Abstract
Mg2SiO4 (Forsterite) ceramics were synthesized by solid state route. The effect of lithium magnesium zinc borosilicate (LMZBS) glass addition on the densification temperature and microwave dielectric properties of forsterite ceramics was investigated. The crystal structure and microstructure of ceramic–glass composites were studied by X-ray diffraction and scanning electron microscopic techniques. The dielectric properties of the sintered samples were measured in the microwave frequency range by the resonance method. Addition of 0.5 wt% LMZBS glass improved densification with ε r = 7.3 and Qxf = 121,200 GHz. Addition of 15 wt% LMZBS glass lowered the sintering temperature to about 950 °C with ε r = 6.75 and Qxf = 30,600 GHz. The reactivity of 15 wt% LMZBS glass added forsterite with silver was also studied. The result shows that forsterite doped with suitable amount of LMZBS glass is a possible material for LTCC and microwave substrate applications.
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs10854-009-9882-7/MediaObjects/10854_2009_9882_Fig1_HTML.gif)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs10854-009-9882-7/MediaObjects/10854_2009_9882_Fig2_HTML.jpg)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs10854-009-9882-7/MediaObjects/10854_2009_9882_Fig3_HTML.gif)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs10854-009-9882-7/MediaObjects/10854_2009_9882_Fig4_HTML.gif)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs10854-009-9882-7/MediaObjects/10854_2009_9882_Fig5_HTML.gif)
Similar content being viewed by others
![](https://media.springernature.com/w215h120/springer-static/image/art%3A10.1007%2Fs10854-015-4140-7/MediaObjects/10854_2015_4140_Fig1_HTML.gif)
References
M.T. Sebastian, Dielectric Materials for wireless Communication (Elsevier, Oxford, 2008), pp. 11–42
T. Takada, S.F. Wang, S. Yoshikawa, S.J. Jang, R.E. Newnham, J. Am. Ceram. Soc. 77, 2485 (1994). doi:10.1111/j.1151-2916.1994.tb04629.x
K.P. Surendran, P. Mohanan, M.T. Sebastian, J. Solid State Chem. 177, 4031 (2004). doi:10.1016/j.jssc.2004.07.018
J.A. Lee, J.H. Lee, J.J. Kim, J. Eur. Ceram. Soc. 26, 2135 (2006). doi:10.1016/j.jeurceramsoc.2005.09.081
H. Ohsato, T. Tsunooka, T. Sugiyama, K. Kakimoto, H. Ogawa, J. Electroceramics 17, 445 (2006)
T.S. Sasikala, M.N. Suma, P. Mohanan, C. Pavithran, M.T. Sebastian, J. Alloy Comp. 461, 555 (2008). doi:10.1016/j.jallcom.2007.07.084
N. Kidani, K. Mizushima, M. Takimoto, U S Patent No. 7276460, 2007
H.P. Jeon, S.K. Lee, S.W. Kim, D.K. Choi, Mater. Chem. Phys. 94, 185 (2005). doi:10.1016/j.matchemphys.2005.04.049
I.W. Chen, G.N. Hassold, D.J. Srolovitz, J. Am. Ceram. Soc. 73, 2865 (1990). doi:10.1111/j.1151-2916.1990.tb06687.x
Acknowledgments
The authors are grateful to Kerala State Council for Science, Technology and Environment for financial support.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Sasikala, T.S., Pavithran, C. & Sebastian, M.T. Effect of lithium magnesium zinc borosilicate glass addition on densification temperature and dielectric properties of Mg2SiO4 ceramics. J Mater Sci: Mater Electron 21, 141–144 (2010). https://doi.org/10.1007/s10854-009-9882-7
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10854-009-9882-7