Abstract
This paper discusses the influence of Flux Cored Arc Welding Process parameters such as welding current, travel speed, voltage on bead profile, metallurgical and mechanical properties of welds of 2 mm thick 409M ferritic stainless steel sheets. The study reveals that, grain coarsening, volume fraction of martensite, hardness of heat affected zone and % of delta ferrite in ER 309 weld metal increases with increase in heat input. However, the results show that variation of heat input does not make any significant effect on tensile strength of the joint. Hence, welding parameters that provide uniform bead profile for the weld are recommended for fabrication.
Similar content being viewed by others
References
John C Lippold and Damian J Kotecki, Welding Metallurgy and Weldability of Stainless Steels, Wiley India (P) Ltd, New Delhi, (2011), 85.
Jeans Yues Gilet, The ferritic solution, International Stainless Steel Forum, International Iron and Steel Institute, Belgium, (2007), 1. http://www.worldstainlesssteel.org
Taban E, Delu E, Dhooge A and Kaluc E, Weld J 12 (2008) 291s.
Greeff M L and Toit M du, Weld J 11 (2006) 243s.
Yamamoto K, Kimura Y, Wei FG and Michima Y, Mater Sci Eng A 329 (2002) 249.
Mohandas T, Madhusudhan Reddy G, Naveed Mohammad, J Mater Process Technol 94 (1999) 133.
Deleu E, Dhooge A, Taban E and Kalnc E, Weld World 53 (2009) R199.
Taban E, Deleu E, Dhooge A and E Kalnc E, Kovove Mater 4 (2007) 67.
Lakshminarayanan A K, Shanmugam K and Balasubramanian V, Ironmak Steelmak 36 (1) (2009) 75.
Kou S and Wang Y H, Weld J 65 (3) (1986) 63-s–70-s.
Shan** Lu, Hidetoshi Fujii and Kiyoshi Nogi, J Mater Sci 43 (2009) 4583.
Shanmugam K, Lakshminarayanan A K and Balasubramanian V, J Mater Sci Tech 25 (2009) 181.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Venkatesan, M.V., Murugan, N., Sam, S. et al. Effect of Heat Input on Macro, Micro and Tensile Properties of Flux Cored Arc Welded Ferritic Stainless Steel Joints. Trans Indian Inst Met 67, 375–383 (2014). https://doi.org/10.1007/s12666-013-0358-3
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12666-013-0358-3