Abstract
The desulfurization and resulfurization of slag containing oxides of vanadium and titanium (CaO–SiO2–MgO–Al2O3–V2O3–TiO2–FeO) in the pretreatment of semi-steel desulfurization at 1623 K were investigated. Based on the ionic structure theory of slag, it could be concluded that V2O3 and TiO2 combined with (O2–) to form complex anions including \({\mathrm{VO}}_{3}^{3-}\), \({\text{Ti}}{\text{O}}_{4}^{{4}-},\) etc., which reduced the activity of (O2–) and decreased the sulfur partition ratio (LS). And FeO enhanced the activity of [O] at the slag–metal interface, which decreased the desulfurization capacity of the slag. Compared to the binary basicity, the presented basicity expression containing V2O3 and TiO2 described the relationship between LS and basicity more accurately. Considering the problems of dilute slag, a large amount of residual slag and much resulfurization in the slagging-off process after pretreatment, the effect of CaO + C-based slag modifier on the resulfurization, melting point and viscosity of the desulfurization slag was investigated. It was proposed that adding 5%–10% of the slag modifier to the desulfurization slag after desulfurization decreased the resulfurization effectively. And the added modifier adjusted the slag viscosity well, which helped to reduce iron loss and residual slag.
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs42243-021-00666-3/MediaObjects/42243_2021_666_Fig1_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs42243-021-00666-3/MediaObjects/42243_2021_666_Fig2_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs42243-021-00666-3/MediaObjects/42243_2021_666_Fig3_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs42243-021-00666-3/MediaObjects/42243_2021_666_Fig4_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs42243-021-00666-3/MediaObjects/42243_2021_666_Fig5_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs42243-021-00666-3/MediaObjects/42243_2021_666_Fig6_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs42243-021-00666-3/MediaObjects/42243_2021_666_Fig7_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs42243-021-00666-3/MediaObjects/42243_2021_666_Fig8_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs42243-021-00666-3/MediaObjects/42243_2021_666_Fig9_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs42243-021-00666-3/MediaObjects/42243_2021_666_Fig10_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs42243-021-00666-3/MediaObjects/42243_2021_666_Fig11_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs42243-021-00666-3/MediaObjects/42243_2021_666_Fig12_HTML.png)
Similar content being viewed by others
References
R.Q. Liang, J.H. Ji, J.C. He, J. Iron Steel Res. Int. 18 (2011) No. S2, 107–112.
N. Yoshie, S. Ikuhiro, K. Naoki, T. Kotaro, M. Yuji, ISIJ Int. 57 (2017) 1029–1036.
W.S. Ge, H.J. Gong, L.K. Jiang, L. Li, L. Chen, Adv. Mater. Res. 807–809 (2013) 2389–2392.
J.F. Xu, F.X. Huang, X.H. Wang, C.L. **g, Metall. Res. Technol. 112 (2015) 504.
J.P. Duan, Y.L. Zhang, X.M. Yang, Int. J. Miner. Metall. Mater. 16 (2009) 375–382.
J. Li, Z.T. Zhang, L.L. Liu, W.L. Wang, X.D. Wang, ISIJ Int. 53 (2013) 1696–1703.
K. Dong, L. Wu, W.J. Liu, R. Zhu, ISIJ Int. 54 (2014) 2248–2254.
Z.S. Ren, X.J. Hu, K.C. Chou, J. Iron Steel Res. Int. 20 (2013) No. 9, 21–25.
X. Tang, C.S. Xu, ISIJ Int. 35 (1995) 367–371.
H.J. Wang, L.J. Wang, S. Seetharaman, Steel Res. Int. 87 (2016) 199–209.
D.Y. Wang, Q.F. Shu, B.J. Yan, L.S. Wu, J. Wang, Y.C. Dong, J. Am. Ceram. Soc. 100 (2017) 4912–4927.
S.Q. Zhang, B. **e, Y. Wang, T. Guan, H.L. Cao, X.L. Zeng, J. Iron Steel Res. Int. 19 (2012) No. 11, 33–38.
L.S. Wu, C. Qi, B. Yan, J. Wang, Y. Dong, Metall. Mater. Trans. B 50 (2019) 924–930.
J.C. Li, Z.C. Guo, J.T. Gao, Ironmak. Steelmak. 41 (2014) 710–714.
J.S. Li, H.Y. Tang, K.M. Sun, D.S. Wen, J. Iron Steel Res. 21 (2009) No. 2, 9–12+22.
C.L. Wang, Q. Lu, S.H. Zhang, F.M. Li, J. Univ. Sci. Technol. Bei**g 13 (2006) 213–217.
X.M. Yang, M. Zhang, C.B. Shi, G.M. Chai, J. Zhang, Metall. Mater. Trans. B 43 (2012) 241–266.
X.M. Yang, C.B. Shi, M. Zhang, G.M. Chai, F. Wang, Metall. Mater. Trans. B 42 (2011) 1150–1180.
X.M. Yang, J.Y. Li, M. Zhang, F.J. Yan, D.P. Duan, J. Zhang, Metals 8 (2018) 1083.
F.S. Li, Y.L. Zhang, Z.C. Guo, JOM 69 (2017) 1632–1638.
H. Xu, Z.F. Zhao, F.Y. Huang, M.C. Zhang, Q. Liu, Y. Zhou, China Metallurgy 21 (2011) No. 11, 26–29.
S. Ueda, T. Kon, T. Miki, S.J. Kim, H. Nogami, ISIJ Int. 55 (2015) 2098–2104.
G.W. Toop, C.S. Somis, Can. Metall. Quart. 1 (1962) 129–152.
E. Maxl, H. Hiebler, H. Presslinger, K. Antlinger, ISIJ Int. 33 (1993) No. 2, 88–97.
A. Werme, Steel Res. Int. 59 (1988) 6–15.
K.C. Mills, ISIJ Int. 33 (1993) 148–155.
H. Ono, K. Nakajima, R. Maruo, S. Agawa, T. Usui, ISIJ Int. 49 (2009) 957–964.
E.J. Jung, W. Wook, I. Sohn, D.J. Min, J. Mater. Sci. 45 (2010) 2023–2029.
Y. Yang, L.D. Teng, S. Seetharaman, Steel Res. Int. 85 (2014) 1588–1596.
R. Tsu**o, J. Nakashima, M. Hirai, Y. Yamada, ISIJ Int. 29 (1989) 92–95.
S.K. Wei, Acta Metall. Sin. 7 (1964) 157–164.
Y. Taniguchi, K. Morita, N. Sano, ISIJ Int. 37 (1997) 956–961.
Y. Nakagawa, K. Suzuki, M. Fukumoto, Trans. Jpn. Inst. Met. 7 (1966) 23–31.
B.W. Yang, B. Song, L.F. Li, L. Chen, Metals 9 (2019) 1239.
S. Ban-Ya, M. Hobo, T. Kaji, T. Itoh, M. Hino, ISIJ Int. 44 (2004) 1810–1816.
B. Deo, J. Halder, B. Snoeijer, A. Overbosch, Ironmak. Steelmak. 32 (2005) 54–60.
K. Sahoo, B. Venkata-Rao, K. Srinivas, D.S.V. Kumar, in: Conference: STIS-2013, NML, Jamshedpur, India, 2013, pp. 1–15.
[38] P.C. Li, X.J. Ning, Metall. Mater. Trans. B 47 (2016) 446–457.
X. Hao, X.H. Wang, Steel Res. Int. 87 (2016) 359–363.
Y. Yang, A.R. McKague, I.D. Sommerville, A. Mclean, Can. Metall. Quart. 36 (1997) 347–354.
G.H. Zhang, K.C. Chou, J. Iron Steel Res. Int. 17 (2010) No. 4, 1–4.
A. Bergman, ISIJ Int. 28 (1988) 945–951.
R.W. Young, J.A. Duffy, G.J. Hassall, Z. Xu, Ironmak. Steelmak. 19 (1992) 201–219.
N.J. Sosinsky, I.D. Sommerville, Metall. Mater. Trans. B 17 (1986) 331–337.
T. Vuolio, V.V. Visuri, T. Paananen, T. Fabritius, Metall. Mater. Trans. B 50 (2019) 1791–1807.
J. Yang, M. Kuwabara, K. Okumura, M. Sano, ISIJ Int. 45 (2005) 1795–1803.
J. Yang, M. Kuwabara, T. Teshigawara, M. Sano, ISIJ Int. 45 (2005) 1607–1615.
R. Nagabayashi, M. Hino, S. Ban-Ya, Tetsu-to-Hagane 74 (1988) 1577–1584.
Acknowledgements
Thanks are given to Liang Chen, a senior engineer at Pangang Group Research Institute Co., Ltd., for discussion and assistance in this work.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Yang, Bw., Hu, Yh., Liu, Sp. et al. Influence of desulfurization slag containing oxides of vanadium and titanium on semi-steel pre-desulfurization. J. Iron Steel Res. Int. 29, 939–950 (2022). https://doi.org/10.1007/s42243-021-00666-3
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s42243-021-00666-3