Abstract
The current study deals with the investigation on the performance characteristics of varying composition of coating mixture comprising carbon nano-tube, alumina and titanium dioxide on the thermal spray coating on mild steel. The performance properties, namely tensile and microhardness, were measured for the varying composition of coating mixture based thermal coating on mild steel. Response surface methodology was adopted to access the interdependencies prevailing between various dependent and independent parameters, namely composition of the mixture, tensile and microhardness. Scanning Electron Microscope coupled with elemental map** were used to show the melting zones features and composition. The experimental results and response graphs indicated that increased weight percentages of carbon nano-tube and TiO2 with an optimal value of alumina at 87.5 percent of total weight showed better performance properties due to better dispersion leading to good bonding suitable for protective coatings. Scanning Electron Microscope images reveal partially melted zones that were restricted to smaller regions, and all particles tend to solidify beginning with a fully molten phase.
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs12541-020-00458-x/MediaObjects/12541_2020_458_Fig1_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs12541-020-00458-x/MediaObjects/12541_2020_458_Fig2_HTML.jpg)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs12541-020-00458-x/MediaObjects/12541_2020_458_Fig3_HTML.jpg)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs12541-020-00458-x/MediaObjects/12541_2020_458_Fig4_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs12541-020-00458-x/MediaObjects/12541_2020_458_Fig5_HTML.jpg)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs12541-020-00458-x/MediaObjects/12541_2020_458_Fig6_HTML.png)
Similar content being viewed by others
References
Odhiambo, J. G., Li, W., Zhao, Y., & Li, C. (2019). Porosity and Its significance in plasma-sprayed coatings. Coatings, 9(7), 460.
An, Y., Li, S., Hou, G., Zhao, X., Zhou, H., & Chen, J. (2017). Mechanical and tribological properties of nano/micro composite alumina coatings fabricated by atmospheric plasma spraying. Ceramics International, 43(6), 5319-5328.
Pandey, V. K., & Verma, A. (2016). An experimental study of effect of the parameters of HVOF coating of WC-10Co-4Cr on mild steel plate. Imperial Journal of Interdisciplinary Research, 2(11), 1050–1060.
Jambagi, S. C., Kar, S., Brodard, P., & Bandyopadhyay, P. P. (2016). Characteristics of plasma sprayed coatings produced from carbon nano-tube doped ceramic powder feedstock. Materials and Design, 112, 392-401.
Popoola, A. P. I., Daniyan, A. A., Umoru, L. E., & Fayomi, O. S. I. (2017). Effect of WO3 nanoparticle loading on the microstructural, mechanical and corrosion resistance of Zn matrix/TiO2-WO3nano-composite coatings for marine application. Journal of Marine Science and Application, 16(1), 102-109.
Manjunatha, S. S., Manjaiah, M., & Basavarajappa, S. (2017). Characterization of Laser Remelted Plasma-Sprayed Mo Coating on AISI 1020 Steel. Silicon, 9(5), 741–751.
Santos, A., Gonzalez, C. and Ramirez, Z.Y., “Characterization of Tungsten Carbide coatings deposited on AISI 1020 steel”. In Journal of Physics: Conference Series Vol. 786, No. 1, p. 012011. IOP Publishing, 2017.
TabkhPaz, M., Park, D. Y., Lee, P. C., Hugo, R., & Park, S. S. (2017). Development of nano-composite coatings with improved mechanical, thermal, and corrosion protection properties. Journal of Composite Materials, 52(8), 1045-1060.
Tian, H. L., Guo, M. Q., Wang, C. L., Tang, Z. H., & Cui, Y. J. (2017). Tribologicalbehaviour of a self-lubricated GO/WC–12Co thermal spray coating. Surface Engineering., 34(10), 1-9.
Saini, H., & Singh, E. P. (2017). Microstructural characterisation of thermal spray coatings on stainless steel AISI SS-316 L. International Journal of Advance Research, Ideas and Innovations in Technology., 3, 1106-1110.
Ichim, L., Prodana, M., & Dumitriu, C. (2016). The elaboration and characterization of a hybrid bionic coating on Ti based on hydroxyapatite and nano-tubes. University Politehnica of Bucharest Scienific Bulletin series B-Chemistry and Material science, 78(1), 161–172.
Zavareh, M. A., Sarhan, A. A. D. M., Zavareh, P. A., & Basirun, W. J. (2016). Electrochemical corrosion behavior of carbon steel pipes coated with a protective ceramic layer using plasma and HVOF thermal spray techniques for oil and gas. Ceramics International, 42(2), 3397-3406.
Sadeghimeresht, E., Markocsan, N., Nylén, P., & Björklund, S. (2016). Corrosion performance of bi-layer Ni/Cr2C3–NiCr HVAF thermal spray coating. Applied Surface Science, 369, 470-481.
Cavallaro, G. F., Francavilla, A., Latour, M., Piluso, V., & Rizzano, G. (2017). Experimental behaviour of innovative thermal spray coating materials for FREEDAM joints. Composites Part B: Engineering, 115, 289-299.
García-Rodríguez, S., López, A. J., Torres, B., & Rams, J. (2016). 316L stainless steel coatings on ZE41 magnesium alloy using HVOF thermal spray for corrosion protection. Surface and Coatings Technology, 287, 9-19.
Günen, A. (2016). Micro-Abrasion Wear Behavior of Thermal-Spray-Coated Steel Tooth Drill Bits. ActaPhysicaPolonica A, 130(1), 217-222.
Lee, H. S., Singh, J. K., & Park, J. H. (2016). Pore blocking characteristics of corrosion products formed on Aluminum coating produced by arc thermal metal spray process in 3.5 wt. % NaCl solution. Construction and Building Materials, 113, 905-916.
Zavareh, M. A., Sarhan, A. A. D. M., Zavareh, P. A., Razak, B. B. A., Basirun, W. J., & Ismail, M. B. C. (2016). Development and protection evaluation of two new, advanced ceramic composite thermal spray coatings, Al2O3–40TiO2 and Cr3C2–20NiCr on carbon steel petroleum oil pi**. Ceramics International, 42(4), 5203-5210.
Sharma, A., & Goel, S. K. (2016). Erosion behaviour of WC–10Co–4Cr coating on 23-8-N nitronic steel by HVOF thermal spraying. Applied Surface Science, 370, 418-426.
Lee, H. S., Singh, J. K., Ismail, M. A., & Bhattacharya, C. (2016). Corrosion resistance properties of aluminum coating applied by arc thermal metal spray in SAE J2334 solution with exposure periods. Metals, 3, 55.
Zhang, S. D., Wu, J., Qi, W. B., & Wang, J. Q. (2016). Effect of porosity defects on the long- term corrosion behaviour of Fe-based amorphous alloy coated mild steel. Corrosion Science, 110, 57-70.
Kulpetchdara, K., Limpichaipanit, A., Rujijanagul, G., Randorn, C., & Chokethawai, K. (2016). Influence of the nano hydroxyapatite powder on thermally sprayed HA coatings onto stainless steel. Surface and Coatings Technology, 306, 181-186.
Singh, H., Sidhu, T. S., Kalsi, S. S., & Karthikeyan, J. (2016). Evolution of the microstructure by high velocity impacts of particles by cold spray. Materials and Manufacturing Processes, 31(11), 1514-1520.
Da Silva, F. S., Bedoya, J., Dosta, S., Cinca, N., Cano, I. G., Guilemany, J. M., & Benedetti, A. V. (2017). Corrosion characteristics of cold gas spray coatings of reinforced aluminum deposited onto carbon steel. Corrosion Science, 114, 57-71.
Luo, W., Selvadurai, U., & Tillmann, W. (2016). Effect of residual stress on the wear resistance of thermal spray coatings. Journal of Thermal Spray Technology., 25, 321-330.
Peat, T., Galloway, A. M., Toumpis, A. I., & Harvey, D. (2016). Evaluation of the synergistic erosion-corrosion behaviour of HVOF thermal spray coatings. Surface and Coatings Technology, 299, 37-48.
**e, Y., Planche, M. P., Raoelison, R., Liao, H., Suo, X., & Hervé, P. (2016). Effect of substrate preheating on adhesive strength of SS 316L cold spray coatings. Journal of Thermal Spray Technology, 25(1–2), 123-130.
Geng, Z., Hou, S., Shi, G., Duan, D., & Li, S. (2016). Tribological behaviour at various temperatures of WC-Co coatings prepared using different thermal spraying techniques. Tribology International, 104, 36-44.
Adnan Al-Bashir, A., Abdul Jawwad, K. A., & Shgair, K. A. (2009). Evaluating the Effects of High Velocity Oxy-Fuel (Hvof) Process Parameters on Wear Resistance of Steel-Shaft Materials. Jordan Journal of Mechanical and Industrial Engineering., 3(2), 157-160.
Fantozzi, D., Matikainen, V., Uusitalo, M., Koivuluoto, H., & Vuoristo, P. (2017). Chlorine- induced high temperature corrosion of Inconel 625 sprayed coatings deposited with different thermal spray techniques. Surface and Coatings Technology, 318, 233-243.
Ghazali, M. J., Forghani, S. M., Hassanuddin, N., Muchtar, A., & Daud, A. R. (2016). Comparative wear study of plasma sprayed TiO2 and Al2O3–TiO2 on mild steels. Tribology International, 93, 681-686.
Maestracci, R., Sova, A., Jeandin, M., Malhaire, J. M., Movchan, I., Bertrand, P., & Smurov, I. (2016). Deposition of composite coatings by cold spray using stainless steel 316L, copper and Tribaloy T-700 powder mixtures. Surface and Coatings Technology, 287, 1-8.
Janka, L., Norpoth, J., Trache, R., & Berger, L. M. (2016). Influence of heat treatment on the abrasive wear resistance of a Cr3C2NiCr coating deposited by an ethene-fuelled HVOF spray process. Surface and Coatings Technology, 291, 444-451.
Bhemuni, V., & Chalamalasetti, S. R. (2014). Statistical model for surface roughness in hard turning of AISI D3 steel. Jordan Journal of Mechanical and Industrial Engineering., 8(6), 393-401.
Ferreira, S. L. C., Bruns, R. E., Ferreira, H. S., Matos, G. D., David, J. M., Brandao, G. C., et al. (2007). Box-behnken design: An alternative for the optimization of analytical methods. AnalyticaChimicaActa, 597, 179–186.
Robert Heimann, B. (2010). Better quality control: stochastic approaches to optimize properties and performance of plasma-sprayed coatings. Journal of Thermal Spray Technology, 19, 765–778.
Vijayanand, P., Amitesh Kumar, K. R., Vijaya Kumar, A., Vinod Kumaran, P., & ArungalaiVendan, S. (2017). Characterizations of plasma sprayed composite coatings over 1020 mild steel. Journal of Mechanical Science and Technology., 31(10), 4747–4754.
Nahvi, S. M., & Jafari, M. (2016). Microstructural and mechanical properties of advanced HVOF-sprayed WC-based cermet coatings. Surface and Coatings Technology, 286, 95–102.
Author information
Authors and Affiliations
Corresponding author
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
About this article
Cite this article
Palani, V., Kumar, A., Vijaya kumar, K.R. et al. Investigations on the Performance Characteristics of Carbon Nano-tubes, Alumina and Titanium Dioxide Based Plasma Sprayed Coatings on AISI 1020 Steel. Int. J. Precis. Eng. Manuf. 22, 365–372 (2021). https://doi.org/10.1007/s12541-020-00458-x
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12541-020-00458-x