Abstract
Wire and arc additive manufacturing (WAAM) enables the building of near net-shape components layer by layer by using arc welding technologies and wire filler metal as feedstock. The study aims at comparing the applicability of two innovative robotic arc welding technologies (cold metal transfer (CMT) and TopTIG) for additive manufacturing (AM) of stainless steel parts. Initially, a process development has been completed with the goal of optimizing material deposition rate during arc time. Both continuous and pulsed current programs were implemented. Then, different thick-walled samples composed of more than one overlapped weld bead per layer were manufactured in 316L stainless steel grade by CMT and TopTIG. Mechanical properties have been determined in as-build samples in different building orientations. WAAM applying CMT and TopTIG welding technologies is analyzed in terms of part quality (defined as the absence of defects such as pores, cracks, and/or lack of fusion defects); surface finishing; part accuracy; productivity; microstructural characteristics; and mechanical properties. Achieved mechanical properties and deposition rates are compared with the state of the art. Findings and conclusions of this work are applicable to the industrial manufacturing of stainless steel parts and requirements to apply these technologies to other expensive materials are finally discussed.
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs40194-018-0606-6/MediaObjects/40194_2018_606_Fig1_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs40194-018-0606-6/MediaObjects/40194_2018_606_Fig2_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs40194-018-0606-6/MediaObjects/40194_2018_606_Fig3_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs40194-018-0606-6/MediaObjects/40194_2018_606_Fig4_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs40194-018-0606-6/MediaObjects/40194_2018_606_Fig5_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs40194-018-0606-6/MediaObjects/40194_2018_606_Fig6_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs40194-018-0606-6/MediaObjects/40194_2018_606_Fig7_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs40194-018-0606-6/MediaObjects/40194_2018_606_Fig8_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs40194-018-0606-6/MediaObjects/40194_2018_606_Fig9_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs40194-018-0606-6/MediaObjects/40194_2018_606_Fig10_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs40194-018-0606-6/MediaObjects/40194_2018_606_Fig11_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs40194-018-0606-6/MediaObjects/40194_2018_606_Fig12_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs40194-018-0606-6/MediaObjects/40194_2018_606_Fig13_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs40194-018-0606-6/MediaObjects/40194_2018_606_Fig14_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs40194-018-0606-6/MediaObjects/40194_2018_606_Fig15_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs40194-018-0606-6/MediaObjects/40194_2018_606_Fig16_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs40194-018-0606-6/MediaObjects/40194_2018_606_Fig17_HTML.png)
Similar content being viewed by others
References
Cranfield University, “WAAM Technology,” 2015
Ding D, Pan Z, Cuiuri D, Li H (2015) Wire-feed additive manufacturing of metal components: technologies, developments and future interests. Int J Adv Manuf Technol 81(1–4):465–481
A. Addison, J. Ding, F. Martina, H. Lockett, S. Williams, and X. Zhang, “Manufacture of complex titanium parts using wire + arc additive manufacture,” in Titanium Europe 2015 Conference, 2015, p. 14
I. D. Harris, “New developments in welding and metal additive manufacturing using directed energy deposition (DED),” in Titanium Europe 2015 Conference, 2015, p. 27
Baufeld B, Van der Biest O, Gault R (2010) Additive manufacturing of Ti–6Al–4V components by shaped metal deposition: microstructure and mechanical properties. Mater Des 31:106–111
Colegrove P (2013) High deposition rate high quality metal additive manufacture using wire + arc. Technology
N. P. Hoye, E. C. Appel, D. Cuiuri, and H. Li, “Characterisation of metal deposition during additive manufacturing of Ti-6Al-4V BY arc-wire methods,” in 24th annual international solid freeform fabrication symposium, 2013, pp. 1015–1023
J. Gu, B. Cong, J. Ding, S. W. Williams, and Y. Zhai, “Wire + arc additive manufacturing of aluminium,” in SFF Symposium, 2014, pp. 451–458
Cong B, Ding J, Williams S (2015) Effect of arc mode in cold metal transfer process on porosity of additively manufactured Al-6.3%Cu alloy. Int J Adv Manuf Technol 76(9–12):1593–1606
D. E. Cooper, “The high deposition rate additive manufacture of nickel superalloys and metal matrix composites,” University of Warwick, 2016
Xu F, Lv Y, Liu Y, Shu F, He P, Xu B (2013) Microstructural evolution and mechanical properties of Inconel 625 alloy during pulsed plasma arc deposition process. J Mater Sci Technol 29(5):480–488
Youheng F, Guilan W, Haiou Z, Liye L (2017) Optimization of surface appearance for wire and arc additive manufacturing of Bainite steel. Int J Adv Manuf Technol 91(1–4):301–3013
Kapil S, Legesse F, Kulkarni P, Joshi P, Desai A, Karunakaran KP (2016) Hybrid-layered manufacturing using tungsten inert gas cladding. Prog Addit Manuf 1:79–91
Williams SW, Martina F, Addison AC, Ding J, Pardal G, Colegrove P (2016) Wire + arc additive manufacturing. Mater Sci Technol 32(7):641–647
Martina F, Mehnen J, Williams SW, Colegrove P, Wang F (2012) Investigation of the benefits of plasma deposition for the additive layer manufacture of Ti-6Al-4V. J Mater Process Technol 212(6):1377–1386
F. Martina and S. Williams, “Wire + arc additive manufacturing vs. traditional machining from solid from solid: a cost comparison,” 2015
Sciaky Inc., “Electron beam additive manufacturing (EBAM) technology,” 2016. Available: http://www.sciaky.com/additive-manufacturing/electron-beam-additive-manufacturing-technology. [Accessed: 08-May-2018]
F. Vega, “Titanium additive manufacturing—a novel game changing technology,” in Titanium 2014 Conference, 2014, p. 24
S. Williams, “Large scale metal wire + arc additive manufacturing of structural engineering parts,” in 69th IIW annual assembly and international conference, 2016, p. 25
Suryakumar S, Karunakaran KP, Bernard A, Chandrasekhar U, Raghavender N, Sharma D (2011) Weld bead modeling and process optimization in hybrid layered manufacturing. Comput Aided Des 43(4):331–344
D. Ding, “Process planning for robotic wire and arc additive manufacturing,” University of Wollogong, 2015
“Fronius International GmbH.” Available: http://www.fronius.com. [Accessed: 08-May-2018]
Opderbecke T, Guiheux S (2009) TOPTIG: robotic TIG welding with integrated wire feeder. Weld Int 23(7):523–529
P. M. S. Almeida and S. Williams, “Innovative process model of Ti–6Al–4V additive layer manufacturing using cold metal transfer (CMT),” in Solid freeform fabrication symposium, 2010, pp. 25–36
“Aceros IMS.” Available: http://www.acerosims.com. [Accessed: 08-May-2018]
“Gefertec GmbH.” Available: http://www.gefertec.com/. [Accessed: 08-May-2018]
Author information
Authors and Affiliations
Corresponding author
Additional information
This article is part of the collection Welding, Additive Manufacturing, and Associated NDT
Rights and permissions
About this article
Cite this article
Rodriguez, N., Vázquez, L., Huarte, I. et al. Wire and arc additive manufacturing: a comparison between CMT and TopTIG processes applied to stainless steel. Weld World 62, 1083–1096 (2018). https://doi.org/10.1007/s40194-018-0606-6
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s40194-018-0606-6