Abstract
HZSM-5 zeolite was screened as catalyst for high density polyethylene degradation at 450‡C, under nitrogen static atmosphere. Two different samples were studied in this condition: HDPE alone and mixed with HZSM-5. The reactor was connected on line to an HP 5890-II gas Chromatograph. Sample degradation was investigated using a Perkin-Elmer Delta 7 Thermobalance, from room temperature to 800‡C, with heating rates of 5.0, 10.0 and 20.0‡C min−1. From TG curves, the activation energies, calculated using an integral kinetic method, decreased 60.6% in the presence of the zeolite.
Similar content being viewed by others
References
W. Kaminski, J. Janning and H. Sinn, Eur. Rubber J., 15 (1979) 161.
R. C. Poller, J. Chem. Tech. Biotechnol., 30 (1980) 152.
A. Lucchesi, G. Maschio and P. Giusti, Poliplasti, 288 (1981) 73.
G. Audisio, A. Silvani, P. L. Beltrame and P. Cartini, J. Anal. Appl. Pyrol., 7 (1984) 83.
Y. Uemichi, Y. Kashiowaya, M. Tsukidate, A. Ayame and H. Kanoh, Bull. Chem. Soc. Jpn., 55 (1983) 2768.
Y. Uemichi, Y. Kashiowaya, A. Ayame and H. Kanoh, Chem. Lett., 1 (1984) 41.
T. Ozawa, Bull. Chem. Soc. Jpn., 38 (1965) 1881.
J. H. Flynn and W. A. Wall, Polym. Lett., 4 (1969) 323.
V. J. Fernandes Jr., DSc. Thesis, Universidade de SÃo Paulo, 1991.
V. J. Fernandes Jr. and A. S. AraÚjo, Química Nova, 18 (1995) 11.
V. J. Fernandes Jr. and A. S. AraÚjo, Thermochim. Acta, 255 (1995) 273.
Author information
Authors and Affiliations
Additional information
This work was supported by Conselho Nacional de Desenvolvimento Cientifico e Tecnológico (CNPq) and CoordenaÇÃo de Apoio ao Pessoal de Ensino Superior (CAPES).
Rights and permissions
About this article
Cite this article
Fernandes, V.J., Araujo, A.S. & Fernandes, G.J.T. Catalytic degradation of polyethylene evaluated by TG. Journal of Thermal Analysis 49, 255–260 (1997). https://doi.org/10.1007/BF01987446
Issue Date:
DOI: https://doi.org/10.1007/BF01987446