Synthesis and Physicochemical Properties of Nanopowders and Ceramics in a CeO2–Gd2O3 System
Nanopowders with a composition of (СeO2)1–x(Gd2O3)x (x = 0.03, 0.05, 0.07, and 0.10) are synthesized by the coprecipitation method using cryotechnologies. The coherent scattering region (CSR) of the powders is 10...
-
Article
Preparation of highly porous Nb x Ta1–x C ceramics from polymer-matrix composite materials based on a phenol-formaldehyde binder and low hydrated hydroxide of niobium and tantalum
Highly porous ceramics based on a niobium-tantalum carbide solid solution of composition Nb0.3Ta0.7C, with a density of 2.70 ± 0.02 g/cm3, total porosity of 77%, and compressive strength in the range 1.5–2.3 MPa ...
-
Article
Preparation of high-porous SiC ceramics from polymeric composites based on diatomite powder
High-porous SiC ceramics (density 0.50–0.58 g/cm3, porosity 82–84 %, compressive stress at break 3.7–6.3 MPa) was prepared by means of polymeric technology and natural raw material (diatomite powder, “Biosilica” ...
-
Article
Low-temperature synthesis of TaC through transparent tantalum-carbon containing gel
Thermodynamic modeling of the synthesis of tantalum monocarbide via the carbothermic reduction of tantalum(V) oxide indicates that TaC synthesis is thermodynamically plausible below 1000°C at pressures from 1 ...