Abstract
Plasma ion nitriding is a flexible and multi-functional casehardening technique used in the given study for surface modifications of AISI M2 tool steel (0.9% C, 4.2% Cr, 5.0% Mo, 6.0% W, and 2.0% V). By varying the plasma treatment time from 1 to 4 hour and the filling gas pressure from 1 to 4 mbar, the surface nitriding was carried out in the abnormal glow region of a pulsed DC discharge. Pre-plasma treatment heating of the samples was performed by a heating unit; the substrate temperature was raised to 500°C, with the ram** rate of 15°C. The resultant microscopic changes in the surface properties of the plasma treated tool steel were studied with different surface characterization techniques such as X-ray Diffraction, Scanning Electron Microscopy and Vickers’s micro-hardness testing. These investigations confirmed the formation of a compound layer on the plasma exposed surface. It was observed that the layer thickness initially increases and then decreases with nitriding time. Similar results were obtained for increasing filling gas pressure. The X-ray Diffraction results showed a down-shift in the original diffraction peaks, which confirms the nitrogen diffusion into the exposed surface and a compound layer formation. A significant improvement in the surface hardness was also vivid, which might be due to the nitrogen diffusion and the formation of a compound layer on the target surface.
Similar content being viewed by others
References
Petrov, S.V. and Saakov, A.G., Technology and equipment for plasma surface hardening of heavy-duty parts, Mater. Manuf. Process., 2002, vol. 17, no. 3, pp. 363–378.
Wu, W.P., Chen, Z.F., and Cong, X.N., Corrosion properties of Pt coatings by double glow plasma, Surface Eng., 2012, vol. 28, no. 8, pp. 627–631.
Uma, D. and Mohanty, N., Plasma-nitriding of tool steels for combined percussive impact and rolling fatigue wear applications, Surf. Coat. Tech., 1998, vol. 107, pp. 55–64.
Chen, C.-L., Chiu, K.-F., Chen, Y.-R., Lin, H.-C., and Chen, C.C., Preparation and characterization of LiMn2O4 cathodes surface-modified by DC pulsed plasma treatment, Journal of the Chinese Chemical Society, 2012, vol. 59, pp. 1258–1263.
Lieberman, M.A., Principles of Plasma Discharges and Materials Processing, John Wiley and Sons, 1994, pp. 253–256.
Bogaerts, A., Neytsa, E., Gijbelsa, R., and Mullenb, J., Gas discharge plasmas and their applications, Spectrochim. Acta: Part B, 2002, vol. 57, pp. 609–658.
Lin, C.-C., Yen, Y.-C., Wu, H.-C., and Wu, N.-L., Synthesis of porous Si particles by metal-assisted chemical etching for Li-ion battery application, Journal of the Chinese Chemical Society, 2012, vol. 59, pp. 1226–1232.
Qiu, F. and Kujanpää, V., Surface hardening of AISI 4340 steel by laser linear oscillation scanning, Surface Eng., 2012, vol. 28, no. 8, pp. 569–575.
Novak, P., Dalibor Vojtech, and Serak, J., Wear corrosion resistance of a plasma nitride PM tool: steel alloyed with nobium, Surf. Coat. Tech., 2006, vol. 200, pp. 5229–5236.
Bacci, T., Borgioli, F., Galvanetto, E., and Pradelli, G., Glow-discharge nitriding of sintered stainless steels, Surf. Coat. Tech., 2012, vol. 139, pp. 251–256.
Sharma, M.K., Saikia, B.K., Phukan, A., and Ganguli, B., Plasma nitriding of austenitic stainless steel in N2 and N2-H2 dc pulsed discharge, Surf. Coat. Tech., 2006, vol. 201, no. 6, pp. 2407–2413.
Basu, A., Dutta Majumdar, J., Alphonsa, J., Mukherjee, S., and Manna, I., Corrosion resistance improvement of high carbon low alloy steel by plasma nitriding, Mater. Lett., 2008, vol. 62, pp. 3117–3120.
Grill, A., Cold Plasma in Material Fabrication, New York: IEEE press, 1993, pp. 134–136.
Elthalabawy, W.M. and Khan, T.I., Microstructural development of diffusion-brazed austenitic stainless steel to magnesium alloy using a nickel interlayer, Mater. Chem. Phys., 2010, vol. 61, pp. 703–712.
Thaiwatthana, S., Janta**, N., and Limthongkul, P., Residual stress measurement of low temperature plasma surface alloyed layer using X-ray diffraction techniques, Surface Eng., 2012, vol. 28, no. 4, pp. 273–276.
Guu, Y.H., Tsai, K.L., and Chen, L.K., An experimental study on electrical discharge machining of manganese-zinc ferrite magnetic material, Mater. Manuf. Process., 2007, vol. 22, no. 1, pp. 66–70.
Ahmadkhaniha, D. and Mahboubi, F., Effects of plasma nitriding on properties of electroless Ni-B coating, Surface Eng., 2012, vol. 28, no. 3, pp. 195–198.
Author information
Authors and Affiliations
Corresponding author
Additional information
The article is published in the original.
About this article
Cite this article
Naz, M.Y., Shukrullah, S., Ghaffar, A. et al. Surface morphology and mechanical strength of AISI M2 tool steel treated in abnormal glow region of plasma. Surf. Engin. Appl.Electrochem. 51, 58–64 (2015). https://doi.org/10.3103/S1068375515010093
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.3103/S1068375515010093