Abstract
The fluorine-bearing iron concentrate is one of the refractory raw materials for pelletization, which is mainly used in Baotou iron and steel company with lots of problems, such as narrow roasting temperature range and low compressive strength of products. According to its specific character, the effects of roasting temperature, time on the compressive strength and microstructure of pellets were researched. The results show that low melting substances formed during the roasting was the dominant reason of those problems. High melting substances were added in the roasting to investigate their effects on the roasting properties of fluorine-bearing iron concentrate pellets. Low melting substances were reduced when chromite was added. The compressive strength of products was 3100N/P when the 2% chromite was added at the roasting temperature of 1150 °C, which was increased 700 N/P compared with the pellets without chromite, and the roasting temperature range was expanded by 170 °C.
Access this chapter
Tax calculation will be finalised at checkout
Purchases are for personal use only
Preview
Unable to display preview. Download preview PDF.
Similar content being viewed by others
References
Ji Junmei, “Beneficiation Test Research for Reducing Fluorine Content in Iron Concentrate of Bao Steel’s Concentrator”, Metal Mine, 7(2004), 35–37.
Wu Huling, “Study on Reasonable Allocation Technology of Iron-making Raw Materials in Bao Gang Factory” (Ph.D. thesis, Northeastern University, 2006), 22–23.
3.Xu Bing, **ong Ling, Yang Yong-bin, Jiang Tao, Li Qian, Wang Jie-Chao, “Study on Fluorie-Bearing Iron Concentrate Pellets Added with Dolomite”, Iron and Steel, 11 (2008), 9–15.
Author information
Authors and Affiliations
Editor information
Editors and Affiliations
Rights and permissions
Copyright information
© 2016 TMS (The Minerals, Metals & Materials Society)
About this chapter
Cite this chapter
Yang, L., Wang, S., Fu, Gh., Guo, Yf., Jiang, T. (2016). The Preheating and Roasting Properties of Fluorine-Bearing Iron Concentrate Pellets and Main Influence Factors. In: Hwang, JY., et al. 7th International Symposium on High-Temperature Metallurgical Processing. Springer, Cham. https://doi.org/10.1007/978-3-319-48093-0_46
Download citation
DOI: https://doi.org/10.1007/978-3-319-48093-0_46
Publisher Name: Springer, Cham
Print ISBN: 978-3-319-48617-8
Online ISBN: 978-3-319-48093-0
eBook Packages: Chemistry and Materials ScienceChemistry and Material Science (R0)