Abstract
In2O3:Sn (Indium Tin Oxide; ITO) films were prepared from a sol solution with highly crystalline ITO nanoparticles (less than 20 nm in size with 10 at.% Sn) which had been prepared by low-pressure spray pyrolysis (LPSP) in a single step. The ITO sol solution was prepared by dispersing LPSP-prepared ITO nanoparticles into ultra pure water. The nanoparticle ITO film was deposited on a glass substrate using a dip-coating method and then annealed in air at various temperatures. The optical transmittances of the ITO films were measured by UV–Vis spectrometry, and the films were found to have a high transparency to visible light (in the case of a film thickness of 250 nm annealed at 400°C, the transparency was in excess of 95% over the range λ=450–800 nm, with a maximum value near 100% at wavelengths above λ=700 nm). The optical transmittances of the films were influenced by the size of the ITO particle used, the film thickness and the annealing temperature. The ITO films showed a minimum resistivity of 9.5×10−2 Ω cm, and their resistivity was affected by both the ITO particle size and the annealing temperature used.
Similar content being viewed by others
References
Alam M.J., Cameron D.C., (2000). Optical and electrical properties of transparent conductive ITO thin films deposited by sol-gel process. Thin Solid Films 377: 455–459
Devi P.S., Chatterjee M., Ganguli D., (2002). Indium tin oxide nano-particles through an emulsion technique. Mater. Lett. 55: 205–210
El Akkad F., Marafi M., Punnoose A., Prabu G., (2000). Effect of substrate temperature on the structural, electrical and optical properties of ITO films prepared by RF magnetron sputtering. Phys. Statu. Solidi A. 177: 445–452
Gao Z., Gao Y.Z., Li Y.H., Yi L., (1999). Effect of Heat Treatment on the Microstructure of Nanophase Indium-Tin Oxide. Nanostruct. Mater. 11: 611–616
Goebbert C., Nonninger R., Aegerter M.A., Scmidt H., (1999). Wet chemical deposition of ATO and ITO coatings using crystalline redispersible in solutions. Thin Solid Films. 351: 79–84
Hamberg I., Granqvist C.G., (1986). Evaporated Sn-doped In2O3 films: Basic optical properties and applications to energy-efficient windows. J. Appl. Phys. 60: R123
Iskandar F., Abdullah M., Yoden H., Okuyama K., (2003). Optical band gap and ultralow dielectric constant materials prepared by a simple dip coating process. J.Appl. Phys. 93(11): 9237–9242
Iskandar F., Abdullah M., Yoden H., Okuyama K., (2004). Silica Films Containing Ordered Pores Prepared by Dip Coating of Silica Nanoparticles and Polystyrene Beads Colloidal Mixture. J. Sol-Gel Sci. Technol. 29(1): 41–47
Itoh Y., Abdullah M., Okuyama K., (2004). Direct preparation of non-agglomerated indium tin oxide nanoparticles by various spray pyrolysis method. J. Mater. Res. 19:1077–1086
Kang Y.C., Park S.B., (1995). A high-volume spray aerosol generator producing small droplets for low pressure applications. J. Aerosol Sci. 26: 1131
Kang Y.C., Park S.B., (1996). Preparation of nanometre size oxide particles using filter expansion aerosol generator. J. Mater. Sci. 31: 2409
Kim H., Horwitz J.S., Kushto G., Pique A., Kafafi Z.H., Gilmore C.M., Chrisey D.B., (2000). Effect of film thickness on the properties of indium tin oxide thin films. J. Appl. Phys. 88: 6021–6025
Lee C.H., Huang C.S., (1994). Spray pyrolysis deposition for indium oxide with different impurities. Mater. Sci. Eng. B 22: 233–240
Lenggoro I.W., Itoh Y., Iida N., Okuyama K., (2003). Control of size and morphology in NiO particle prepared by a low-pressure spray Pyrolysis. Mater. Res. Bull. 38: 1819
Meng L., dos-Santos M.P., (1988). Properties of indium tin oxide films prepared by rf reactive magnetron sputtering at different substrate temperature. Thin Solid Films 322: 56–62
Minami T., 2005. Transparent conducting oxide semiconductors for transparent electrodes. Semicond. Sci. Technol. 20, S35–S44
Okuyama K., Lenggoro I.W., (2003). Preparation of Nanoparticle via Spray Route. Chem. Eng. Sci. 58: 537
Saito S., (1990). Chobiryushi Handbook. Fuji Techno System, Japan, p. 35–36
Sawada Y., Kobayashi C., Seki S., Hunakubo H., (2002). Highky-conducting indium-tin-oxide transparent films fabricated by spray CVD using ethanol solution of indium (III) chroride and tin (II) chrolide. Thin Solid Films 409: 46–50
Tomonaga H., Morimoto T., (2001). Indium-tin oxide coatings via chemical solution deposition. Thin Solid Films 392: 243–248
Udawatte C.P., Yanagisawa K., (2001). Fabrication of Low-porosity Indium Tin Oxide Ceramics in Air from Hydrothermally Prepared Powder. J. Am. Ceram. Soc. 84: 231–253
Vossen J.L., (1977). Transparent Conducting Films. Phys. Thin Films 9: 1
Wei Q., Zheng H., Huang Y., (2001). Direct patterning ITO transparent conductive coatings. Sol. Energ. Mater. Sol. C. 68: 383–390
Yanagisawa K., Udawatte C.P., Nasu N., (2000). Preparation and Characterization of Fine Indium Tin Oxide (ITO) Powders by a Hydrothermal Treatment and Post Annealing Method. J. Mater. Res. 15: 1404–1408
Acknowledgements
Grant-in-Aids and a fellowship sponsored by the Ministry of Education, Culture, Sports, Science and Technology of Japan and the Japan Society for the Promotion of Science (JSPS) are gratefully acknowledged. Postdoctoral fellowship from JSPS for F.I. is also acknowledged. This work was also supported in part by the New Energy and Industrial Technology Development Organization (NEDO)’s “Nanotechnology Materials Program-Nanotechnology Particle Project” based on funds provided by the Ministry of Economy, Trade, and Industry (METI), Japan.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Ogi, T., Iskandar, F., Itoh, Y. et al. Characterization of dip-coated ITO films derived from nanoparticles synthesized by␣low-pressure spray pyrolysis. J Nanopart Res 8, 343–350 (2006). https://doi.org/10.1007/s11051-005-9006-0
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11051-005-9006-0