Arrays of test structures consisting of sub-150 nm wide beams were lithographically fabricated in poly(methyl methacrylate) (PMMA) and used to measure the elastic mechanical properties of the material. Capillary forces that arise during the drying of rinse liquids from the test structures caused the nanoscale polymer beams to deform. The initial capillary forces were defined by the test structure geometry, and the magnitudes of the forces were quantified using a two-dimensional Young–Laplace equation. The deformation of the nanostructured beams was measured experimentally and compared to a model based on continuum-level bending beam mechanics, thereby enabling the calculation of the Young’s modulus (E) of the material. For PMMA beams greater than 100 nm in width E was calculated to be 5.1 GPa at room temperature, which corresponds closely to the elastic modulus of bulk PMMA. The Young’s moduli of structures with dimensions less than 100 nm were measured to be less than the bulk value and the origin of the decrease is discussed in terms of dimension dependent properties and polymer degradation during fabrication. The polymer nanostructures also were determined to mechanically deform more readily with increasing characterization temperature.
Similar content being viewed by others
References
International Technology Roadmap for Semiconductors (ITRS) 2005 Ed. (Semicon. Indus. Ass., San Jose, CA 2005)
J.N. Helbert, T. Dack, Handbook of VLSI Microlithography, 2nd Ed. (Noyes/William Andrews, LLC, Norwich, NY 2001)
D. Bellet, L. Canham, Adv. Mater. 10, 487 (1998)
T. Tanaka, M. Morigami, N. Atoda, J. Electrochem. Soc. 140, L115 (1993)
T. Tanaka, M. Morigami, N. Atoda, Japan. J. Appl. Phys. 32, 6059 (1993)
H.B. Cao, P.F. Nealey, W.D. Domke, J. Vac. Sci. Technol. B 18, 3303 (2000)
M.P. Stoykovich, H.B. Cao, K. Yoshimoto, L.E. Ocola, P.F. Nealey, Adv. Mater. 15, 1180 (2003)
K. Yoshimoto, M.P. Stoykovich, H.B. Cao, J.J. de Pablo, P.F. Nealey, W.J. Drugan, J. Appl. Phys. 96, 1857 (2004)
H. Namatsu, K. Kurihara, M. Nagase, K. Iwadate, K. Murase, Appl. Phys. Lett. 66, 2655 (1995)
J. Malzbender, J.M.J. den Toonder, A.R. Balkenende, G. de With, Mater. Sci. Eng. R 36, 47 (2002)
G.M. Pharr, W.C. Oliver, MRS Bull. 7, 28 (1992)
J.M.G. Cowie, Polymers: Chemistry and Physics of Modern Materials, 2nd edn. (Chapman and Hall, Great Britain, 1991)
J.L. Keddie, R.A.L. Jones, R.A. Cory, Europhys. Lett. 27, 59 (1994)
J.L. Keddie, R.A.L. Jones, R.A. Cory, Faraday Discuss. 98, 219 (1994)
W.E. Wallace, J.H. van Zanten, W.L. Wu, Phys. Rev. E 52, R3329 (1995)
J.A. Forrest, K. Dalnoki-Veress, J.R. Stevens, J.R. Dutcher, Phys. Rev. Lett. 77, 2002 (1996)
J.A. Forrest, K. Dalnoki-Veress, J.R. Dutcher, Phys. Rev. E 56, 5705 (1997)
J. Mattsson, J.A. Forrest, L. Böorjesson, Phys. Rev. E 62, 5187 (2000)
D.S. Fryer, P.F. Nealey, J.J. de Pablo, Macromolecules 33, 6439 (2000)
J.A. Torres, P.F. Nealey, J.J. de Pablo, Phys. Rev. Lett. 85, 3221 (2000)
D.S. Fryer, R.D. Peters, E.J. Kim, J.E. Tomaszewski, J.J. de Pablo, P.F. Nealey, C.C. White, W.L. Wu, Macromolecules 34, 5627 (2001)
R.S. Tate, D.S. Fryer, S. Pasqualini, M. Montague, J.J. de Pablo, P.F. Nealey, J. Chem. Phys. 115, 9982 (2001)
T.S. Jain, J.J. de Pablo, J. Chem. Phys. 120, 9371 (2004)
C.J. Ellison, J.M. Torkelson, Nature Mater. 2, 695 (2003)
C.W. Frank, V. Rao, M.M. Despotopoulou, R.F.W. Pease, W.D. Hinsberg, R.D. Miller, J.F. Rabolt, Science 273, 912 (1996)
D.B. Hall, J.M. Torkelson, Macromolecules 31, 8817 (1998)
B. Frank, A.P. Gast, T.P. Russell, H.R. Brown, C.J. Hawker, Macromolecules 29, 6531 (1996)
T.R. Böhme, J.J. de Pablo, J. Chem. Phys. 116, 9939 (2002)
K. van Workum, J.J. de Pablo, Nano Lett. 3, 1405 (2003)
K. Yoshimoto, T.S. Jain, P.F. Nealey, J.J. de Pablo, J. Chem. Phys. 122, 144712 (2005)
C.M. Stafford, B.D. Vogt, C. Harrison, D. Julthongpiput, R. Huang, Macromolecules 39, 5095 (2006)
B. Briscoe, L. Fiori, E. Pelillo, J. Phys. D 31, 2395 (1998)
M. Radmacher, R.W. Tillmann, M. Fritz, H.E. Gaub, Science 257, 1900 (1992)
C.G. Simon Jr., N. Eidelman, Y. Deng, N.R. Washburn, Macromol. Rapid Commun. 25, 2003 (2004)
C.A. Tweedie, D.G. Anderson, R. Langer, K.J. Van Vliet, Adv. Mater. 17, 2599 (2005)
A.G. Every, Meas. Sci. Technol. 13, R21 (2002)
J.A. Forrest, K. Dalnoki-Veress, J.R. Dutcher, Phys. Rev. E 58, 6109 (1998)
R. Hartschuh, Y. Ding, J.H. Roh, A. Kisliuk, A.P. Sokolov, C.L. Soles, R.L. Jones, T.J. Hu, W.L. Wu, A.P. Mahorowala, J. Polym. Sci. B Polym. Phys. 42, 1106 (2004)
W. Cheng, G. Fytas, A.V. Kiyanova, M.Y. Efremov, P.F. Nealey, Macromol. Rapid Commun. 27, 702 (2006)
R. Hotz, J.K. Krüger, W. Possart, R. Tadros-Morgane, J. Phys.: Condens. Matter 13, 7953 (2001)
C.M. Stafford, C. Harrison, K.L. Beers, A. Karim, E.J. Amis, M.R. Vanlandingham, H.-C. Kim, W. Volksen, R.D. Miller, E.E. Simonyi, Nat. Mater. 3, 545 (2004)
C.M. Stafford, S. Guo, C. Harrison, M.Y.M. Chang, Rev. Sci. Instrum. 76, 062207 (2005)
H.D. Espinosa, B.C. Prorok, M. Fischer, J. Mech. Phys. Solids 51, 47 (2003)
J.-H. Zhao, M. Kiene, C. Hu, P.S. Ho, Appl. Phys. Lett. 77, 2843 (2000)
J.-H. Zhao, T. Ryan, P.S. Ho, A.J. McKerrow, W.-Y. Shih, J. Appl. Phys. 88, 3029 (2000)
The 3D finite element modeling of the deformation of the test structure beams was performed using ANSYS 11 (ANSYS) for beams with H = 500 nm, BW = 100 nm, ΔPi = 4 MPa, and E = 5 GPa similar to the experimental PMMA beams.
W.M. Cheng, G.A. Miller, J.A. Manson, R.W. Hertzberg, L.H. Sperling, J. Mater. Sci. 25, 1917 (1990)
J.A. Johnson, D.W. Jones, J. Mater. Sci. 29, 870 (1994)
S.I. Naqui, I.M. Robinson, J. Mater. Sci. 28, 1421 (1993)
M.E. James, Polymer Data Handbook (Oxford, New York, 1999)
R.S. Lakes, Viscoelastic Solids (CRC, Boca Raton, FL, 1999)
S.Y. Chou, P.R. Krauss, P.J. Renstrom, Appl. Phys. Lett. 67, 3114 (1995)
S.Y. Chou, P.R. Krauss, P.J. Renstrom, Science 272, 85 (1996)
C.J. Ellison, R.L. Ruszkowski, N.J. Fredin, J.M. Torkelson, Phys. Rev. Lett. 92, 095702 (2004)
W.C. Hu, K. Sarveswaran, M. Lieberman, G.H. Bernstein, J. Vac. Sci. Technol. B 22, 1711 (2004)
B.D. Gates, Q.B. Xu, M. Stewart, D. Ryan, C.G. Willson, G.M. Whitesides, Chem. Rev. 105, 1171 (2005)
L.E. Ocola, D. Tennant, G. Timp, A. Novembre, J. Vac. Sci. Technol. B 17, 3164 (1999)
F.J. Pantenburg, S. Achenbach, J. Mohr, J. Vac. Sci. Technol. B 16, 3547 (1998)
M.J. Rooks, E. Kratschmer, R. Viswanathan, J. Katine, R.E. Fontana, S.A. MacDonald, J. Vac. Sci. Technol. B 20, 2937 (2002)
Author information
Authors and Affiliations
Corresponding author
Additional information
PACS
62.25.+g; 68.35.Gy; 81.16.Nd
Rights and permissions
About this article
Cite this article
Stoykovich, M., Yoshimoto, K. & Nealey, P. Mechanical properties of polymer nanostructures: measurements based on deformation in response to capillary forces. Appl. Phys. A 90, 277–283 (2008). https://doi.org/10.1007/s00339-007-4262-8
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00339-007-4262-8