Abstract
NBR/phenolic interpenetrating networks (IPNs) offer a wide variety of mechanical and physical properties at moderately high temperature. This temperature stability along with oil and fuel resistance property has made IPNs appropriate candidates for various applications. In the present work, NBR compounds containing 5, 7 and 12 phr of Novolac, as a curable phenolic resin was formulated using a two-roll mill. Low and high acrylonitrile NBR; KNB 35L and Europrene N4560 were selected in the compound and the same condition of mixing was applied in the blend preparation stage. Curing test, followed by a cooling period and the stress relaxation test were carried out consecutively and automatically in a rubber process analyzer. The samples presented various relaxation times. The relaxation curves were well estimated by Maxwell model and the Prony coefficients were determined. Furthermore, compression test was performed on the samples, so that the set or permanent deformation of each sample was measured. The results of both tests have indicated that by adding phenolic resin into the NBR matrices, the viscoelastic behavior of the compounds become more elastic, to the detriment of the viscous component. This phenomenon would be due to IPN formation in the compounds. In addition, by increasing the phenolic resin content in the compounds, the difference between maximum and minimum torque (M H − M L) value became greater, which is an indicator of higher cross-link density and IPN formation. Swelling test results confirmed more extensive cross-links in the compounds by addition of more resin into the compound.
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs13726-012-0100-8/MediaObjects/13726_2012_100_Fig1_HTML.gif)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs13726-012-0100-8/MediaObjects/13726_2012_100_Fig2_HTML.gif)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs13726-012-0100-8/MediaObjects/13726_2012_100_Fig3_HTML.gif)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs13726-012-0100-8/MediaObjects/13726_2012_100_Fig4_HTML.gif)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs13726-012-0100-8/MediaObjects/13726_2012_100_Fig5_HTML.gif)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs13726-012-0100-8/MediaObjects/13726_2012_100_Fig6_HTML.gif)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs13726-012-0100-8/MediaObjects/13726_2012_100_Fig7_HTML.gif)
Similar content being viewed by others
References
Chiang CL, Ma CCM, Wu DL, Kuan HC (2003) Preparation, characterization, and properties of novolac-type phenolic/SiO2 hybrid organic–inorganic nanocomposite materials by sol–gel method. J Polym Sci Polym Chem 41:905–913
Paul DR, Barlow JW (1979) Multiphase polymers-advances in chemistry series. ACS, Wisconsin, vol 176
Nigam V, Setua DK, Mathur GN (2001) Hybrid filler system for nitrile rubber vulcanizates. J Mater Sci 36:43–47
Horowitz J, Kosfeld R, Angew (1981) Macromolecular chemistry, vol 3. Academic Press, New York
Sasidharan Achary P, Gouri C, Ramaswamy R (2001) Reactive bonding of natural rubber to metal by a nitrile–phenolic adhesive. J Appl Polym Sci 81:2597–2608
Rifle JS, McGrath JE, Lesko JJ, Ward TC, Hedrick JC (2000) Void-free flame retardant phenolic networks: properties and processability. CS Tyberg, Virginia
Ciesielski A (1999) An introduction to rubber technology. Rapra, London
Hamed GR (2002), Materials and compound. Hamed GR (ed) Department of Polymer Science, chap 2, vol 1. The University of Akron, Akron, Ohio, pp 125–142
Minford JD (1993) Handbook of aluminium bonding technology data. Marcel Dekker, New York
Klempner D, Frisch KC, Frisch LC (1969) Topologically interpenetrating polymer networks, University of Detroit, Michigan, pp 229–246
Abele M, Buysch HJ, Schrage H, Vernaleken H (1993) Use of certain phenolic resins for reinforcing rubber vulcanizates, US Patent 5,214,100
Patel K, Desai D, Bhuva S (2009) Development and characterization of novel interpenetrating network (IPN) foams from epoxy ester and aliphatic epoxy resin. Eur J Chem 6:341–347
Bower MV, Gant VS (1994) Stress relaxation functions methods of approximation. Department of Mechanical and Aerospace Engineering of the University of Alabama, Huntsville
Dondi G, Simone A, Sangiorgi C (2007) Characterization of a crumb rubber mixture for road restraint systems. In 4th international SIIV congress, Palermo, Italy, vol. Ш, pp 174–182
Xu EDM (2009) Dry rolling friction and wear of elastomer systems and their finite element modelling. Technical University of Kaiserslautern, Kaiserslautern, pp 34–47
Jobish J, Vijayalakshmi R (2009) Mechanical properties and swelling behavior of cross-linked natural rubber/chitosan blends. Int J Polym Anal Charact 14:508–526
Karrabi M, Mohammadian-Gezaz S (2010) Study of the cure characteristics and viscoelastic behavior of styrene-butadiene rubber compounds by using a rubber process analyzer. J Vinyl Addit Technol 16:209–216
Karrabi M, Mohammadian-Gezaz S (2011) Investigation of viscoelastic and curing properties of carbon black filled SBR compounds using rubber process analyzer. Iran Polym J 20:15–27
Leblanc J (2005) An investigation on the effect of reclaimed rubber on viscoelastic properties and rheology of natural rubber. J Appl Polym Sci 95:90–106
Van der Vegt AK (2006) From polymers to plastics, VSSD, EBook. ISBN:9071301621
Leblanc J, Cartault M (2001) Advanced torsional dynamic methods to study the morphology of uncured filled rubber compounds. J Appl Polym Sci 80:2093–2104
Katerina D, Papoulia VP, Panoskaltsis NV, Kurup IK (2010) Rheological representation of fractional order viscoelastic material models. Rheol Acta 49:381–400
Roylance D (2001) Engineering viscoelasticity. Department of Materials Science and Engineering, Massachusetts Institute of Technology, Cambridge, MA
Polukoshko S, Hofmanis J (2009) Use of “CATERPILLAR”—SSA method for analysis and forecasting of industrial and economic indicators. In: Environment technology resources proceedings of the 7th international scientific and practical conference, Lavita, Rezekne, vol. II, pp 241–248
Hassani H (2007) Singular spectrum analysis: methodology and comparison. J Data Sci 5:239–257
Acknowledgments
The authors express their sincere thanks to Iran Polymer and Petrochemical Institute and also TEAM Middle East Pipeline Integrity Co. for providing financial assistance to this the research project.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Mirabedini, A.S., Karrabi, M. & Ghasemi, I. Viscoelastic behavior of NBR/phenolic compounds. Iran Polym J 22, 25–32 (2013). https://doi.org/10.1007/s13726-012-0100-8
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s13726-012-0100-8