Abstract
Inconel 718 is known to be among the most difficult-to-machine materials due to its special properties which cause the short tool life and severe surface damages. The properties, which are responsible for poor machinability, include rapid work hardening during machining; tendency to weld with the tool material at high temperature generated during machining; the tendency to form a built-up edge during machining; and the presence of hard carbides, such as titanium carbide and niobium carbide, in their microstructure. Conventional method of machining Inconel 718 with cemented carbide tool restricts the cutting speed to a maximum 30 m/min due to the lower hot hardness of carbide tool, high temperature strength and low thermal conductivity of Inconel 718. The introduction of new coated carbide tools has increased cutting speed to 100 m/min; nevertheless, the time required to machine this alloy is still considerably high. High speed machining using advanced tool material, such as CBN, is one possible alternative for improving the productivity of this material due to its higher hot hardness in comparison with carbide tool. This paper specifically deals with surface quality generated under high speed finishing turning conditions on age-hardened Inconel 718 with focus on surface roughness, metallographic analysis of surface layer and surface damages produced by machining. Both coated and uncoated CBN tools were used in the tests, and a comparison between surfaces generated by both tools was also discussed.
Similar content being viewed by others
References
Bailey JA, Jeelani S, Becker SE (1976) Surface integrity in machining AISI4340 steel. J Eng Ind 98(3):999–1007
Field M (1973) Surface integrity—a new requirement for improving reliability of aerospace hardware, Proceedings of 18th Annual National SAMPE Symposium
Sadat AB, Reddy MY (1992) Surface integrity of Inconel-718 nickel-base superalloy using controlled and natural contact length tools. Part I. Lubricated. Exp Mech 32(3):282–288
Sadat AB, Reddy MY (1993) Surface integrity of Inconel 718 nickel based superalloy using controlled and natural contact length tools. Part II. Unlubricated. Exp Mech 33(4):343–348
Arunachalam R, Mannan MA (2000) Machinability of nickel-based high temperature alloys. Mach Sci Technol 4(1):127–168
Ezugwu EO, Bonney J, Yamane Y (2003) An overview of the machinability of aeroengine alloys. J Mater Process Technol 134(2):233–253
Watmon TB, Anthony CI (2010) Coating cutting tools with hard substance lowers friction co-efficient and improves tool life—a review. In: Proceedings of the International MultiConference of Engineering and Computer Scientists. IMECS, Hong Kong, pp 17–19
Pawade RS, Suhas S, Joshi S, Brahmankar PK, Rahman M (2007) An investigation of cutting forces and surface damage in high-speed turning of Inconel 718. J Mater Process Technol 192–193:139–146
Sharman ARC, Amarasinghe A, Ridgway K (2008) Tool life and surface integrity aspects when drilling and hole making in Inconel 718. J Mater Process 200(1):424–432
Sharman ARC, Dewes RC, Aspinwall DK (2001) Tool life when high speed ball nose end milling Inconel 718. J Mater Process Technol 118(1–3):9–35
Kitagawa T, Kubo A, Maekawa K (1997) Temperature and wear of cutting tools in high-speed machining of Inconel 718 and Ti-6Al-6V-2Sn. Wear 202:142–148
Mitsuo A, Uchida S, Nihira N, Iwaki M (1998) Improvement of high-temperature oxidation resistance of titanium nitride and titanium carbide films by aluminum ion implantation. Surf Coat Technol 103–104:98–103
Desmaison J, Lefort P, Billy M (1979) Oxidation of titanium nitride in oxygen: behavior of TiN and TiN plates. Oxid Met 13(3):203–221
Zhou BM, Chen C, Huang Q, An Q (2009) Study on surface damages caused by turning NiCr20TiAl nickel-based alloy. J Mater Process Technol 209:5802–5809
Chou KH, Song C (2004) Tool nose radius effects on finish hard turning. J Mater Process Technol 148:259–268
Knuefermann MMW, Read RFJ, Nunn R, Clark IE, Fleming MA (2001) 22 nm Ra surface finish achieved with AMBORITE DBN 45 in ultra-precision turning of hardened steel. Ind Diam Rev No. 2:87–92
Connolly TM, Starink PA, Reed S (2003) Short crack initiation and growth at 600°C in notched specimens of Inconel718. Mater Sci Eng, A 340(1–2):139–154
Ma J, Wu M, Du Y, Chen S, ** W, Fu W, Yang L, Wen A (2009) Formation of nanocrystalline niobium carbide (NbC) with a convenient route at low temperature. J Alloy Comp 475(1–2):415–417
El-Wardany TI, Kishawy HA, Elbestawi MA (2000) Surface integrity of die material in high speed hard machining. Part 1: Micrographical analysis. J Manuf Sci Eng 122(4):620–631
Reed RC (2006) The superalloys: fundamentals and applications. Cambridge University Press
Baker SP (1993) The analysis of depth-sensing indentation data. Mater Res Soc Symp Proc 308:209–216
Isakov, E (2009) Cutting data for turning steel. Industrial Press, Inc
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Zhou, J., Bushlya, V., Avdovic, P. et al. Study of surface quality in high speed turning of Inconel 718 with uncoated and coated CBN tools. Int J Adv Manuf Technol 58, 141–151 (2012). https://doi.org/10.1007/s00170-011-3374-7
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00170-011-3374-7