Abstract
Ternary fcc Ni-Co-Mo diffusion couples annealed at 1273 and 1473 K have been scanned to measure composition profiles by using electron probe microanalysis. The interdiffusion coefficients were extracted using the Whittle–Green method from the measured composition profiles of the ternary diffusion couples. Based on the diffusion coefficients reported in the literature and data determined in the present work, the diffusion mobilities for fcc Ni-Co-Mo alloys were assessed. In addition, diffusion paths and composition profiles were simulated with presently assessed mobility parameters. In general, reasonable agreements have been reached and the resulted mobility database can be used to investigate the diffusion behavior of the ternary fcc Ni-Co-Mo alloys in wide composition and temperature ranges.
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs11669-017-0587-y/MediaObjects/11669_2017_587_Fig1_HTML.gif)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs11669-017-0587-y/MediaObjects/11669_2017_587_Fig2_HTML.gif)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs11669-017-0587-y/MediaObjects/11669_2017_587_Fig3_HTML.gif)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs11669-017-0587-y/MediaObjects/11669_2017_587_Fig4_HTML.gif)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs11669-017-0587-y/MediaObjects/11669_2017_587_Fig5_HTML.gif)
Similar content being viewed by others
References
J.R. Davis, ASM Specialty Handbook: Nickel, Cobalt, and Their Alloys, Materials Park, Ohio, 2000
X.J. Liu, H.H. Hu, J.J. Han, Y. Lu, and C.P. Wang, CALPHAD, 2012, 38, p 140-145
N.Q. Zhu, J.C. Li, X.G. Lu, Y.L. He, and J.Y. Zhang, Metall. Mater. Trans. A, 2015, 46, p 5444-5455
X.W. He, W.B. Zhang, M.Y. Yan, C. Chen, Y. Du, L.J. Zhang, and B.Y. Huang, CALPHAD, 2015, 49, p 35-40
A. Davin, V. Leroy, D. Coutsouradis, and L. Habraken, Cobalt, 1963, 19, p 51-56
Y. Wang, N.Q. Zhu, H. Wang, and X.G. Lu, Metall. Mater. Trans. A, 2017, 48, p 943-947
C.E. Campbell, W.J. Boettinger, and U.R. Kattner, Acta Mater., 2002, 50, p 775-792
Y.W. Cui, M. Jiang, I. Ohnuma, K. Oikawa, R. Kainuma, and K. Ishida, J. Phase Equilib. Diffus., 2008, 29, p 2-10
Y. Chen, B. Tang, G. Xu, C. Wang, H. Kou, J. Li, and Y. Cui, Metall. Mater. Trans. A, 2014, 45, p 1647-1652
A.G. Nikitin, S.V. Spichak, Y.S. Vedula, and A.G. Naumovets, J. Phys. D, 2009, 42, p 055301
D.P. Whittle and A. Green, Scr. Metall., 1974, 8, p 883-884
J.S. Kirkaldy and D.J. Young, Diffusion in the Condensed State, The Institute of Metals, London, 1987, p 83-87
J.O. Andersson and J. Ågren, J. Appl. Phys., 1992, 72, p 1350-1355
B. Jönsson, Z. Metallkd., 1994, 85, p 502-509
O. Redlich and A.T. Kister, Ind. Eng. Chem. Res., 1948, 40, p 345-348
C. Zhang, Y.L. Liu, Y. Du, Y.B. Peng, and J. Wang, CALPHAD, 2016, 55, p 243-251
T. Heumann and A. Kottmann, Z. Metallkd., 1953, 44, p 139-154
Y. Lijima and K. Hirano, J. Jpn. Inst. Met., 1971, 35, p 511-517
T. Ustad and H. Sorum, Phys. Status Solidi A, 1973, 20, p 285-294
J. Kucera, K. Ciha, and K. Stransky, Czech, J. Phys. B, 1977, 27, p 758-768
S.B. Jung, T. Yamane, Y. Minamino, K. Hirano, H. Araki, and S. Saji, J. Mater. Sci. Lett., 1992, 11, p 1333-1337
M.S.A. Karunaratne and R.C. Reed, Defect and Diffusion Forum, Vol 237-240, Trans Tech Publications Ltd., Dürnten, 2005, p 420-425
G. Neumann and V. Tölle, Philos. Mag. A, 1986, 54, p 619-629
J.F. Wang, Y. Wang, N.Q. Zhu, and X.G. Lu, J. Phase Equilib. Diffus., 2017, 38, p 37-50
Acknowledgments
Y. Wang gratefully acknowledges the financial support from National Key R&D Program of China (Grant Number: 2017YFB0701502). XG Lu acknowledges the Shanghai Municipal Science and Technology Commission Project (Grant Number: 14521100603). Thermo-Calc software AB is appreciated for providing the DICTRA software.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Wang, Y., Lu, XG. Interdiffusion and Diffusion Mobility for Fcc Ni-Co-Mo Alloys. J. Phase Equilib. Diffus. 38, 656–664 (2017). https://doi.org/10.1007/s11669-017-0587-y
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11669-017-0587-y