Abstract
Van der Waals (vdW) heterodiodes based on two-dimensional (2D) materials have shown tremendous potential in photovoltaic detectors and solar cells. However, such 2D photovoltaic devices are limited by low quantum efficiencies due to the severe interface recombination and the inefficient contacts. Here, we report an efficient MoS2/AsP vdW hetero-photodiode utilizing a unilateral depletion region band design and a narrow bandgap AsP as an effective carrier selective contact. The unilateral depletion region is verified via both the Fermi level and the infrared response measurements. The device demonstrates a pronounced photovoltaic behavior with a short-circuit current of 1.3 μA and a large open-circuit voltage of 0.61 V under visible light illumination. Especially, a high external quantum efficiency of 71%, a record high power conversion efficiency of 9% and a fast response time of 9 μs are achieved. Our work suggests an effective scheme to design high-performance photovoltaic devices assembled by 2D materials.
Similar content being viewed by others
Introduction
Photodetectors based on two-dimensional (2D) layered materials have been widely studied since the discovery of graphene due to their atomic layer thicknesses, strong light-matter interactions and layer-dependent electronic and optical properties1,2,3,4,39. MoS2 is a promising 2D material for high-performance visible photodetectors9,11, and AsP is a typical p-type 2D semiconductor with a narrow bandgap of 0.2–0.3 eV in bulk19,20,40. Thick MoS2 flakes with weak p-type conduction and thick AsP flakes are exfoliated to build the van der Waals pp+ heterodiode. The MoS2/AsP heterodiode exhibits a gate-tunable backward-like diode behavior with a current rectification ratio over 6 × 103. Upon 520 nm laser illumination, the heterodiode exhibits a pronounced photovoltaic effect with a short-circuit current as high as 1.3 μA and a large open-circuit voltage of 0.61 V, enabling an ultrahigh photocurrent to dark current ratio over 1 × 106. Specifically, a high responsivity of 0.3 A W−1 and a high external quantum efficiency of 71% are obtained under zero bias. Remarkably, a high power conversion efficiency of 9% and a fast response time of 9 μs are achieved, which, to the best of our knowledge, are the highest values ever reported for photovoltaic detectors based on 2D vdWHs24,25.
Results
Device characterizations and electrical properties
Figure 1a shows the schematic of the fabricated MoS2/AsP vdWHs device. Immediately after the fabrication process, the device was coated by a thin PMMA layer to protect it from oxidation by oxygen in the air. The MoS2 flake is placed on the AsP flake for better light absorption owing to a much larger bandgap value. The heavily p-doped Si substrate is used as a back gate to tune the carrier densities in each flake. The metal on the AsP side is defined as drain electrode while that on MoS2 side as source electrode. Supplementary Fig. 2a presents the optical image of the completely fabricated MoS2/AsP vdWHs device, where we can see both the MoS2 and AsP flakes are relatively thick. In order to investigate the properties of the individual MoS2, AsP flakes and the heterodiode separately, each of the MoS2 and AsP flakes are wired with two electrodes. Figure 1b shows the line scan profile of the heterostructure from the atomic force microscope (AFM) image, and the inset is the AFM image of the fabricated device. No air bubbles except for some surface contaminant can be seen in overlap** heterojunction region, indicating a good interface quality of the heterostructure. The thicknesses of MoS2 and AsP flakes are estimated to be 66 and 59 nm, respectively. The crystalline quality of MoS2, AsP and heterostructure were examined by Raman characterization (Supplementary Fig. 2b). Two strong peaks are observed at 385 and 410.5 cm−1 in the Raman spectrum of MoS2 flake, representing the in-plane vibration mode \(E_{2{\mathrm{g}}}^1\) and out-of-plane vibration mode \(A_{1{\mathrm{g}}}\), respectively33. For AsP flake, three main peaks are located at 226, 236, and 252 cm−1, corresponding to the \(A_{\mathrm{g}}^1\), \(B_{\mathrm{g}}^2\), and \(A_{\mathrm{g}}^2\) modes, respectively19. No peak shift or degradation is observed in the spectrum of the heterojunction region compared to the peaks from the individual MoS2 flake, indicating the high crystalline quality of the junction region. The Raman peaks of the AsP component in the junction region almost disappears, most likely due to limited input light reaching the AsP flake owing to the thick MoS2.
The electrical characteristics of the MoS2/AsP vdWHs device are measured first in an ambient environment. Interestingly, a large drain current over 10 μA at negative bias and a small current of several nA at positive bias are observed in Fig. 1c, indicating a backward-like diode is formed, which is contrary to one’s expectations at first glance. Since few layer MoS2 (with thickness of several nanometers) is a typical n-type 2D semiconductor and AsP is an intrinsically p-type, a normal pn junction forward diode is often observed when these two materials are stacked to build the heterojunction. To understand the mechanism of this contrary electrical behavior of the MoS2/AsP vdWHs diode, the electrical transport of both the individual MoS2 and AsP field effect transistors (FET) are separately measured. As shown in Supplementary Fig. 3, the transfer curve of the thick MoS2 FET exhibits an abnormal light p-type conduction behavior with a very weak gate modulation of the channel carrier density. The p-type conduction of thick MoS2 flakes (with thickness larger than 50 nm) is further verified via a systematic investigation of MoS2 FETs with different flake thicknesses (Supplementary Fig. 15 and Note 4). The light p-type conduction of thick MoS2 here may be attributed to the impurities-induced do** effect or the defect-induced do** effect (e.g., S adatoms)41,42. The weak gate control is likely due to the thick MoS2 channel. In addition, the nonlinear I–V curves of MoS2 FET indicate a Schottky contact between Cr metal and MoS2. The transfer curve of the AsP FET (Supplementary Fig. 4a) shows a large channel current and strong p-type conduction over the gate voltage range from −60 to 60 V with mild modulations, which means the Fermi level is close to the valance band maximum of AsP and the hole density is high. The linear I–V curves of AsP FET (Supplementary Fig. 4b, c) indicate an Ohmic contact between Cr metal and AsP. Based on these results, we can conclude that a pp+ heterojunction is formed in this MoS2/AsP vdWHs diode. The Fermi level position is vital in the operation of this backward-like diode. The gate-tunable I–V curves of the MoS2/AsP vdWHs diode are also measured and shown in Fig. 1d and Supplementary Fig. 5. It is interesting that the positive current monotonically increases while the negative current is almost unchanged when swee** Vg from −60 to 60 V. This suggests that the gate modulation of diode positive current results from the modulation of hole concentration in AsP, which influences the probability of hole tunneling through the heterojunction. The gate-dependent rectification ratio is shown in the inset in Fig. 1d. A high rectification ratio over 6 × 103 is obtained at Vg = −60 V. The rectification ratio decreases fast at the negative Vg and then saturates near to 1 at the positive Vg with increasing Vg, showing a gate-tunable current rectifying of the MoS2/AsP vdWHs diode.
Device operation mechanism and verification of unilateral depletion region
As above state, the relative position of Fermi level determines the operation of this pp+ heterojunction. Thus, kelvin probe force microscopy (KPFM) technique is used to measure the surface potential of both layers, from which the Fermi level difference can be obtained. To accurately obtain the surface potential, we assembly a clean MoS2/AsP heterostructure with the similar layer thicknesses (Supplementary Fig. 6). As shown in Fig. 2a, b, the Fermi level of AsP is ~41 meV higher than that of MoS2. Based on these results and the band structures of thick MoS2 and AsP layers (Supplementary Fig. 7)40,43, the energy band alignments of the MoS2/AsP vdWHs diode at different bias conditions are depicted in Fig. 2c–f. In equilibrium state, after MoS2 and AsP are brought in physical contact with each other, the minority electrons in AsP will move into MoS2, creating more holes in AsP. As a result, a hole accumulation region is formed at AsP side whereas a wide depletion region formed at the MoS2 side. In other words, a heterojunction with unilateral depletion region in MoS2 is formed. At small negative bias −0.5 V < Vds < 0 V, holes injected from the MoS2 side are hindered by both the large heterojunction barrier and the Schottky barrier, while minority electrons are injected from the AsP side, thereby leading to a small current magnitude as shown in Fig. 1c. At large negative bias Vds < −0.5 V, both the heterojunction barrier and the Schottky barrier are reduced. Thus, holes are easily injected into MoS2 and then cross over the heterojunction barrier, forming a large hole-dominant current as shown in Fig. 1c. At positive bias Vds > 0 V, although the holes are easily injected into AsP, they are blocked by the large valance band offset (~0.8 eV) at the MoS2/AsP interface. Meanwhile the electrons can hardly be injected into MoS2 because of the large Schottky barrier for electrons. Accordingly, the current is low at positive bias as shown in Fig. 1c.
To further confirm the unilateral depletion region is formed in this MoS2/AsP vdWHs pp+ heterodiode, an electrical I–V curve and infrared (IR) photovoltaic response method are used to distinguish the different band structures of the pp+ and pn heterojunctions. A normal MoS2/AsP pn heterodiode is fabricated as a control by choosing a thin MoS2 (thickness of 9 nm) and AsP (thickness of 21 nm) flakes (Supplementary Fig. 16). As shown in Fig. 3a, for the normal MoS2/AsP pn heterodiode, both the n-type MoS2 and p-type AsP are partially depleted (bilateral depletion region), resulting in a built-in electric field with direction pointing to AsP side. Therefore, a regular forward diode behavior is observed, as shown in Fig. 3b. When an IR light is incident, the photogenerated electrons in AsP can easily cross over the heterointerface due to the small conduction band offset, thus a negative short-circuit current is formed in this normal MoS2/AsP pn heterodiode, as shown in Fig. 3c. In contrast; in the MoS2/AsP pp+ heterodiode with unilateral depletion region, since the MoS2 is hole-depleted and AsP is hole-accumulated, the direction of the built-in electric field is pointing towards the MoS2 side, opposite to that in MoS2/AsP pn heterodiode. Therefore, an abnormal backward-like diode behavior is observed, as shown in Fig. 3e. Under IR illumination, the photogenerated holes are blocked by the large valance band offset, resulting in no IR photovoltaic response, as shown in Fig. 3f. Both the I–V curves and the IR photovoltaic response definitely confirm that our MoS2/AsP pp+ heterodiode has a unilateral depletion region in its band structure.
High efficiency and fast photovoltaic response of the MoS2/AsP vdWHs diode
Next, we focus on the photoresponse properties of the MoS2/AsP vdWHs diode with unilateral depletion region and evaluate its performance in photovoltaic detectors in visible wavelength range. All the photoresponse measurements are conducted at zero gate voltage (Vg = 0 V) unless otherwise stated. Figure 4a shows the Ids–Vds curves of the MoS2/AsP vdWHs diode under dark and 520 nm laser illumination, respectively. Obviously, the curve is upshifted under illumination, exhibiting a distinct photovoltaic response. A high short-circuit current Isc of 1.3 μA and a large open-circuit voltage Voc of 0.61 V are obtained under the power density of 108.8 mW mm−2 corresponding to 100× AM 1.5 intensity. The photocurrent to dark current ratio is over 1 × 106 at zero bias, showing an ultrahigh signal-to-noise ratio. As a comparison, no obvious visible photovoltaic response is observed in the normal MoS2/AsP pn heterodiode (Supplementary Figs. 16–19). The output electrical power Pel, which describes the electricity generation capability of a photovoltaic detector or solar cell, is defined as Pel = Ids·Vds. The gray rectangle region in Fig. 4a indicates where the maximum electrical power Pmax can be obtained. The fill factor (FF) and power conversion efficiency (PCE) can be calculated as follows: FF = Pmax/Isc·Voc, PCE = Pmax/Pin, where Pin is the incident optical power25. A Pmax of 0.39 μW, a FF of 0.5 and a PCE of 9% are achieved under the power density of 108.8 mW mm−2 or incident power of 4.35 μW. The large PCE, to the best of our knowledge, is the highest value ever reported for photovoltaic detectors based on 2D vdWHs24,25. We are aware that absorption efficiency is thickness-dependent, thus the quantum efficiency and power conversion efficiency are thickness-related. To investigate the effect of thickness on the device performance, six MoS2/AsP heterojunction devices with different layer thicknesses (Supplementary Fig. 21) are fabricated according to the conduction type of MoS2 and AsP flakes, as classified in the Supplementary Table 1 and Note 5. Via comprehensive comparison of the photovoltaic response of the six devices (Supplementary Figs. 22–31 and Table 2), it can be concluded that the thickness-related absorption efficiency of MoS2 is not the major reason for the large performance variation. Instead, the thickness-dependent band profile of the heterojunction is the key factor determining the photovoltaic efficiency of the MoS2/AsP heterodiode, as detailed below.
To further investigate the photovoltaic response of the MoS2/AsP vdWHs diode, power dependent photoresponse are measured. As shown in Fig. 4b and Supplementary Fig. 8, with increasing the optical power, the I–V curves keep on shifting upward. Thus the output electrical power Pel are increased as shown in Fig. 4c. From Fig. 4d, the short-circuit current Isc increases almost linearly with optical power (Isc ∝ P1.05 by power law fitting), whereas open-circuit voltage Voc shows a logarithmic relationship with optical power (Supplementary Fig. 14 and Note 3). Figure 4e displays the power dependent fill factor (FF) and power conversion efficiency (PCE). Both the FF and PCE decrease with decreasing incident power. Nevertheless, a PCE greater than 1% is still obtained at power density as low as 0.109 mW mm−2, corresponding to an incident power of 4.25 nW. To quantitatively evaluate the performance of the MoS2/AsP vdWHs photovoltaic detector, responsivity and external quantum efficiency (EQE) are calculated at zero drain bias. The responsivity is defined as R = Iph/Pin·A, where Iph is the net photocurrent, A is the junction area of the vdWHs device. EQE is the ratio of collected charge carriers to incident photons and can be calculated by EQE = Isc·h·c/e·λ·Pin, where h, c, λ are the Planck’s constant, the speed of light and wavelength of the incident laser, respectively. A responsivity of 0.3 A W−1 and EQE of 71% are obtained at power density of 108.8 mW mm−2. Considering the large power variation range (three orders of magnitudes), the responsivity and EQE of the MoS2/AsP vdWHs photovoltaic detector is relatively robust, showing a good linear dynamic range. The gate modulated photovoltaic response of the MoS2/AsP vdWHs diode are also measured and provided in Supplementary Fig. 9 and Note 2.
The mechanism of the enhanced photovoltaic response of the device under 520 nm laser illumination can be explained by the energy band diagram of the MoS2/AsP vdWHs diode. As shown in Fig. 5a, when the device is under 520 nm illumination, most of the electron-hole pairs are generated in the top MoS2 channel due to the relatively thick MoS2 flake. Under the large built-in electric field in the MoS2 unilateral depletion region, the electrons freely move to the AsP side and are collected by the drain electrode, meanwhile the holes move to the MoS2 side and are collected by the source electrode. Thus, a negative Voc and positive Isc is observed in Fig. 4a. Note that only electrons cross the heterointerface without any barrier block and efficiently collected by the AsP carrier selective contact via the rapid recombination with majority holes in AsP not the photogenerated holes in the MoS2 unilateral depletion region. By this means, although a little part of energy (approximately 0.25 eV per one photon) is lost, the recombination of photogenerated electron-hole pairs are significantly suppressed and the carrier collection efficiency is greatly improved, thus the EQE and PCE are enhanced as we mentioned previously. In order to confirm the photovoltaic response is mainly induced by the heterojunction not the Schottky junction effect, scanning photocurrent map** is used to acquire the photocurrent distribution. As seen in Fig. 5b, a clear photocurrent is observed in the whole junction area and no obvious current is generated near the metal contacts, which unambiguously demonstrates the photovoltaic current indeed originates from the heterojunction. We also demonstrate that no photovoltaic response is seen for the MoS2 FET device (Supplementary Fig. 13). The photoswitching and response speed are also important for a practical photodetector. Figure 5c presents the photoswitching response of the diode at zero bias under a periodical on/off laser illumination. The photoswitching response under different power densities and different biases are provided in Supplementary Figs. 11 and 12, respectively. The current rapidly increases when the laser is on and recovers to the dark state quickly when is off. A good stability is demonstrated with multiple and reproducible switching. The response time is achieved by using a digital oscilloscope to record the fast-varying photocurrent signals. As shown in Fig. 5d, the rise and decay processes are very fast with a rise time of 9 μs and a fall time of 5 μs, which are among the fastest response times for photovoltaic detectors based 2D vdWHs29,34,44,45. The fast response is attributed to the unilateral depletion region design, by which the interface trap** effect is greatly reduced since only electrons cross the interface and rapidly recombine with the holes in the accumulation region. This is confirmed by the response time of the normal MoS2/AsP pn heterodiode (Supplementary Fig. 20), which shows one order of magnitude slower response time than that of the MoS2/AsP heterodiode with unilateral depletion region. The spectral response of the MoS2/AsP vdWHs diode is also measured and shown in Supplementary Fig. 10. The diode shows a broadband photovoltaic response from visible to near infrared wavelengths with a peak response at about 600 nm, indicating its potential application in solar cells. Finally, for a comprehensive comparison, the figure of merits for photovoltaic detectors or solar cells based on 2D vdWHs are shown in Supplementary Table 3. It can be seen that our device based on thick MoS2/AsP vdWHs with unilateral depletion region manifests the highest PCE and fastest response time. The fill factor and open-circuit voltage Voc are also comparable to previous works based on other vertical 2D vdWHs diodes. Our work suggests van der Waals heterodiodes based on 2D materials with unilateral depletion region band designs and narrow bandgap semiconductor carrier selective contacts are more suitable for high-performance photovoltaic detectors and solar cells.
MoS2/BP vdWHs photodiode with unilateral depletion region
The vdWHs photodiodes with unilateral depletion region band structure can be applied to other 2D semiconductors, for example BP (similar to AsP). A MoS2/BP vdWHs photodiode with unilateral depletion region was successfully fabricated and demonstrated similar photovoltaic response (Supplementary Figs. 32–35 and Note 6). In comparison with MoS2/AsP vdWHs photodiode, the MoS2/BP vdWHs photodiode exhibits lower photovoltaic efficiency and device performance, which may be attributed to a different band alignment of the heterojunction and/or the unoptimized band profile of the device.
Discussions
In summary, we have proposed and demonstrated a van der Waals heterodiode with a unilateral depletion region and a narrow bandgap semiconductor carrier selective contact for high-performance photovoltaic detectors, which was successfully fabricated by assembling thick weak p-type MoS2 and narrow bandgap AsP 2D layers. We show that this kind van der Waals heterodiode can overcome the severe tunneling-assisted interface recombination of photogenerated electron-hole pairs and inefficient carrier selective contacts inevitable in previous 2D heterodiodes based photovoltaic detectors. Meanwhile the unilateral depletion region configuration can greatly reduce the interface trap** effect of the photogenerated carriers. As a result, the MoS2/AsP heterodiode exhibits a pronounced photovoltaic effect with a short-circuit current as high as 1.3 μA and a large open-circuit voltage of 0.61 V under 520 nm laser illumination. More importantly, a record high power conversion efficiency of 9% and a fast response time of 9 μs are achieved. Our work lays a foundation for the next generation of 2D vdWHs photovoltaic devices comprising a combination of a large bandgap semiconductor as the depleted absorption layer and a narrow bandgap semiconductor as the effective carrier selective contact.
Methods
Device fabrication
The MoS2/AsP vdWHs investigated here were fabricated by a commonly used dry transfer method utilizing a polydimethylsiloxane (PDMS) carrier. First, relative thick AsP flakes were mechanically exfoliated from an as-grown AsP crystal using Scotch tape and transferred onto a silicon substrate (with 300 nm SiO2). Then, MoS2 flakes were exfoliated onto the PDMS film from the commercial bulk crystal (2D Semiconductors, America) and transferred onto the AsP flake to form the heterostructure under the optical microscope assisted by an aligned transfer platform. The exfoliation and transfer processes were conducted in the N2-protection glovebox to minimize the oxidation of AsP. For device fabrication, electron-beam lithography (EBL, FEI F50 SEM with NPGS system) was employed to define the electrode patterns. A Cr/Au (15 nm/55 nm) metal thin film was deposited as the contact electrodes by thermal evaporation, followed by the standard lift-off process.
Characterizations and measurements
Raman spectra were achieved by a confocal Raman/PL system (LabRAM HR800) using 532 nm laser as an excitation source. The thickness and surface potential of the two layers were obtained by AFM and KPFM, respectively (Bruker Multimode 8). The electrical characterizations of the MoS2/AsP vdWHs devices were performed in a probe station (Lake Shore) using a semiconductor device parameter analyzer (Agilent, B1500). The devices were wire-bonded onto a 24-pin chip carrier and a 520 nm laser was used for photoresponse measurements. A supercontinuum light source (YSL sc-pro) is employed to obtain the spectral photocurrent response. An oscilloscope (Tektronix DPO 5204, 100 MHz, 2.5 G/s) was used to record the transient photocurrent response to resolve the photoresponse time. In all the photocurrent measurements, the laser was focused on the device with a ×20 objective (NA = 0.45), and the laser spot is near flat with a size of about ∼20 μm, larger than the heterojunction area to make sure a uniform illumination. All the devices were measured at room temperature in an ambient environment.
Data availability
The data that support the plots within this paper and other findings of this study are available from the corresponding author upon reasonable request. The source data underlying Figs. 1a, c, 3b, c, e, f, 4a–f, 5c, d and Supplementary Figs. 2b, 3–5, 8–13, 15, 17–20, 22–27, 29, 30, and 32–35 are provided as a Source Data file.
References
Koppens, F. H. L. et al. Photodetectors based on graphene, other two-dimensional materials and hybrid systems. Nat. Nanotechnol. 9, 780 (2014).
Huo, N. & Konstantatos, G. Recent progress and future prospects of 2D-based photodetectors. Adv. Mater. 30, 1801164 (2018).
Cheng, J., Wang, C., Zou, X. & Liao, L. Recent advances in optoelectronic devices based on 2D materials and their heterostructures. Adv. Opt. Mater. 7, 1800441 (2019).
Long, M., Wang, P., Fang, H. & Hu, W. Progress, challenges, and opportunities for 2D material based photodetectors. Adv. Funct. Mater. 0, 1803807 (2018).
**a, F., Mueller, T., Lin, Y.-m, Valdes-Garcia, A. & Avouris, P. Ultrafast graphene photodetector. Nat. Nanotechnol. 4, 839 (2009).
Yin, Z. et al. Single-layer MoS2 phototransistors. ACS Nano 6, 74–80 (2012).
Buscema, M. et al. Fast and broadband photoresponse of few-layer black phosphorus field-effect transistors. Nano Lett. 14, 3347–3352 (2014).
Yuan, H. et al. Polarization-sensitive broadband photodetector using a black phosphorus vertical p–n junction. Nat. Nanotechnol. 10, 707 (2015).
Lopez-Sanchez, O., Lembke, D., Kayci, M., Radenovic, A. & Kis, A. Ultrasensitive photodetectors based on monolayer MoS2. Nat. Nanotechnol. 8, 497 (2013).
Liu, E. et al. High responsivity phototransistors based on few-layer ReS2 for weak signal detection. Adv. Funct. Mater. 26, 1938–1944 (2016).
Wang, X. et al. Ultrasensitive and broadband MoS2 photodetector driven by ferroelectrics. Adv. Mater. 27, 6575–6581 (2015).
Mudd, G. W. et al. High broad-band photoresponsivity of mechanically formed InSe–Graphene van der Waals heterostructures. Adv. Mater. 27, 3760–3766 (2015).
Hu, P. et al. Highly responsive ultrathin GaS nanosheet photodetectors on rigid and flexible substrates. Nano Lett. 13, 1649–1654 (2013).
Cao, Y. et al. Strong enhancement of photoresponsivity with shrinking the electrodes spacing in few layer GaSe photodetectors. Sci. Rep. 5, 8130 (2015).
Guo, Q. et al. Black phosphorus mid-infrared photodetectors with high gain. Nano Lett. 16, 4648–4655 (2016).
Huang, M. et al. Broadband black-phosphorus photodetectors with high responsivity. Adv. Mater. 28, 3481–3485 (2016).
Zhou, X. et al. Highly anisotropic GeSe nanosheets for phototransistors with ultrahigh photoresponsivity. Adv. Sci. 5, 1800478 (2018).
Zhou, X. et al. Ultrathin SnSe2 flakes grown by chemical vapor deposition for high-performance photodetectors. Adv. Mater. 27, 8035–8041 (2015).
Long, M. et al. Room temperature high-detectivity mid-infrared photodetectors based on black arsenic phosphorus. Sci. Adv. 3, e1700589 (2017).
Amani, M., Regan, E., Bullock, J., Ahn, G. H. & Javey, A. Mid-wave infrared photoconductors based on black phosphorus-arsenic alloys. ACS Nano 11, 11724–11731 (2017).
Tan, W. C. et al. A black phosphorus carbide infrared phototransistor. Adv. Mater. 30, 1705039 (2018).
Liu, Y., Cai, Y., Zhang, G., Zhang, Y.-W. & Ang, K.-W. Al-doped black phosphorus p–n homojunction diode for high performance photovoltaic. Adv. Funct. Mater. 27, 1604638 (2017).
Konstantatos, G. Current status and technological prospect of photodetectors based on two-dimensional materials. Nat. Commun. 9, 5266 (2018).
Wang, L. et al. 2D photovoltaic devices: progress and prospects. Small Methods 2, 1700294 (2018).
Li, C. et al. Engineering graphene and TMDs based van der Waals heterostructures for photovoltaic and photoelectrochemical solar energy conversion. Chem. Soc. Rev. 47, 4981–5037 (2018).
Jariwala, D., Davoyan, A. R., Wong, J. & Atwater, H. A. Van der Waals materials for atomically-thin photovoltaics: promise and outlook. ACS Photon. 4, 2962–2970 (2017).
Liu, Y., Huang, Y. & Duan, X. Van der Waals integration before and beyond two-dimensional materials. Nature 567, 323–333 (2019).
Lee, C.-H. et al. Atomically thin p–n junctions with van der Waals heterointerfaces. Nat. Nanotechnol. 9, 676 (2014).
Cheng, R. et al. Electroluminescence and photocurrent generation from atomically sharp WSe2/MoS2 heterojunction p–n diodes. Nano Lett. 14, 5590–5597 (2014).
Furchi, M. M., Pospischil, A., Libisch, F., Burgdörfer, J. & Mueller, T. Photovoltaic effect in an electrically tunable van der Waals heterojunction. Nano Lett. 14, 4785–4791 (2014).
Deng, Y. et al. Black phosphorus–monolayer MoS2 van der Waals heterojunction p–n diode. ACS Nano 8, 8292–8299 (2014).
Hong, T. et al. Anisotropic photocurrent response at black phosphorus–MoS2 p–n heterojunctions. Nanoscale 7, 18537–18541 (2015).
Chen, Y. et al. High-performance photovoltaic detector based on MoTe2/MoS2 Van der Waals heterostructure. Small 14, 1703293 (2018).
Pezeshki, A., Shokouh, S. H. H., Nazari, T., Oh, K. & Im, S. Electric and photovoltaic behavior of a few-layer α-MoTe2/MoS2 dichalcogenide heterojunction. Adv. Mater. 28, 3216–3222 (2016).
Wang, F. et al. Tunable GaTe-MoS2 van der Waals p–n junctions with novel optoelectronic performance. Nano Lett. 15, 7558–7566 (2015).
Yang, S. et al. Self-driven photodetector and ambipolar transistor in atomically thin GaTe-MoS2 p–n vdW heterostructure. ACS Appl. Mater. Inter. 8, 2533–2539 (2016).
Feng, W. et al. A fast and zero-biased photodetector based on GaTe–InSe vertical 2D p–n heterojunction. 2D Mater. 5, 025008 (2018).
Wang, P. et al. Arrayed Van Der Waals broadband detectors for dual-band detection. Adv. Mater. 29, 1604439 (2017).
Wu, F. et al. AsP/InSe Van der Waals tunneling heterojunctions with ultrahigh reverse rectification ratio and high photosensitivity. Adv. Funct. Mater. 29, 1900314 (2019).
Liu, B. et al. Black arsenic–phosphorus: layered anisotropic infrared semiconductors with highly tunable compositions and properties. Adv. Mater. 27, 4423–4429 (2015).
Liu, Y. et al. Vertical charge transport and negative transconductance in multilayer molybdenum disulfides. Nano Lett. 17, 5495–5501 (2017).
Kc, S., Longo, R. C., Addou, R., Wallace, R. M. & Cho, K. Impact of intrinsic atomic defects on the electronic structure of MoS2 monolayers. Nanotechnology 25, 375703 (2014).
Wang, L. et al. MoS2/Si heterojunction with vertically standing layered structure for ultrafast, high-detectivity, self-driven visible–near infrared photodetectors. Adv. Funct. Mater. 25, 2910–2919 (2015).
Li, D., Wang, B., Chen, M., Zhou, J. & Zhang, Z. Gate-controlled BP–WSe2 heterojunction diode for logic rectifiers and logic optoelectronics. Small 13, 1603726 (2017).
Kwak, D.-H., Ra, H.-S., Jeong, M.-H., Lee, A. Y. & Lee, J.-S. High-performance photovoltaic effect with electrically balanced charge carriers in black phosphorus and WS2 heterojunction. Adv. Mater. Inter. 5, 1800671 (2018).
Acknowledgements
This work was supported by the National Natural Science Foundation of China (Grant No. 61725505, 11734016, 61521005, 61874043, and 61674157), Key research project of frontier science of CAS (Grant No.QYZDB-SSW-JSC031), Program of Shanghai Subject Chief Scientist (19XD1404100), Shanghai Sailing Program (Grant No. 19YF1454600), Natural Science Foundation of Shanghai (Grant No. 18ZR1445900 and 18ZR1445800), and China Postdoctoral Science Foundation (Grant No. 2018M632171). D.J. acknowledges support from Penn Engineering Startup funds.
Author information
Authors and Affiliations
Contributions
W.D.H. conceived and supervised the project. F.W. fabricated the devices and performed the electrical and photoresponse characterizations. H.X. performed the KPFM measurements. L.C. and W.C.R. provided the AsP bulk crystals. F.W., Q.L., Z.W., Y.W., M.L. and P.W. performed the data analysis. J.S.M., F.S.C., X.S.C., W.L., C.X.S., A.L.P. and D.J. assisted with data analysis and interpretation. F.W., W.D.H., P.W. and X.W. wrote the manuscript. All authors discussed the results and revised the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Peer review information Nature Communications thanks Sanjay Behura and the other, anonymous, reviewer(s) for their contribution to the peer review of this work.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Source data
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Wu, F., Li, Q., Wang, P. et al. High efficiency and fast van der Waals hetero-photodiodes with a unilateral depletion region. Nat Commun 10, 4663 (2019). https://doi.org/10.1038/s41467-019-12707-3
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-019-12707-3
- Springer Nature Limited
This article is cited by
-
Boosting performances of ZnO microwire homojunction ultraviolet self-powered photodetector by coupled interfacial engineering and plasmonic effects
Science China Materials (2024)
-
High-performance photodetector based on ReS2/WSe2/Te dual van der Waals heterojunctions
Journal of Materials Science (2024)
-
High-performance broadband photodetector based on PtSe2/MoS2 heterojunction from visible to near-infrared region
Science China Information Sciences (2024)
-
Two-dimensional materials for future information technology: status and prospects
Science China Information Sciences (2024)
-
Lead halide perovskite sensitized WSe2 photodiodes with ultrahigh open circuit voltages
eLight (2023)