Using the energy approach, a calculation model was built to determine the period of subcritical growth of a system of cracks in metal plates, subjected to long-term static tension and local electrochemical corrosion. The effect of a corrosive environment on the residual life of a plate with a system of periodic and doubly periodic cracks was evaluated.
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs11003-024-00823-5/MediaObjects/11003_2024_823_Fig1_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs11003-024-00823-5/MediaObjects/11003_2024_823_Fig2_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs11003-024-00823-5/MediaObjects/11003_2024_823_Fig3_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs11003-024-00823-5/MediaObjects/11003_2024_823_Fig4_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs11003-024-00823-5/MediaObjects/11003_2024_823_Fig5_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs11003-024-00823-5/MediaObjects/11003_2024_823_Fig6_HTML.png)
References
I. M. Dmytrakh, and V. V. Panasyuk, The Influence of Corrosive Environments on the Local Fracture of Metals at Stress Concentrators [in Ukrainian], Karpenko Physico-Mechanical Institute, Lviv (1999).
P. Arnoux, “Atomistic simulations of stress corrosion cracking,” Corr. Sci., 52, 1247–1257 (2010). https://doi.org/10.1016/j.corsci.2009.12.024
M. Alqahtani, A. Starr, and M. Khan, “Experimental and theoretical aspects of crack assisted failures of metallic alloys in corrosive environments – A review,” Materials Today: Proc., 66, Is. 4, 2530–2535 (2022). https://doi.org/10.1016/j.matpr.2022.07.075
Z. Chen, Y. Dai, and Y. Liu, “Life prediction of corrosion-fatigue based on a new crack growth rate model with damage and the extended finite element method,” Eng. Fract. Mech., 289, art. no. 109445 (2023). https://doi.org/10.1016/j.engfracmech.2023.109445
O. Ye. Andreikiv, I. Ya. Dolins’ka, A. R. Lysyk, and N. B. Sas, “Mathematical modeling of fracture processes in plates with systems of cracks under the action of long-term loads, high temperatures, and corrosive media,” J. of Math. Sci., 236, Is. 2, 212–223 (2019). https://doi.org/10.1007/s10958-018-4107-3
J. Hu, Y. Tian, H. Teng, L. Yu, and M. Zheng, “The probabilistic life time prediction model of oil pipeline due to local corrosion crack,” Theor. and Appl. Fract. Mech., 70, 10–18 (2014). https://doi.org/10.1016/j.tafmec.2014.04.002
A. M. Syrotyuk, and I. M. Dmytrakh, “Methods for the evaluation of fracture and strength of pipeline steels and structures under the action of working media. Part I. Influence of the corrosion factor,” Mater. Sci., 50, No. 3, 324–3391 (2014). https://doi.org/10.1007/s11003-014-9724-5
O. Ye. Andreikiv, V. R. Skal’s’kyi, I. Ya. Dolins’ka, and A. R. Dzyubyk, “Influence of corrosive hydrogenating media on the residual service life of structural elements in the maneuvering mode of operation,” Mater. Sci., 54, No. 1, 61–68 (2018). https://doi.org/10.1007/s11003-018-0158-3
N. Zviagin, S. Nastasiak, V. Kolodii, and Yu. Kolodii, “An analogue of the Griffiths problem for the propagation of corrosion-mechanical cracks,” Visnyk Lviv. Univ., Ser. Mekh.-Math., Is. 92, 111–117 (2021). https://doi.org/10.30970/vmm.2021.92.111-117
O. E. Andreikiv, I. Ya. Dolinska, S. V. Nastasiak, and M. S. Shefer, “Determination of the residual service life of a torsion bar under the influence of corrosive media,” Mater. Sci., 57, No. 5, 633–639 (2022). https://doi.org/10.1007/s11003-022-00589-8
N. Yadznak, “Generalization of the equivalent area method for the case of short fatigue cracks in a three-dimensional body,” Visnyk Lviv. Univ., Ser. Mekh.-Math., Is. 89, 134–141 (2020). http://publications.lnu.edu.ua/bulletins/index.php/mmf/issue/view/464
M. P. Savruk, Stress Intensity Factor in Bodies with Cracks [in Russian], Naukova Dumka, Kyiv (1988).
O. N. Romaniv, S. Ya. Yarema, G. N. Nikiforchyn, N. A. Makhutov, and M. M. Stadnyk, “Fatigue and cyclic crack resistance of structural materials,” Vol. 4 in: V. V. Panasyuk (Ed.) Fracture Mechanics and Strength of Materials [in Russian], Naukova Dumka, Kyiv (1990).
Author information
Authors and Affiliations
Corresponding author
Additional information
Translated from Fizyko-Khimichna Mekhanika Materialiv, Vol. 59, No. 5, 61–67, September–October, 2023.
Rights and permissions
Springer Nature or its licensor (e.g. a society or other partner) holds exclusive rights to this article under a publishing agreement with the author(s) or other rightsholder(s); author self-archiving of the accepted manuscript version of this article is solely governed by the terms of such publishing agreement and applicable law.
About this article
Cite this article
Andreikiv, O.Y., Dolinska, I.Y., Zviahin, N.S. et al. Determination of the Residual Life of a Plate with a System of Cracks Under the Action of Long-Term Static Load and Corrosive Environment. Mater Sci (2024). https://doi.org/10.1007/s11003-024-00823-5
Received:
Published:
DOI: https://doi.org/10.1007/s11003-024-00823-5