The mechanism of crack propagation in concrete specimens containing cracks under shear loading conditions is studied. The shear box test of pre-cracked (double edge cracks) concrete specimens is carried out under laboratory conditions. The higher order displacement discontinuity formulation and the special crack tip elements for the treatment of crack ends is used to numerically simulate the crack propagation mechanism of brittle solids under direct shear loading. A special modeling technique is also proposed to take into account the effect of crack overlap** on the fracturing process of the bridge area in between the two parallel cracks. In this study, the wing cracks are produced at the first stage of loading and continued their propagation paths toward the shear loading direction. The crack propagation path of the double edge cracked specimens in the bridge area is mostly affected by ligament angles and crack length whereas the shear strength is closely related to the failure pattern. The coalescence mechanism of cracks indicated that the pre-cracked concrete failure occurs in mixed mode in case of non-overlap** cracks configuration and in tensile mode for the overlap** cracks. Finally, comparing the numerical and experimental results validated the crack propagation modeling and verified the accuracy and efficiency of the proposed numerical method.
Similar content being viewed by others
References
H. H. Einstein, D. Veneziano, G. B. Baecher, and K. J. O’Reilly, “The effect of discontinuity persistence on rock slope stability,” Int. J. Rock Mech. Min. Sci. Geomech. Abstr., 20, No. 5, 227–236 (1983).
N. R. Barton, “Review of a new shear strength criterion for rock joints,” Eng. Geol., 7, 287–332 (1973).
B. Ladany and G. Archambault, “Simulation of shear behavior of a jointed rock mass,” in: Proc. of the 11th Symp. Rock Mechanics (ATME) (1970), pp. 105–125.
Z. T. Bieniawski, “Mechanism of brittle fracture of rock. Part II. Experimental studies,” Int. J. Rock Mech. Min. Sci. Geomech. Abstr., 4, No. 4, 407–423 (1967).
A. Bobet and H. H. Einstein, “Fracture coalescence in rock-type materials under uniaxial and biaxial compression,” Int. J. Rock Mech. Min. Sci., 35, 863–888 (1998a).
A. Bobet and H. H. Einstein, “Numerical modeling of fracture coalescence in a model rock material,” Int. J. Fract., 92, 221–252 (1998b).
T. Savilahti, E. Nordlund, and O. Stephansson, “Shear box testing and modeling of joint bridge,” in: N. Barton and O. Stephansson (Eds.), Rock Joints (Proc. of Int. Symp. on Rock Joints, June 4–6, 1990, Loen, Norway), Balkema, Rotterdam (1990), pp. 295–300.
R. H. C. Wong, W. L. Leung, and S. W. Wang, “Shear strength study on rock-like models containing arrayed open joints,” in: D. Elsworth, J. P. Tinucci, and K. A. Heasley (Eds.), Rock Mechanics in the National Interest, Swets & Zeitlinger Lisse, Leiden (2001), pp. 843–849.
C. Gehle and H. K. Kutter, “Breakage and shear behavior of intermittent rock joints,” Int. J. Rock Mech. Min. Sci., 40, 687–700 (2003).
A. Ghazvinian, M. R. Nikudel, and V. Sarfarazi, “Effect of rock bridge continuity and area on shear behavior of joints,” in: Proc. of the 11th ISRM Congress (July 9–13, 2007, Lisbon, Portugal), Lisbon, Portugal (2007).
A. Ghazvinian, V. Sarfarazi, W. Schubert, and M. Blumel, “A study of the failure mechanism of planar non-persistent open joints using PFC2D,” Rock Mech. Rock Eng., 45, 677–693 (2011).
V. Sarfarazi, A. Ghazvinian, W. Schubert, et al., “Numerical simulation of the process of fracture of echelon rock joints,” Rock Mech. Rock Eng., 47, No. 4, 1355–1371 (2013), doi: 10.1007/s00603-013-0450-3.
K. Ravi-Chandar and W. G. Knauss, “An experimental investigation into dynamic fracture: III. On steady-state crack propagation and crack branching,” Int. J. Fract., 26, 141–154 (1984).
H. Horii and S. Nemat-Nasser, “Compression-induced microcrack growth in brittle solids: axial splitting and shear failure,” J. Geophys. Res., 90, 3105–3125 (1985).
J. F. Huang, G. L. Chen, Y. H. Zhao, and R. Wang, “An experimental study of the strain field development prior to failure of a marble plate under compression,” Tectonophysics, 175, 269–284 (1990).
P. S. Theocaris and M. Sakellariou, “Crack propagation in brittle materials under compressive stresses studied by caustics,” J. Mater. Sci., 26, No. 6, 1640–1646 (1991).
R. H. C. Wong, K. T. Chau, C. A. Tang, and P. Lin, “Analysis of crack coalescence in rock-like materials containing three flaws – Part I: experimental approach,” Int. J. Rock Mech. Min. Sci., 38, 909–924 (2001).
Y. P. Li, L. Z. Chen, and Y. H. Wang, “Experimental research on pre-cracked marble under compression,” Int. J. Solids Struct., 42, 2505–2516 (2005).
C. H. Park, Coalescence of Frictional Fractures in Rock Materials, Ph.D. Dissertation, Purdue University, West Lafayette, Indiana (2008).
S. Q. Yang, Y. H. Dai, L. J. Han, and Z. Q. **, “Experimental study on mechanical behavior of brittle marble samples containing different flaws under uniaxial compression,” Eng. Fract. Mech., 76, 1833–1845 (2009).
C. H. Park and A. Bobet, “Crack coalescence in specimens with open and closed flaws: a comparison,” Int. J. Rock Mech. Min. Sci., 46, 819–829 (2009).
C. H. Park and A. Bobet, “Crack initiation, propagation and coalescence from frictional flaws in uniaxial compression,” Eng. Fract. Mech., 77, 2727–2748 (2010).
R. P. Janeiro and H. H. Einstein, “Experimental study of the cracking behavior of specimens containing inclusions (under uniaxial compression),” Int. J. Fract., 164, 83–102 (2010).
S. Q. Yang, “Crack coalescence behavior of brittle sandstone samples containing two coplanar fissures in the process of deformation failure,” Eng. Fract. Mech., 78, 3059–3081 (2011).
P. Cheng-zhi and C. **, “Breakage characteristics and its influencing factors of rock-like material with multi-fissures under uniaxial compression,” Trans. Nonferrous Met. Soc. China, 22, 185–191 (2012).
K. Wallin, “A simple fracture mechanical interpretation of size effects in concrete fracture toughness tests,” Eng. Fract. Mech., 99, 18–29 (2013).
A. R. Ingraffea and F. E. Heuze, “Finite element models for rock fracture mechanics,” Int. J. Num. Anal. Meth. Geomech., 4, 25–43 (1980).
M. Fatehi Marji and I. Dehghani, “Kinked crack analysis by a hybridized boundary element/boundary collocation method,” Int. J. Solids Struct., 47, 922–933 (2010).
M. Fatehi Marji, H. Hosseini-Nasab, and A. H. Kohsary, “A new cubic element formulation of the displacement discontinuity method using three special crack tip elements for crack analysis,” JP J. Solids Struct., 1, 61–91 (2007).
C. A. Tang, P. Lin, R. H. C. Wong, and K. T. Chau, “Analysis of crack coalescence in rock-like materials containing three flaws – Part II: Numerical approach,” Int. J. Rock Mech. Min. Sci., 38, 925–939 (2001).
R. H. C. Wong, C. A Tang, K. T. Chau, and P. Lin, “Splitting failure in brittle rocks containing pre-existing flaws under uniaxial compression,” Eng. Fract. Mech., 69, 1853–1871 (2002).
F. Erdogan and G. C. Sih, “On the crack extension in plates under plane loading and transverse shear,” J. Basic Eng., 85, 519–527 (1963).
M. A. Hussian, E. L. Pu, and J. H. Underwood, “Strain energy release rate for a crack under combined mode I and mode II,” in: Fracture Analysis, ASTM STP 560 (1974), pp. 2–28.
G. C. Sih, “Strain-energy-density factor applied to mixed mode crack problems,” Int. J. Fract., 10, 305–321 (1974).
B. Shen and O. Stephansson, “Modification of the G-criterion for crack propagation subjected to compression,” Eng. Fract. Mech., 47, 177–189 (1994).
M. F. Marji, H. Hosseinin–Nasab, and A. H. Kohsary, “On the uses of special crack tip elements in numerical rock fracture mechanics,” Int. J. Solids Struct., 43, 1669– 1692 (2006).
M. F. Marji, “On the use of power series solution method in the crack analysis of brittle materials by indirect boundary element method,” Eng. Fract. Mech., 98, 365– 382 (2013).
H. Haeri, K. Shahriar, M. F. Marji, and P. Moarefvand, “A coupled numerical- experimental study of the breakage process of brittle substances,” Arabian J. Geosci., 8, No. 2, 809–825 (2013), doi: 10.1007/s12517-013-1165-1.
H. Haeri, K. Shahriar, M. F. Marji, and P. Moarefvand, “On the strength and crack propagation process of the pre-cracked rock-like specimens under uniaxial compression,” Strength Mater., 46, No. 1, 140–152 (2014).
H. Haeri, M. F. Marji, K. Shahriar, and P. Moarefvand, “On the HDD analysis of micro cracks initiation, propagation and coalescence in brittle substances,” Arabian J. Geosci., 8, No. 5, 2841–2852 (2015), doi: 10.1007/s12517-014-1290-5.
H. Haeri, K. Shahriar, M. F. Marji, P. Moarefvand, “Investigation of fracturing process of rock-like Brazilian disks containing three parallel cracks under compressive line loading,” Strength Mater., 46, No. 3, 404–416 (2014).
H. Haeri, K. Shahriar, M. F. Marji, P. Moarefvand, “Simulating the effect of disc erosion in TBM disc cutters by a semi-infinite DDM,” Arabian J. Geosci., 8, No. 6, (2014), doi: 10.1007/s12517-014-1489-5.
J. T. Chen and H. K. Hong, “Review of dual boundary elements methods with emphasis on hypersingular integrals and divergent series,” Appl. Mech. Rev., 52, 17–33 (1999).
M. H. Aliabadi, Fracture of Rocks, Computational Mechanics Publications, Southampton, UK (1998).
Q. Rao, Z. Sun, O. Stephansson, et al., “Shear fracture (mode II) of brittle rock,” Int. J. Rock Mech. Min. Sci., 40, 355–375 (2003).
S. Kahraman and R. Altindag, “A brittleness index to estimate fracture toughness,” Int. J. Rock Mech. Min. Sci., 41, 343–348 (2004).
K. J. Shou and S. L. Crouch, “A higher order displacement discontinuity method for analysis of crack problems,” Int. J. Rock Mech. Min. Sci. Geomech. Abstr., 32, 49–55 (1995).
S. L. Crouch, Analysis of Stresses and Displacements around Underground Excavations: An Application of the Displacement Discontinuity Method, University of Minnesota Geomechanics Report, Minneapolis, Minnesota (1967).
H. Guo, N. I. Aziz, and R. A. Schmidt, “Linear elastic crack tip modeling by displacement discontinuity method,” Eng. Fract. Mech., 36, 933–943 (1990).
C. Scavia, “Fracture mechanics approach to stability analysis of crack slopes,” Eng. Fract. Mech., 35, 889–910 (1990).
M. H. Aliabadi and D. P. Rooke, Numerical Fracture Mechanics, Computational Mechanics Publications, Southampton, UK (1991).
M. F. Marji, H. Hosseini-Nasab, and A. Hosseinmorsgedy, “Numerical modeling of the mechanism of crack propagation in rocks under TBM disc cutters,” J. Mech. Mater. Struct., 2, 439–457 (2009).
G. R. Irwin, “Analysis of stress and strains near the end of a crack traversing a plate,” J. Appl. Mech., 24, 361–364 (1957).
Author information
Authors and Affiliations
Corresponding author
Additional information
Translated from Problemy Prochnosti, No. 4, pp. 130 – 146, July – August, 2015.
Rights and permissions
About this article
Cite this article
Haeri, H. Simulating the Crack Propagation Mechanism of Pre-Cracked Concrete Specimens Under Shear Loading Conditions. Strength Mater 47, 618–632 (2015). https://doi.org/10.1007/s11223-015-9698-z
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11223-015-9698-z