Abstract
Magnesium ferrite is a very important magnetic material due to its interesting magnetic and electrical properties and its chemical and thermal stability. Here we report on the magnetic and transport properties of epitaxial MgFe2O4 thin films grown on MgO (001) by molecular beam epitaxy. The structural properties and chemical composition of the MgFe2O4 films were characterized by X-Ray diffraction and X-Ray photoelectron spectroscopy, respectively. The nonsaturation of the magnetization in high magnetic fields observed for M (H) measurements and the linear negative magnetoresistance (MR) curves indicate the presence of anti-phase boundaries (APBs) in MgFe2O4. The presence of APBs was confirmed by transmission electron microscopy. Moreover, post annealing decreases the resistance and enhances the MR of the film, suggesting migration of the APBs. Our results may be valuable for the application of MgFe2O4 in spintronics.
Similar content being viewed by others
Introduction
Spinel ferrites, of the general formula MFe2O4 (M = Mn, Co, Ni, Mg, or Zn), have recently attracted considerable attention due to their interesting magnetic and electrical properties with enhanced chemical and thermal stability1,2,3. Among them, magnesium ferrite (MgFe2O4) is a soft magnetic n-type semiconductor with a partially inverse spinel structure. It has high sensitivity, good chemical stability and its band gap of ~ 2.0 eV makes it a suitable candidate for a wide range of applications in heterogeneous catalysis, adsorption, sensors, organic pollutants, lithium-ion batteries and photoelectrochemical water splitting4,5,6,7,8. Moreover, it has a high Curie temperature, adding it as a potential candidate in spintronics. So far, most studies have focused on MgFe2O4 nanoparticles4,5,6,7,8 or nanopillars9. However, less attention has been paid to epitaxial MgFe2O4 thin films although they are of great interest from both fundamental and practical perspectives. There have been relatively few attempts to grow MgFe2O4 thin films using pulsed laser deposition (PLD)10,11 or molecular beam epitaxy (MBE)12,13. None of them studied the effects of natural growth defects on the transport properties, such as anti-phase boundaries, which are expected to be common in oxide-based nanoelectronic and spintronic devices.
In this paper, we report on the magnetic and transport properties of epitaxial MgFe2O4 thin films grown on MgO (001) substrates by molecular beam epitaxy. The structural properties and chemical composition of the MgFe2O4 films were characterized by high resolution X-ray diffraction (XRD) and X-ray photoemission spectroscopy (XPS), respectively. The magnetic and transport properties were investigated using a physical property measurement system (PPMS). We observed a large non-saturated field and a negative linear magnetoresistance (MR) due to the presence of anti-ferromagnetic (AF) anti-phase boundaries in the MgFe2O4. The presence of the APBs was clearly verified by high resolution scanning transmission electron microscopy (HRSTEM) characterization. Moreover, our results also suggest that post annealing can cause migration of the APBs, which decreases the resistance and enhances the MR of the film.
Results
Sample preparation and characterization
MgFe2O4 thin films, with different thicknesses, were grown on (100) oriented MgO single crystal substrates in an oxygen–plasma-assisted molecular beam epitaxy (MBE) system. The base pressure of the system is better than 5 × 10−10 Torr. The substrates were chemically cleaned prior to insertion into the growth chamber and then cleaned in situ by annealing at 600°C in ultra-high vacuum (UHV) for 1/2 hour followed by further annealing in 1 × 10−5 Torr oxygen for 2 hours. Co-deposition was used to grow the thin films, i.e., material fluxes were produced by e-beam evaporation of separate pure MgO and metallic Fe sources. The growth rates for Fe and MgO were set to 0.6 Å/s and 0.3 Å/s, respectively. During growth, the substrate temperature was maintained at 300°C and the plasma source was operated with an oxygen partial pressure of 2 × 10−5 Torr and a current of 30 mA. After deposition, the samples were annealed at 300°C, with the same oxygen partial pressure, for 3 hours. Reflection high energy electron diffraction (RHEED) was employed to establish the growth mode. RHEED patterns for the MgO substrate and MgFe2O4 thin films (Fig. 1a and 1b) show vertical lattice rods and sharp Kikuchi lines, representative of a well-ordered and smooth surface, demonstrating the epitaxial growth of the MgFe2O4 films on MgO substrates. The structural properties and chemical composition were further investigated using a high resolution XRD system and XPS. Figure 1c shows the full range XRD, from 10 to 100 degrees, for a 114 nm thick MgFe2O4 film on a MgO substrate. Only the (200) and (400) peaks for the MgO substrate and the (008) and (004) peaks for the MgFe2O4 film are observed indicating the epitaxial growth of the MgFe2O4. The peak positions for MgO (400) and MgFe2O4 (008) located at 93.88° and 94.47° respectively, which are consistent with the well-established values. X-ray photoemission spectroscopy compositional analysis of the surface of the MgFe2O4 film is shown in Figure 1d. The Mg 2p and Fe 3p peaks have been consistently energy shifted to align the C 1s peak position to a binding energy (BE) of 284.7 eV. The XPS characterization indicates the atomic ratio of Mg : Fe is around 1 : 2. To investigate the interface between MgO and MgFe2O4, Figure 1e presents a low-magnification high angle angular dark field (HAADF) STEM image showing the whole thickness of a MgFe2O4 thin film (bright) on a MgO substrate (dark). The interfaces are sharp and defect free which further confirms MgFe2O4 films were epitaxially grown on the MgO substrates. A selected area electron diffraction (SAED) pattern of the interface between MgO and MgFe2O4 is shown in Fig. 1f. The red circles highlight the SAED spots for MgFe2O4 only and the blue circles highlight the SAED spots for the MgO and MgFe2O4. A small lattice mismatch is observed indicating the high quality of the epitaxial thin film.
Magnetic and transport properties
The magnetic properties of the MgFe2O4 thin films were investigated by means of a PPMS (Quantum Design). Temperature dependent M (H) loops of a 114 nm thick MgFe2O4 thin film are displayed in Fig. 2a. The external magnetic field is applied in the film plane along [100] direction. It is clear that the film is ferromagnetic in nature at all the temperatures. The coercivity increases with decreasing temperature. The measured magnetization at 300 K and at 1 T is around 115 emu/cm3, which is larger than the value reported for MgFe2O4 nano pillars9 but smaller than the value for MgFe2O4 grown on sapphire substrates11. Interestingly, the magnetization does not saturate in a field of 1T for all temperatures. Figure 2b shows M (H) loops for the same 114 nm thick MgFe2O4 thin film measured at room temperature with the external magnetic field applied along [100] and [110] directions. A significant difference between the M (H) loops for the two field directions is clearly observed. At room temperature, for a 114 nm thick MgFe2O4 thin film, with the field along the [100] direction, the coercivity field is 127 Oe. While when the field is along the [110] direction, the coercivity field increases to 216 Oe. Moreover, the M (H) loop for the field along [110] is much squarer than for field applied along [100]. It is clear that the easy axis, for the films grown, is along the [110] direction and hard axis is along the [100] direction. Figure 3a shows the magnetoresistance curves of a 114 nm thick MgFe2O4 thin film on a MgO substrate measured at different temperatures, where MR is defined as MR = R(H)/R(0)-1. The transport properties of MgFe2O4 were measured using the conventional four-probe method in the PPMS (Inset of Fig. 3a). A bias current of 4 µA was applied between the two outer contact electrodes along the [100] direction of the MgO substrate and a Keithley 2400 was used to measure the voltage drop. The external field was applied along the current direction. From Figure 3a, one can clearly see that the resistance shows a linear response to the external field at all temperatures. The MR ratio as a function of temperature is summarized in Figure 3b. It should be noted that the MR ratio increases with decreasing temperature. A MR ratio of −0.55% was obtained at room temperature and a MR of −3% was achieved at 80K. We would like to mention here that the shape of the MR curves is independent of temperature.
Discussion
Presence of APBs
The observed very large saturation field and negative linear MR can be attributed to and explained by the presence of antiphase boundaries, which are natural defects occurring during growth. The existence of APBs has been verified in numerous systems, for example, magnetite on MgO substrates14,15,16,17,18,19,20,21,22, Ba0.6Sr0.4TiO3 on (001) MgO23, Ba(Zr,Ti)O3 on (001) MgO24 and etc. The reported anti-phase boundaries in epitaxial Fe3O4 films grown on MgO substrates is a consequence of lattice parameter of Fe3O4 (8.397 Å) being almost twice of that of the MgO substrate (4.213 Å) and its spinel structure being of lower symmetry (Fd3m) than that of MgO (Fm3m). The presence of these APBs defects in Fe3O4 contributes to unusual magnetic and transport properties, such as the magnetization non-saturation even at very high field14,15, super-paramagnetic behavior in Fe3O4 films16,17, miscompensation of the spin moments at the surface and at the APBs contribute a giant magnetization18, a greater MR response across the AF-APBs19,20,21 and a large transversal MR22. Similar to Fe3O4, MgFe2O4 has a lattice parameter of (8.38 Å) and its spinel structure is of lower symmetry (Fd-3m). Therefore APBs are expected to form during growth of MgFe2O4 on MgO. To confirm the existence of the APBs, we show in Figure 4a a dark field cross-sectional HRTEM image of a 114 nm MgFe2O4 thin film on a MgO substrate. Several APBs are clearly visible. To highlight their presence, some APB domains are marked with dotted blue lines. Notably, MgFe2O4 is a partially inverse spinel. Thus, the spin configuration for atoms separated across APBs will be in a non-collinear configuration which means the spin states will be at least partially antiparallel. Therefore, the observed very large saturation field and negative linear MR in MgFe2O4 can be explained by the presence of AF-APBs. APB induced MR has been also observed in Ba0.6Sr0.4TiO323 and Ba(Zr,Ti)O324 films on MgO substrates. As can be done for Fe3O4, we schematically drew the spin structure disturbance due to the presences of AF-APBs, with and without an in-plane external field, as the inset of Figure 3a. The external field aligns the spins far from the boundary and the spins at the APBs rotate by an angle of φAF (marked in the inset of Figure 3b), where φAF is the angle between the spins at the left side of the APB and the external field. We can write the conductivity of the film as σ = σ0 + t02 cos2φAF, where σ0 is due to spin-dependent scattering at the interface without an external field and the second term is dependent on the MR effect21. The MR ratio for MgFe2O4 is around half that for Fe3O4, for the same thickness, indicating the AF APBs in MgFe2O4 are not as sharp as those in Fe3O4 and the exchange stiffness for the AF exchange interaction at the boundaries is not as strong as for Fe3O4. The underlying reason is that MgFe2O4 is a partially inverse spinel. φAF may not be zero in the absence of an external field. According to Ref. 14, the equation M = Ms (1-b/Hn) can be used to describe the approach towards saturation, of the magnetization (M) as a function of field, a value for the exponent (n) near 0.4 was obtained for MgFe2O4. This value is smaller than that for Fe3O4 (0.5) but it is almost the same as for NiFe2O4 films25.
To study effect of strain on APB formation, we prepared 4 sets of MgFe2O4 films in different strain states. The thicknesses of those 4 sets of MgFe2O4 films are around 114 nm (S1), 100 nm (S2), 90 nm (S3) and 60 nm (S4), respectively. Figure 4b shows XRD spectra for those 4 sets of MgFe2O4 films. To calculate the strain for those films, first the out-of-plane lattice constant a⊥ is calculated with , where dhkl is the spacing of lattice planes with the Miller indices (hkl), θ is the corresponding Bragg angle of the films, λ the wavelength of X-rays used and n is an integer. The calculated out-of-plane lattice constants a⊥ are 8.379 Å (S1), 8.377 Å (S2), 8.373 Å (S3) and 8.368 Å (S4), respectively. Thus, the corresponding strains for the films (e) are 0.1%, 0.07%, 0.03% and 0.004%, respectively, which can be calculated from . Where a0 is the lattice constant of MgFe2O4 (8.38 Å). Figure 4c shows R-T curves for those 4 sets of MgFe2O4 films. The resistivity of the films decreases with decreasing strain. The underline physics is that the APB domain size increases with decreasing strain. To confirm this, we estimated the APB domain size δ from the XRD data using δ = 0.9λ/(B cosθ), where B is the half-width value of the XRD peaks. The estimated APB domain sizes for those 4 sets of MgFe2O4 films are 12 nm, 18 nm, 21 nm and 29 nm, respectively. The strain as a function of grain size is summarized in Fig. 4d. One can see that with decreasing the strain, the APB domain size increases which results in the decrease in the resistivity.
Effect of post annealing on electrical properties of MgFe2O4
To investigate the effect of post annealing, in the presence oxygen, on the electrical properties of MgFe2O4 films, Figure 5a shows R-T curves for an as-grown 114 nm thick MgFe2O4 film (black line) and after annealing in an oxygen partial pressure of 2 × 10−5 Torr at 300°C for 3 hours (red line). Post annealing significantly decreases the resistance of the samples. At room temperature, the resistance for an as-grown sample was 5200 Ω which decreased to 2600 Ω after annealing. Post annealing also reduces the activation energy (Ea) of the sample. The R-T plots were fitted with the relationship . The activation energies for the as-grown sample and the sample after annealing were 76.4 meV and 67.1 meV, respectively. We also measured the MR of the as-grown MgFe2O4 sample (Figure 5b). It was found that post annealing also increases the MR ratio. The effect of post annealing can be understood as follows. First, the APBs in MgFe2O4 may migrate during annealing. It has been shown in Fe3O4 that post annealing at 300°C is sufficient to cause the migration of the APBs26 which increases the APB domain size and decreases the resistance and activation energy of the films21. Therefore, it is reasonable to believe that APBs in MgFe2O4 can also migrate during annealing. Figure 5c shows XRD data for the as-grown 114 nm thick MgFe2O4 film (black line) and after annealing in an oxygen partial pressure of 2 × 10−5 Torr at 300°C for 3 hours (red line). The half-width value of the MgFe2O4 peak decreases after annealing, indicating an increase in the APB domain size. Another possible reason is that post annealing may modify the oxygen vacancies and nanodomain structures in MgFe2O4 which also will affect the resistivity and MR of the sample27,28.
In summary, we investigated the magnetic and transport properties of epitaxial MgFe2O4 thin films grown on MgO (001) substrates. Large saturation fields and a linear negative MR were observed indicating the presence of APBs in MgFe2O4. The existence of APBs was further directly confirmed by HRSTEM characterization. The migration of APBs was also discussed. Our results may be valuable for the future application of MgFe2O4 in spintronics.
Methods
MgFe2O4 thin films with different thicknesses were grown on MgO (100) oriented single crystal substrates using an oxygen–plasma-assisted molecular beam epitaxy system. Co-deposition was used to grow the thin films. MgFe2O4 films in different strain states were prepared by controlling the film thickness. The magnetic and transport properties were examined by means of a physical property measurement system (PPMS, Quantum Design). X-ray photoelectron spectrometry measurements were performed in an Omicron Nanotechnology Spectroscopy system equipped with an Ar ion miller in the preparation chamber.
References
**ang, X., Fan, G., Fan, J. & Li, F. Porous and superparamagnetic magnesium ferrite film fabricated via a precursor route. J. Alloy Comp. 499, 30 (2010).
Bárcena, C. et al. Zinc ferrite nanoparticles as MRI contrast agents. Chem. Commun. 19, 2224 (2008).
Bao, N. et al. Controlled Growth of Monodisperse Self-Supported Superparamagnetic Nanostructures of Spherical and Rod-Like CoFe2O4 Nanocrystals. J. Am. Chem. Soc. 131, 12900 (2009).
Hamdeh, H. H. et al. Magnetic properties of partially-inverted zinc ferrite aerogel powders. J. Appl. Phys. 81, 1851 (1997).
Busca, G., Finocchio, E., Lorenzelli, V., Trombetta, M. & Rossini, S. A. IR study of alkene allylic activation on magnesium ferrite and alumina catalysts. J. Chem. Soc. Faraday Trans. 92, 4687 (1996).
Su, N. R. et al. Fabrication of MgFe2O4–ZnO heterojunction photocatalysts for application of organic pollutants. Mater. Lett. 122, 201 (2014).
Pan, Y. et al. MgFe2O4 nanoparticles as anode materials for lithium-ion batteries. Electrochimica Acta 109, 89 (2013).
Hou, Y., Zuo, F., Dagg, A. & Feng, P. Three-Dimensional Branched Cobalt-Doped a-Fe2O3 Nanorod/MgFe2O4 Heterojunction Array as a Flexible Photoanode for Efficient Photoelectrochemical Water Oxidation. Angew. Chem. Int. Ed. 52, 1248 (2013).
Kim, D. H., Aimon, N. M., Sun, X. & Ross, C. A. Compositionally Modulated Magnetic Epitaxial Spinel/Perovskite Nanocomposite Thin Films. Adv. Funct. Mater. 24, 2334 (2014).
Kim, K. S. et al. Influence of oxygen partial pressure on the epitaxial MgFe2O4 thin films deposited on SrTiO3 (1 0 0) substrate. J. Alloy Comp. 503, 460 (2010).
Gupta, R. K. & Yakuphanoglu, F. Epitaxial growth of MgFe2O4 (111) thin films on sapphire (0001) substrate. Mater. Lett. 65, 3058–3060 (2011).
Cheng, J., Lazarov, V. K., Sterbinsky, G. E. & Wessels, B. W. Synthesis, structural and magnetic properties of epitaxial MgFe2O4 thin films by molecular beam epitaxy. J. Vac. Sci. Technol. B 27, 148 (2009).
Lee, D. S. et al. The magnetic properties of strained and relaxed Fe3−xMgxO4 ferrite films on MgO(001) and SrTiO3(001) by molecular beam epitaxy. J. Appl. Phys. 101, 09M523 (2007).
Margulies, D. T. et al. Origin of the Anomalous Magnetic Behavior in Single Crystal Fe3O4 Films. Phys. Rev. Lett. 79, 5162 (1997).
Margulies, D. T. et al. Anomalous moment and anisotropy behavior in Fe3O4 films. Phys. Rev. B 53, 9175 (1996).
Eerenstein, W., Hibma, T. & Celotto, S. Mechanism for superparamagnetic behavior in epitaxial Fe3O4 films. Phys. Rev. B 70, 184404 (2004).
Voogt, F. C. et al. Superparamagnetic behavior of structural domains in epitaxial ultrathin magnetite films. Phys. Rev. B 57, R8107 (1998).
Arora, S. K. et al. Giant magnetic moment in epitaxial Fe3O4 thin films on MgO(100). Phys. Rev. B 77, 134443 (2008).
Arora, S. K., Sofin, R. G. S. & Shvets, I. V. Magnetoresistance enhancement in epitaxial magnetite films grown on vicinal substrates. Phys. Rev. B 72, 134404 (2005).
Eerenstein, W., Palstra, T. T. M., Saxena, S. S. & Hibma, T. Spin-polarized transport across sharp antiferromagnetic boundaries. Phys. Rev. Lett. 88, 247204 (2002).
Wu, H. C. et al. Probing One Antiferromagnetic Antiphase Boundary and Single Magnetite Domain Using Nanogap Contacts. Nano Lett. 10, 1132 (2010).
Wu, H. C. et al. Transversal magneto-resistance in epitaxial Fe3O4 and Fe3O4/NiO exchange biased system. Appl. Phys. Lett. 101, 052402 (2012).
Jiang, J. C., Lin, Y., Chen, C. L., Chu, C. W. & Meletis, E. I. Microstructures and surface step-induced antiphase boundaries in epitaxial ferroelectric Ba0.6Sr0.4TiO3 thin film on MgO. J. Appl. Phys. 91, 3188 (2002).
He, J. et al. Twin-coupled domain structures in epitaxial relaxor ferroelectric Ba(Zr,Ti)O3 thin films on (001) MgO substrate. Phil. Mag. Lett. 89, 493 (2009).
Venzke, S. et al. Epitaxial growth and magnetic behavior of NiFe2O4 thin films. J. Mater. Res. 11, 1187 (1996).
Eerenstein, W., Celotto, S., Palstra, T. T. M. & Hibma, T. Diffusive motion of antiphase domain boundaries in Fe3O4 films. Phys. Rev. B 68, 014428 (2003).
Ruiz-Zepeda, F. et al. Nanodomain induced anomalous magnetic and electronic transport properties of LaBaCo2O5.5+δ highly epitaxial thin films. J. Appl. Phys. 115, 024301 (2014).
Liu, M., Ma, C. R., Enriquez, E., Xu, X., Bao, S. Y. & Chen, C. L. Effect of Annealing Ambient on Electrical Properties of LaBaCo2O5.5+δ Thin Films. J. Nano Res. 27, 25 (2014).
Acknowledgements
This work was supported by Bei**g Institute of Technology Research Fund Program for Young Scholars, Science Foundation of Ireland (SFI) under Contract No. 06/IN.1/I91, National Plan for Science and technology (Nos. NPST 1598-02 and NPST 1466-02) of King Abdulaziz City for Science and Technology. H.C.W., MA.A. and MO.A. thank Saudi Aramco for the financial support (project No. 6600028398). O. M. and A. S. acknowledge the financial support by the Bolashak Program funded by the Kazakhstan government.
Author information
Authors and Affiliations
Contributions
H.C.W. and MOH.A. conceived the study. O.M., A.S. and C.C. grew the sample. H.C.W. performed the magnetic and transport measurements. A.K., A.M. and H.Z.Z. carried out the STEM measurements. MOU. A. and I.V.S. gave scientific advice. H.C.W. wrote the manuscript. All authors discussed the results and commented on the manuscript.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Rights and permissions
This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivs 4.0 International License. The images or other third party material in this article are included in the article's Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder in order to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by-nc-nd/4.0/
About this article
Cite this article
Wu, HC., Mauit, O., Coileáin, C. et al. Magnetic and transport properties of epitaxial thin film MgFe2O4 grown on MgO (100) by molecular beam epitaxy. Sci Rep 4, 7012 (2014). https://doi.org/10.1038/srep07012
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep07012
- Springer Nature Limited
This article is cited by
-
Unusual dielectric properties of hollow magnesium ferrite nanospheres: a potential lightweight microwave absorber
Journal of Materials Science (2022)
-
Growth and magnetic properties of spin coated Co0.6Zn0.4Mn0.3Fe1.7O4 ultrathin films on silicon (100), (110) and (111) substrates
Journal of Materials Science: Materials in Electronics (2018)
-
MgO/Cu2O Superlattices: Growth of Epitaxial Two-Dimensional Nanostructures
Journal of Electronic Materials (2016)