boundary condition for phonons with the incident direction \({{{{{{\bf{s}}}}}}}_{r}\) and the reflected direction \({{{{{\bf{s}}}}}}\) is specified by25,49
On the other hand, phonons reflected from diffusely reflecting boundaries have the same energy in each direction, i.e.,
where \({{{{{\bf{n}}}}}}\) is the exterior normal unit vector of the boundary.
The thermalizing boundary condition is expressed as13,25,49
where \({{{{{\bf{n}}}}}}\) is the exterior normal unit vector of the boundary. \({T}_{B}\) is the temperature of the thermalizing boundary condition.
In-house code based on the discrete-ordinate method and finite volume method49 is adopted to solve the phonon BTE. The propagation direction and spatial domain is discretized, and the phonon BTE is transformed into a set of algebraic equations. These algebraic equations are solved iteratively. After a convergence test, we sample 512 propagating directions and 1000 spatial meshes for all cases.
Lattice dynamics calculations
To perform the mode-level phonon BTE calculations, the phonon properties including the group velocity, heat capacity, and relaxation time are needed as input information. These parameters are obtained using the standard anharmonic lattice dynamics approach considering up to three-phonon scattering37,39. To consider the defect scattering by Ge atoms, we adopt the Tamura model38. All the lattice dynamics calculations are performed on the ALAMODE package39.
When comparing the MD and phonon BTE results, the phonon properties are extracted from the same system as the MD simulation: Si crystal with Tersoff potential12. The phonon population is assumed to be classical. We compute atomic forces for displaced configurations using the LAMMPS package15 and extract harmonic and third-order anharmonic interatomic force constants by fitting the relation between atomic forces and the displacements. A supercell of \(4\times 4\times 4\) and the second nearest atom neighbor is considered to obtain the third-order anharmonic interatomic force constants. The thermal conductivity of Si is calculated based on the single-mode relaxation time approximation method. We use \(60\times 60\times 60\) q-points to sample the Brillouin zone. The obtained values of classical thermal conductivity at 100 K and 300 K are 817 W/m-K and 272 W/m-K, which has around 10% difference with the EMD results (Fig. 1c) may due to the ignorance of higher-order scattering process or the single-mode relaxation time approximation11.
To consider more realistic situations, we extract phonon properties from first-principles calculations with the quantum phonon population (Bose-Einstein distribution). We carried out the first-principles calculations using the Quantum ESPRESSO package50 to calculate the atomic forces and extract harmonic and third-order anharmonic interatomic force constants by fitting the relation between atomic forces and the displacements. A supercell of \(4\times 4\times 4\) and the fourth nearest atom neighbor is considered to obtain the third-order anharmonic interatomic force constants. The thermal conductivity of Si is calculated based on the single-mode relaxation time approximation method. We use \(60\times 60\times 60\) q-points for all temperatures to sample the Brillouin zone. The bulk thermal conductivity of Si for different temperatures is provided in Supplementary Note S3.
In the BTE solver, we cannot directly sample phonon modes from lattice dynamics calculations due to the huge computational cost. After a convergence test, we divide the phonon frequency into 200 bins and average the properties of phonons in each bin according to49:
Data availability
The authors declare that the data supporting the findings of this study are available in the main article, Supplementary Information and Source data file. Source data are provided with this paper.
Code availability
The authors declare that the code supporting the findings of this study is available from the corresponding author upon request.
References
Cahill, D. G. et al. Nanoscale thermal transport. II. 2003–2012. Appl. Phys. Rev. 1, 011305 (2014).
Drabold, D. A. & Estreicher S. K. Theory of Defects in Semiconductors. (Springer, Berlin, 2007).
Callaway, J. & von Baeyer, H. C. Effect of point imperfections on lattice thermal conductivity. Phys. Rev. 120, 1149 (1960).
Lindsay, L., Broido, D. A. & Reinecke, T. L. Thermal conductivity and large isotope effect in GaN from first principles. Phys. Rev. Lett. 109, 095901 (2012).
Yang, N., Zhang, G. & Li, B. Ultralow thermal conductivity of isotope-doped silicon nanowires. Nano Lett. 8, 276–280 (2008).
Zhao, M. et al. Defect engineering in development of low thermal conductivity materials: a review. J. Eur. Ceram. Soc. 37, 1–13 (2017).
Qian, X., Zhou, J. & Chen, G. Phonon-engineered extreme thermal conductivity materials. Nat. Mater. 20, 1188–1202 (2021).
Chang, C. W. et al. Isotope effect on the thermal conductivity of boron nitride nanotubes. Phys. Rev. Lett. 97, 085901 (2006).
Pop, E. Energy dissipation and transport in nanoscale devices. Nano Res. 3, 147–169 (2010).
Bao, H., Chen, J., Gu, X. & Cao, B. A review of simulation methods in micro/nanoscale heat conduction. ES Energy Environ. 1, 16–55 (2018).
Gu, X., Fan, Z. & Bao, H. Thermal conductivity prediction by atomistic simulation methods: recent advances and detailed comparison. J. Appl. Phys. 130, 210902 (2021).
Tersoff, J. Modeling solid-state chemistry: Interatomic potentials for multicomponent systems. Phys. Rev. B 39, 5566 (1989).
Hu, Y. et al. Unification of nonequilibrium molecular dynamics and the mode-resolved phonon Boltzmann equation for thermal transport simulations. Phys. Rev. B 101, 155308 (2020).
Li, Z. et al. Influence of thermostatting on nonequilibrium molecular dynamics simulations of heat conduction in solids. J. Chem. Phys. 151, 234105 (2019).
Plimpton, S. Fast parallel algorithms for short-range molecular dynamics. J. Comput. Phys. 117, 1–19 (1995).
Yan, Z., Liu, G., Khan, J. M. & Balandin, A. A. Graphene quilts for thermal management of high-power GaN transistors. Nat. Commun. 3, 827 (2012).
Darwish, A. M., Bayba, A. J. & Hung, H. A. Accurate determination of thermal resistance of FETs. IEEE Trans. Microwave Theory Tech. 53, 306–313 (2005).
Pop, E., Sinha, S. & Goodson, K. E. Heat generation and transport in nanometer-scale transistors. Proc. IEEE 94, 1587–1601 (2006).
Smirnov, V. I. & Gavrikov, A. A. Thermal resistance meter for power transistors with heating power modulation. IEEE Trans. Instrum. Meas. 73, 1–9 (2024).
Li, D. & McGaughey, A. J. Phonon dynamics at surfaces and interfaces and its implications in energy transport in nanostructured materials—an opinion paper. Nanoscale Microscale Thermophys. Eng. 19, 166–182 (2015).
Xu, J. et al. Nonequilibrium phonon transport induced by finite sizes: effect of phonon-phonon coupling. Phys. Rev. B 104, 104310 (2021).
Chen, G. Thermal conductivity and ballistic-phonon transport in the cross-plane direction of superlattices. Phys. Rev. B 57, 14958 (1998).
Schleeh, J. et al. Phonon black-body radiation limit for heat dissipation in electronics. Nat. Mater. 14, 187–192 (2015).
McGaughey, A. J. & Kaviany, M. Quantitative validation of the Boltzmann transport equation phonon thermal conductivity model under the single-mode relaxation time approximation. Phys. Rev. B 69, 094303 (2004).
Loy, J. M., Murthy, J. Y. & Singh, D. A fast hybrid Fourier–Boltzmann transport equation solver for nongray phonon transport. J. Heat Transfer 135, 011008 (2013).
Xu, Q., Zhou, J., Liu, T. H. & Chen, G. Effect of electron-phonon interaction on lattice thermal conductivity of SiGe alloys. Appl. Phys. Lett. 115, 023903 (2019).
Ho, C. Y., Ackerman, M. W., Wu, K. Y., Oh, S. G. & Havill, T. N. Thermal conductivity of ten selected binary alloy systems. J. Phys. Chem. Ref. Data 7, 959–1178 (1978).
Kaiser, J. et al. Thermal transport at the nanoscale: a Fourier’s law vs. phonon Boltzmann equation study. J. Appl. Phys. 121, 044302 (2017).
Feng, T. et al. Spectral analysis of nonequilibrium molecular dynamics: spectral phonon temperature and local nonequilibrium in thin films and across interfaces. Phys. Rev. B 95, 195202 (2017).
Majumdar, A. Microscale heat conduction in dielectric thin films. J. Heat Transfer 115, 7–16 (1993).
Kaviany, M. & Kanury, A. Principles of heat transfer. Appl. Mech. Rev. 55, B100–B102 (2002).
Kittel, C. Introduction to Solid State Physics. (John Wiley & Sons, New Jersey, 1953).
Zhang, Q. et al. Defect facilitated phonon transport through kinks in boron carbide nanowires. Nano Lett. 17, 3550–3555 (2017).
Vallabhaneni, A. K., Singh, D., Bao, H., Murthy, J. & Ruan, X. Reliability of Raman measurements of thermal conductivity of single-layer graphene due to selective electron-phonon coupling: a first-principles study. Phys. Rev. B 93, 125432 (2016).
Sullivan, S. et al. Optical generation and detection of local nonequilibrium phonons in suspended graphene. Nano Lett. 17, 2049–2056 (2017).
Zobeiri, H., Hunter, N., Wang, R., Wang, T. & Wang, X. Direct characterization of thermal nonequilibrium between optical and acoustic phonons in graphene paper under photon excitation. Adv. Sci. 8, 2004712 (2021).
Gu, X., Fan, Z., Bao, H. & Zhao, C. Revisiting phonon-phonon scattering in single-layer graphene. Phys. Rev. B 100, 064306 (2019).
Tamura, S. I. Isotope scattering of dispersive phonons in Ge. Phys. Rev. B 27, 858 (1983).
Tadano, T., Gohda, Y. & Tsuneyuki, S. Anharmonic force constants extracted from first-principles molecular dynamics: applications to heat transfer simulations. J. Phys. Condens. Matter 26, 225402 (2014).
Artanov, A. A. et al. Self-heating effect in a 65 nm MOSFET at cryogenic temperatures. IEEE Transac. Electron Devices 69, 900–904 (2022).
Warzoha, R. J. et al. Applications and impacts of nanoscale thermal transport in electronics packaging. J. Electron. Packag. 143, 020804 (2021).
Tsao, J. Y. et al. Ultrawide-bandgap semiconductors: research opportunities and challenges. Adv. Electron. Mater. 4, 1600501 (2018).
George, A. et al. Thermoelectric enhancement of silicon membranes by ultrathin amorphous films. ACS Appl. Mater. Interfaces 11, 12027–12031 (2019).
Myers, T. J. et al. Smoothing surface roughness using Al2O3 atomic layer deposition. Appl. Surf. Sci. 569, 150878 (2021).
Liu, C. et al. Unexpected do** effects on phonon transport in quasi-one-dimensional van der Waals crystal TiS3 nanoribbons. Nat. Commun. 14, 5597 (2023).
Pettes, M. T., Jo, I., Yao, Z. & Shi, L. Influence of polymeric residue on the thermal conductivity of suspended bilayer graphene. Nano Lett. 11, 1195–1200 (2011).
Wang, Z. et al. Thermal transport in suspended and supported few-layer graphene. Nano Lett. 11, 113–118 (2011).
Schelling, P. K., Phillpot, S. R. & Keblinski, P. Comparison of atomic-level simulation methods for computing thermal conductivity. Phys. Rev. B 65, 144306 (2002).
Hu, Y., Shen, Y. & Bao, H. Ultra-efficient and parameter-free computation of submicron thermal transport with phonon Boltzmann transport equation. Fundam. Res. https://doi.org/10.1016/j.fmre.2022.06.007 (2022).
Giannozzi, P. et al. QUANTUM ESPRESSO: a modular and open-source software project for quantum simulations of materials. J. Phys. Condens. Matter 21, 395502 (2009).
Acknowledgements
Y.H., J.X., and H.B. acknowledge the support by the National Natural Science Foundation of China (Grant No. 52122606, H.B.). We would also like to thank Dr. **aokun Gu from Shanghai Jiao Tong University for valuable discussion on lattice dynamics calculations. The computations in this paper were run on the \(\pi\) 2.0 cluster supported by the Center for High Performance Computing at Shanghai Jiao Tong University.
Author information
Authors and Affiliations
Contributions
H.B. and Y.H. conceived and designed the research, H.B. supervised the research. Y.H. and J.X. performed numerical simulation, analyzed the data, and prepared the figures and manuscript with discussions with X.R. X.R. revised the paper. All the authors contributed to the data analysis and the preparation of the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Peer review
Peer review information
Nature Communications thanks Jie Ren and the other anonymous reviewer(s) for their contribution to the peer review of this work. A peer review file is available.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Source data
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Hu, Y., Xu, J., Ruan, X. et al. Defect scattering can lead to enhanced phonon transport at nanoscale. Nat Commun 15, 3304 (2024). https://doi.org/10.1038/s41467-024-47716-4
Received:
Accepted:
Published: