Abstract
A newly-developed technique for the simultaneos characterization of the oxide-silicon interface properties and of bulk impurities was used for a systematic study of the nitridation process of thin oxides. This technique is based upon surface recombination velocity measurements, and does not require the formation of a capacitor structure, so it is very suitable for the characterization of as-grown interfaces.
Oxides grown both in dry and in wet enviroments were considered, and nitridation processes in N2O and in NO were compared to N2 annealing processes. The effect of nitridation temperature and duration were also studied, and RTO/RTN processes were compared to conventional furnace nitridation processes.
Surface recombination velocity was correlated with nitrogen concentration at the oxide-silicon interface obtained by Secondary Ion Mass Spectroscopy (SIMS) measurements. Surface recombination velocity (hence surface state density) decreases with increasing nitrogen pile-up at the oxide-silicon interface, indicating that in nitrided interfaces surface state density is limited by nitridation. NO treatments are much more effective than N2O treatments in the formation of a nitrogen-rich interface layer and, as a consequence, in surface state reduction.
Surface state density was measured in fully processed wafers before and after constant current stress. After a complete device process surface states are annealed out by hydrogen passivation, however they are reactivated by the electrical stress, and surface state results after stress were compared with data of surface recombination velocity in as-processed wafers.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
V. Lehmann and H. Föil, J. Electrochem. Soc. 135, 2831 (1988)
M. L. Polignano, A. P. Caricato, A. Modelli and R. Zonca, Proc. of the Electrochemical Society Symposium ALTECH 99, edited by B. Kolbesen, C. Claeys and F. Tardif, The Electrochemical Society, 1999, p. 38
B. E. Deal, E. L. MacKenna, and P. L. Castro, J. Electrochem. Soc. 116, 997 (1969)
M. L. Polignano, N. Bellafiore, D. Caputo, A. P. Caricato, A. Modelli, R. Zonca, J. of the Electrochem. Soc., (1999), to be published
E. Yablonovitch, D. L. Aliara, C. C. Chang, T. Gmitter and T. B. Bright, Phys. Rev. Letters 57, 249 (1986)
B. Adamowicz and H. Hasegawa, Jpn. J. Appl. Phys. 37, 1631 (1998)
Y. Gao, J. Appi. Phys. 64, 3760 (1988)
M. Bersani, M. Fedrizzi, M. Sbetti, M. Anderle, in Characterisation and Metrology for ULSI Tecnology, AIP Conference proceeding 449, ed. by D. G. Seiler, A. C. Diebold, W. M. Bullís, T. J. Shaffner, R. McDonald and E. J. Walters, 892–896, Woodbury, New York (1998).
E. N. Nicollian and J. R. Brews, MOS Physics and Technology, Wiley, New York, 1982
E.P. Gusev, H.-C. Lu, E. L. Garfunkel, T. Gustafsson and M. L. Green, IBM J. Res. Develop. 43, 1, (1999)
T. Hori, Gate dielectrics and MOS ULSI, Springer Verlag, Berlin, 1997, p. 225
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Polignano, M.L., Alessandri, M., Brazzelli, D. et al. Characterization of nitrided silicon-silicon dioxide interfaces. MRS Online Proceedings Library 591, 200–205 (1999). https://doi.org/10.1557/PROC-591-207
Published:
Issue Date:
DOI: https://doi.org/10.1557/PROC-591-207