Abstract
Accelerated oxidation tests have been conducted on a number of Co-Cr, Co-Al, and Co-Cr-Al alloys coated with a thin film of Na2SO4 and exposed at 600 to 750 °C in O2-SO2-SO3 environments containing 0.0095-5 pct (SO2 + SO3). Generally, Co-Cr and Co-Cr-Al alloys reacted nonuniformly, usually in the form of pits, and Co-Al alloys suffered broad frontal attack. The morphology of the reaction product was observed to be dependent on temperature andP SO3 Under all conditions, a thin sulfur-rich band containing sulfides was observed at the alloy/scale interface, and cobalt dissolved near this interface and formed Co3O4 and/or CoSO4(s) in different regions of the reaction product.
Similar content being viewed by others
References
D. J. Wortman, R. E. Fryxell, and I.I. Bessen:Proceedings of the Third Conf. on Gas Turbine Materials in a Marine Environment, session V, paper 11, pp. 1-11, sponsored by U.S. Naval Ship Engineering Center and U. K. Ship Department, held at the University of Bath, England, September 1976, available from U. S. Naval Sea Systems Command, SEA 05231, Washington, DC.
R. H. Barkalow and F. S. Pettit: inHigh Temperature Metal Halide Chemistry, D. L. Hildenbrand and D. D. Cubicciotti, eds., The Electrochemical Society, Princeton, NJ, 1978, p. 617.
P. Hancock: inHigh Temperature Metal Halide Chemistry, D. L. Hildenbrand and D.D. Cubicciotti, eds., The Electrochemical Society, Princeton, NJ, 1978, p. 645.
D. A. Shores, K. L. Luthra, and D. W. McKee: inHigh Temperature Metal Halide Chemistry, D. L. Hildenbrand and D. D. Cubicciotti, eds., The Electrochemical Society, Princeton, NJ, 1978, p. 538.
D.W. McKee, D.A. Shores, and K. L. Luthra:J. Electrochemical Society, 1978, vol. 125, pp. 411–19.
V. I. Hanby:J. Eng. Power, 1974, vol. 96, pp. 129–33.
C. A. Stearns, R. A. Miller, F.J. Kohl, and G. C. Fryberg:High Temperature Metal Halide Chemistry, D. L. Hildenbrand and D. D. Cubicciotti, eds., The Electrochemical Society, Princeton, NJ, 1978, pp. 468–83.
D. J. Wortman, R. E. Fryxell, K. L. Luthra, and P. A. Bergman:Thin Solid Films. 1979, vol. 64, pp. 281–88.
R. L. Jones and S. T. Gadomski: Naval Research Laboratory, Washington, DC, unpublished research, 1977.
K.L. Luthra and D.A. Shores:J. Electrochem. Society, 1980, vol. 127, pp. 2202–10.
J. A. Goebel, F. S. Pettit, and G. W. Goward:Metall. Trans., 1973, vol. 4, pp. 261–78.
R. A. Rapp and K.S. Goto:Second International Symposium on Molten Salts, J. Braunstein and J. R. Selman, eds., The Electrochemical Society, Pennington, NJ, 1981, pp. 159–71.
JANAF Thermochemical Tables, The Dow Chemical Company, Midland, MI, 1971; Supplement, 1974.
R. H. Barkalow and F. S. Pettit:Fourth Conf. on Gas Turbine Materials in a Marine Environment, sponsored by U. S. Naval Sea Systems Command and U. K. Ministry of Defense Ship Department and held at Annapolis, MD, June 1979, distributed by U. S. Naval Sea Systems Command, SEA 05231, Washington, DC, pp. 493-524.
K.L. Luthra:Metall. Trans. A, 1982, vol. 13A, p. 1647.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Luthra, K.L. Low Temperature Hot Corrosion of Cobalt-Base Alloys: PartI. Morphology of the Reaction Product. Metall Trans A 13, 1843–1852 (1982). https://doi.org/10.1007/BF02647841
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF02647841