Abstract
A series of Co-Sn alloys was solidified. It was found that the as-cast microstructure of the Co-20.5at.%Sn alloy, which on the basis of literature reports has long been thought to be the eutectic composition, contains much primary phase besides lamellar eutectics. The cooling curve of this alloy contains two exothermic peaks. In contrast, when a Co-24.0at.%Sn alloy was solidified, an entire lamellar eutectic was obtained in the as-cast microstructure. Also, the thermal analyses indicate that there is only one solidification reaction in this alloy. It is suggested that the actual eutectic composition of the Co-Sn system is around Co-24.0at.%Sn, and the corresponding eutectic temperature is about 1385 K.
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs11669-009-9504-3/MediaObjects/11669_2009_9504_Fig1_HTML.gif)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs11669-009-9504-3/MediaObjects/11669_2009_9504_Fig2_HTML.jpg)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs11669-009-9504-3/MediaObjects/11669_2009_9504_Fig3_HTML.gif)
Similar content being viewed by others
References
K. Ishida, T. Nishizawa, The Co-Sn (Cobalt-Tin) System. J. Phase Equilib. Diffus 12(1), 88-93 (1991)
H. Comert, J. N. Pratt, The Thermodynamic Properties of Solid Cobalt-Tin Alloys. Thermochim. Acta 84, 273-286 (1985)
Y.V.V.R.S. Murty, T.Z. Kattamis, Structure of Highly Undercooled Cobalt-Tin Eutectic Alloy. J. Cryst. Growth 22(3), 219-224 (1974)
M.J. Li, K. Kuribayashi, Nucleation-Controlled Microstructures and Anomalous Eutectic Formation in Undercooled Co-Sn and Ni-Si Eutectic Melts. Metall. Mater. Trans. A 34(12), 2999-3008 (2003)
B. Wei, D. M. Herlach, F. Sommer, W. Kurz, Rapid Solidification of Undercooled Eutectic and Monotectic Alloys, Mater. Sci. Eng. A 173(1-2), 355-359 (1993)
Y. C. Liu, Lamellar Spacing and Mechanical Property of Undercooled Ti-45Al-2Cr-2Nb Alloy. Mater. Lett 57(15), 2262-2266 (2003)
Acknowledgment
The financial support from the National Natural Science Foundation of China under Grant No. 50571068 is greatly appreciated.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Liu, L., Li, J.F., Zhao, S. et al. Redetermination of the Eutectic Composition of the Co-Sn Binary Alloy. J. Phase Equilib. Diffus. 30, 242–245 (2009). https://doi.org/10.1007/s11669-009-9504-3
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11669-009-9504-3