Abstract
The weathering and environmental factors to which components are exposed during their useful life can promote damage and, consequently, premature failure in service. Thus, through the morphological analysis of fracture surfaces, it is possible to identify the failure modes and the main fractographic aspects present on the fracture surface. From these data, it is possible to increase the knowledge of the behavior of the material in service or even to have information for preventive corrections in the processing and use of material. Fractographic studies of carbon fiber (CF)/thermoplastic matrix composites are still little explored in the literature and can bring important contributions to understanding the failure mode of this class of materials. The objective of this work is to study the fractographic aspects of CF/polyamide 6 (PA6) composite exposed to two different conditionings, that is, distilled water at 80 ºC and saline solution, tested in tensile. Scanning electron microscopy analyses showed that the CF/PA6 laminate has a good consolidation and an excellent CF/matrix interface. Plastic deformations and fiber bridging are present in the fracture surface of the unconditioned specimens. However, after conditioning in distilled water at 80 ºC, the matrix became more fragile and the interface weaker. The conditioning in saline solution was less aggressive due to the salt effect that decreased the water migration into the specimens. The fractographic study performed shows in detail the influence of environmental deterioration using accelerated weathering on the fracture surface of thermoplastic laminates tested in tensile.
Similar content being viewed by others
References
Yao S-S, ** F-L, Rhee KY et al (2018) Recent advances in carbon-fiber-reinforced thermoplastic composites: a review. Compos B Eng 142:241–250. https://doi.org/10.1016/j.compositesb.2017.12.007
Montagna LS, Morgado GFM, Lemes AP, Passador FR, Rezende MC (2022) Recycling of carbon fiber-reinforced thermoplastic and thermoset composites: A review. J Thermoplast Compos Mater 0(0):1–26. https://doi.org/10.1177/08927057221108912
Sauer M, Kuhnel M, Witten E (2020) Carbon fiber reinforced plastic (CFRP) market report: Trends, forecast and competitive analysis. Lucintel – Global Management Consulting & Market Research Firm. https://www.lucintel.com/
EASA: European Aviation Safety Agency (n.d.) www.easa.europa.eu/en
McKeen LW (2019) Chapter 7 - Polyamides (Nylons). The effect of UV light and weather on plastics and elastomers (fourth edition). Plastics Design Library 185–222. https://doi.org/10.1016/B978-0-12-816457-0.00007-1
Venoor V, Park JH, Kazmer DO, Sobkowicz MJ (2021) Understanding the effect of water in polyamides: A review. Polym Rev 61:598–645. https://doi.org/10.1080/15583724.2020.1855196
Kondo MY, Montagna LS, Morgado GFM, de Castilho ALG, Batista LAPS, Botelho EC, Costa ML, Passador FP, Rezende MC, Ribeiro MV (2022) Recent advances in the use of Polyamide-based materials for the automotive industry. Polímeros 32(2):e2022023. https://doi.org/10.1590/0104-1428.20220042
Alessi S, Pitarresi G, Spadaro G (2014) Effect of hydrothermal ageing on the thermal and delamination fracture behaviour of CFRP composites. Compos B Eng 67:145–153. https://doi.org/10.1016/j.compositesb.2014.06.006
Shan L, Hui Tao R, Yi Yan L, Mu Huan S (2011) Environmental degradation of carbon fiber reinforced polymer (CFRP) and steel bond subjected to hygrothermal aging and loading. Mater Sci Forum 675:559–562. https://doi.org/10.4028/www.scientific.net/MSF.675-677.559
Abdel-Monsef S, Renarta J, Carreras L, Maimía P, Turon A (2022) Environmental effects on the cohesive laws of the composite bonded joints. Compos Part A Appl Sci Manuf 155:106798. https://doi.org/10.1016/j.compositesa.2021.106798
Franco LAL, Graça MLA, Silva FS (2008) Fractography analysis and fatigue of thermoplastic composite laminates at different environmental conditions. Mater Sci Eng, A 488:505–513. https://doi.org/10.1016/j.msea.2007.11.053
Purslow D (1987) Matrix fractography of fibre-reinforced thermoplastics, Part 1. Peel failures. Composites 18(5):365–374. https://doi.org/10.1016/0010-4361(87)90360-0
Cândido GM, Rezende MC, Donadon MV, de Almeida SFM (2012) Fractografia de Compósito Estrutural Aeronáutico Submetido à Caracterização de Tenacidade à Fratura Interlaminar em Modo I. Polímeros 22(1):41–53. https://doi.org/10.1590/S0104-14282012005000019
Rezende MC (2007) Fractografia de Compósitos Estruturais. Polímeros 17(3):1–11. https://doi.org/10.1590/S0104-14282007000300003
Greenhalgh ES (2009) Failure analysis and fractography of polymer composites. ISBN 978–1–84569–217–9 (book)
Hashemi S, Kinloch AJ, Williamsv (1990) The analysis of interlaminar fracture in uniaxial fibre-polymer composites. Proc Royaç Soc A: Math Phys Eng Sci 427(1872):173–199. https://doi.org/10.1098/rspa.1990.0007
Schultheisz CR, Waas AM (1996) Compressive failure of composites, part I: Testing and micromechanical theories. Prog Aerosp Sci 32:1–42. https://doi.org/10.1016/0376-0421(94)00002-3
Montagna LS, Morgado GFM, Santos LFP, Guimarães A, Passador FR, Rezende MC (2023) Mechanical performance of carbon fiber/polyamide 6: comparative study between conditioning in distilled water with heating and saline solution. Submitted in Materials Research
ASTM D5229/D5229M-2020 - Standard test method for moisture absorption properties and equilibrium conditioning of polymer matrix composite material
ASTM D1141–98 - 2021 Standard practice for preparation of substitute ocean water
ASTM D3039/D3039M-08 - Standard test method for tensile properties of polymer matrix composite materials
Hein LRO, Campos KA, Caltabiano PCRO, Kostov KG (2013) A brief discussion about image quality and sem methods for quantitative fractography of polymer composites. Scanning 35:196–204. https://doi.org/10.1002/sca.21048
Purslow D (1988) Fractography of fibre-reinforced thermoplastics, Part 3. Tensile, compressive and flexural failures. Composites 19:5. https://doi.org/10.1016/0010-4361(88)90123-1
Psarski M, Pracella M, Galeski A (2000) Crystal phase and crystallinity of polyamide 6/functionalized polyolefin blends. Polymer 41(13):4923–4932. https://doi.org/10.1016/S0032-3861(99)00720-X
Pigłowski J, Gancarz I, Wlaźlak M, Kammer H-W (2000) Crystallization in modified blends of polyamide and polypropylene. Polymer 41(18):6813–6824. https://doi.org/10.1016/S0032-3861(00)00034-3
Kim KY, Ye L (2004) Interlaminar fracture toughness of CF/PEI composites at elevated temperatures: roles of matrix toughness and fibre/matrix adhesion. Compos Part A Appl Sci Manuf 35:477–487
Roulin-Moloney AC (1989) Fractography and failure mechanisms of polymers and composites. Elsevier
Hertzberg RW, Manson JA (1980) Microfractography of polymer fractures. Academic Press, Fatigue of Engineering Plastics, New York
Friedrich K, Walter R, Voss H, Karger-Kocsis J (1986) Effect of short fibre reinforcement on the fatigue crack propagation and fracture of PEEK matrix composites. Composites 17:205–216
Gamstedt EK, Östlund S (2001) Fatigue propagation of fibre-bridged cracks in unidirectional polymer-matrix composites. Appl Compos Mater 8:385–410. https://doi.org/10.1023/A:1012677604599
Sjogren A, Asp L, Greenhalgh E, Hiley MJ (2002) Interlaminar crack propagation in CFRP: Effects of temperature and loading conditions on fracture morphology and toughness. Composite Materials: Testing, Design, and Acceptance Criteria, Mar 26–27 2001(1416):235–252. Phoenix, AZ, United States. ASTM Special Technical Publication
Silva TC, Moraes DVO, Morgado GFM, Gonçalves VO, Costa DHS, Marques TPZ, Passador FR, Rezende MC (2022) Mechanical characterization and fractographic study of the carbon/PEI composite under static and fatigue loading. Mech Adv Mater Struct. https://doi.org/10.1080/15376494.2022.2134952
Purslow D (1981) Some fundamental aspects of composites fractography. Composites 12(4):241–247. https://doi.org/10.1016/0010-4361(81)90012-4
Acknowledgements and Funding
The authors thank the Brazilian Funding institutions Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES, 001) and Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq – Processes 305,123/2018–13, 10,196/2018–3, and 405,675/2018–6) for the financial support, and also the Federal Government Program ‘Rota 2030’ linked to the “Development of Skills for Design and Manufacturing of Tooling for Composite Parts” n° 27,194.03.03/2020.01–00 for the financial support; the Lightweight Structures Laboratory from IPT (Instituto de Pesquisas Tecnológicas do Estado de São Paulo) for the coordination, and also the Brazilian Funding Institutions FIPT (Fundação de Apoio do IPT), FUNDEP (Fundação de Desenvolvimento da Pesquisa) for the administrative support.
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Conflict of interest
No potential conflict of interest was reported by the author(s).
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Highlights
Fractographic analysis of CF/PA6 composites after environmental conditioning.
Rights and permissions
Springer Nature or its licensor (e.g. a society or other partner) holds exclusive rights to this article under a publishing agreement with the author(s) or other rightsholder(s); author self-archiving of the accepted manuscript version of this article is solely governed by the terms of such publishing agreement and applicable law.
About this article
Cite this article
Montagna, L.S., de Melo Morgado, G.F., Guimarães, A. et al. Fractographic study of thermoplastic composites based on carbon fiber/PA6 conditioned in heated distilled water and saline solution and tested in tensile. J Polym Res 30, 447 (2023). https://doi.org/10.1007/s10965-023-03826-z
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s10965-023-03826-z