Abstract
Changes in various properties of Hafnium Oxide (HfO2) high k-dielectric thin films, grown on Silicon (Si) substrate by 500 cycles and 1000 cycles of Atomic Layer Deposition (ALD) technique; having nominal thickness of around 50 nm and 120 nm were studied as a function of Low Energy Ion Beam (LEIB) irradiation. In this article, we have attentively studied (i) 350 keV Xe for 50 nm films and (ii) 275 keV Ne and 450 keV Kr for 120 nm films LEIB irradiation defect induced modifications in HfO2 thin films. The pristine and irradiated films were studied by various techniques. The variation of grain size as a function of low energy ion irradiation was measured by Field Emission Scanning Electron Microscopy (FESEM) while the substantial Root Mean Square (RMS) surface roughness and particle size distribution was measured by Atomic Force Microscopy (AFM). Structural changes studied using X-Ray Diffraction (XRD) revealed the change of state from amorphous to crystalline nature of the films for thickness < 100 nm while the samples with thickness > 100 nm changed from monoclinic crystal phase to orthorhombic. Systematic X-Ray Photoelectron Spectroscopy (XPS) study showed that deposited films are highly oxygen deficient (HfOx<2) and post-irradiation of films at high energy, having thickness > 120 nm, the films underwent complete oxidation leading to the formation of a new carbon compound CxHfyOz. Relative study of < 100 nm and > 100 nm films showed that, the 50 nm films has low resistivity compared to 120 nm thick films. So, films > 100 nm can be used in a Metal Oxide Semiconductor (MOS) device to reduce the leakage current.
Similar content being viewed by others
Data availability
Data can be made available on reasonable request.
References
B. Schmidt, K. Wetzig, Ion-Solid Interactions, Ion Beams in Materials Processing and Analysis (Springer, Vienna, 2012). https://doi.org/10.1007/978-3-211-99356-9_2
A.V. Krasheninnikov, K. Nordlund, J. Appl. Phys. 107, 71301 (2010)
J. Singh, H. Gupta et al., Mater. Sci. Semicond. Process. 108, 104885 (2020)
S.O. Kucheyev, J.S. Williams, C. Jagadish et al., Phys. Rev. B—Condens. Matter Mater. Phys. 67, 94115 (2003)
J. Singh, R.G. Singh et al., Org. Electron. 87, 105932 (2020)
D.K. Avasthi, G.K. Mehta, Mater. Sci. 145, 47 (2011)
W.J. Weber, E. Wendler, Modelling Effects of Radiation Damage, in Ion Beam Modification of Solids, vol. 61, ed. by W. Wesch, E. Wendler (Springer, Cham, 2016). https://doi.org/10.1007/978-3-319-33561-2_3
J.F. Ziegler, M.D. Ziegler, J.P. Biersack, Nucl. Instrum. Methods Phys. Res., Sect. B 268, 1818 (2010)
H. Wiedemann, Springer Cham 4, 3 (2015)
K. **, Y. Zhang, W.J. Weber, Synergistic effects of nuclear and electronic energy deposition on damage production in KTaO3. Mater. Res. Lett. 6, 531 (2018)
S.K. Singh, R. Singhal, Nucl. Instrum. Methods Phys. Res., Sect. B 407, 118 (2017)
P. Kumar, K. Mal, S. Kumar, I. Sulania, Surf. Interface Anal. 48, 969 (2016)
M. Kumar, P.G. Ganesan et al., Nanotechnology 19, 175606 (2008)
P. Kumar, Semicond. Sci. Technol. 31, 035014 (2016)
M. Kumar, T. Jangid et al., Nanoscale Res. Lett. 11, 1 (2016)
P. Kumar, U.B. Singh et al., Beilstein J. Nanotechnol. 5, 1864 (2014)
I. Sulania, D.C. Agarwal et al., Phys. Chem. Chem. Phys. 18, 20363 (2016)
P. Kumar, P. Jain, I. Sulania, Surf. Interface Anal. 48, 196 (2016)
D. Chiappe, A. Toma et al., Small 9, 913 (2013)
M. Liedke, A. Keller et al., Phys. Rev. B 87, 024424 (2013)
H. Liu, M. Li et al., Adv. Mater. 26, 2718 (2014)
M.K. Sharma, D.K. Mishra et al., J. Appl. Phys. 110, 063902 (2011)
R. Kumar, V. Kumar, Opt. Mater. 88, 320 (2019)
R.W. Johnson, A. Hultqvist, S. Bent, Mater. Today 17, 236 (2014)
S. Mueller, J. Mueller, A. Singh et al., Adv. Func. Mater. 22, 2412 (2012)
P. Kumar, G. Rodrigues et al., Pramana—J. Phys. 59, 805 (2002)
J.F. Ziegler, J.P. Biersack, M.D. Ziegler, Nuclear instruments and methods in physics research section B: beam interactions with materials and atoms. Nucl. Instrum. Methods Phys. Res. Sect. B: Beam Interact. Mater. Atoms 268, 1818 (2010)
I. Horcas et al., Rev. Sci. Instrum. 78, 013705 (2007)
P. Rauwel, E. Rauwel et al., J. Appl. Phys. 112, 104107 (2012)
K.M. Law, S. Budhathoki et al., Sci. Rep. 10, 18357 (2020)
S.K. Singh, V.V. Siva, P. Kumar, Appl. Phys. A 127, 524 (2021)
R. Kumar, V. Chauhan et al., J. Alloy. Compd. 831, 154698 (2020)
N. Manikanthababu et al., Nucl. Instrum. Methods Phys. Res. Sect. B: Beam Interact. Mater. Atoms 379, 230–234 (2016)
T. Tan et al., Chin. Phys. B 25, 117306 (2016)
W. Zhang et al., Nanoscale Res. Lett. (2017). https://doi.org/10.1186/s11671-016-1812-z
M. Liu et al., Surf. Sci. 576, 67 (2005)
C. Morant et al., Surf. Interface Anal. 16, 304 (1990)
C. Rodenbücher et al., Appl. Phys. Lett. 108, 252903 (2016)
S. Mandal et al., Materials Today: Proceedings 39, 1821 (2021)
C. Hu, K. **a et al., Energy Environ. Sci. 15, 1406 (2022)
Y. Bourezig, B. Bouabdallah et al., Int. J. Nanoelectron. Mater. 2, 63 (2009)
A. Vergara, E. Llobet, Front. Neuroeng. 4, 1 (2012)
Acknowledgements
The authors are thankful to Dr. S. Bhattacharya for hel** with the Atomic Layer Deposition (ALD) process for the growth of the films. Authors are indebted to Inter University Accelerator Centre (IUAC), New Delhi, India for providing the ion beam facility. The authors are also grateful to Dr. G. D. Verma, IIT Roorkee for providing the XPS measurements. For the AFM measurements, the authors would like to thank Dr. T. Som of Institiue of Physics (IoP), Bhubaneswar and the Central Research Facility (CRF) of Kalinga Institute of Industrial Technology (KIIT), Bhubaneswar. This work is supported by DST_FIST, New Delhi under grant #SR/FST/ET-1/2021/862.
Funding
DST_FIST, #SR/FST/ET-1/2021/862, Udai Singh.
Author information
Authors and Affiliations
Contributions
SM: Investigation, Visualization, Formal analysis, Writing—original draft. UPS: Conceptualization, Writing—review & editing, Supervision. PK: Resources, Supervision.
Corresponding author
Ethics declarations
Competing interest
The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper.
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Springer Nature or its licensor (e.g. a society or other partner) holds exclusive rights to this article under a publishing agreement with the author(s) or other rightsholder(s); author self-archiving of the accepted manuscript version of this article is solely governed by the terms of such publishing agreement and applicable law.
About this article
Cite this article
Mandal, S., Singh, U.P. & Kumar, P. Influence of low energy ion irradiation on oxygen deficient hafnium oxide (HfO2) thin films. J Mater Sci: Mater Electron 34, 1216 (2023). https://doi.org/10.1007/s10854-023-10614-4
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s10854-023-10614-4