Summary
The synthesis of a new BCT Fe phase was performed in Fe/Ir(100) superlattices grown by MBE. Magnetic properties of 57Fe/Ir(100) superlattices with 4 ml Fe and variable Ir thickness (2–30 Å) are investigated by 57Fe conversion electron Mössbauer spectroscopy in the 4.2–300 K temperature range. Two spectral components are evidence, related, respectively, to Fe atoms involved in the central part of the iron layers and at the interface between iron and iridium layers. The appearance of a high magnetic hyperfine splitting in the iron BCT structure above a volume threshold of 12 Å3 is evidenced. Marked differences are observed between the mean magnetic properties and the local ones suggesting strong relaxation effects.
Similar content being viewed by others
References
Andrieu S., Miecuch M., Hennet L., Hubsch J. and Snoeck E., Europhys. Lett., 26 (1994) 189.
Andrieu S., Lahatra Razafindrasima F., Snoeck E., Renevier H., Brunel M. and Piecuch M., Phys. Rev. B, 52 (1995) 9938.
Andrieu S., Snoek E., Arcade Ph. and Piecuch M., J. Appl. Phys., 77 (1994) 189.
Bauer Ph. and Marchal G., Proc. SIS, edited by I. Ortalli, Vol. 50 (Editrice Compositori, Bologna) 1996, p. 895.
Macedo W. A. and Keune W., Phys. Rev. Lett., 61 (1988) 475.
Shiga M., Phys. Status Solidi B, 43 (1971) K37.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Bauer, P., Andrieu, S. & Piecuch, M. Magnetic properties of 57Fe/Ir(100) superlattices. Il Nuovo Cimento D 18, 299–304 (1996). https://doi.org/10.1007/BF02458908
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF02458908
PACS
- 68.65
- Layer structures: multilayers, and superlattices (growth structure, and nonelectronic properties)