Abstract
In this study, the effects of Cu addition to Sn-58Bi-0.5Ag solder were investigated with respect to the alloy properties and fracture behavior of solder joints. The results show that adding Cu to the solder did not cause a significant change in the melting temperature. The melting temperature of all samples was 153.3–155.4°C. With the addition of Cu, the wettability of the solder first increased and subsequently decreased. When the Cu content was 0.5 wt.%, the area of spread was greatest (28.32 mm2), the wettability angle was lowest (12.9°), and the tensile strength of the solder joint was the highest (35.73 MPa). In addition, the proper amount of Cu content helped to refine the microstructure of eutectic solder and reduce the brittleness of joints. With increasing Cu content, the fracture mechanism of solder joints changed from a mixed fracture of toughness and brittleness to a brittle fracture.
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs11664-022-09601-y/MediaObjects/11664_2022_9601_Fig1_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs11664-022-09601-y/MediaObjects/11664_2022_9601_Fig2_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs11664-022-09601-y/MediaObjects/11664_2022_9601_Fig3_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs11664-022-09601-y/MediaObjects/11664_2022_9601_Fig4_HTML.jpg)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs11664-022-09601-y/MediaObjects/11664_2022_9601_Fig5_HTML.jpg)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs11664-022-09601-y/MediaObjects/11664_2022_9601_Fig6_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs11664-022-09601-y/MediaObjects/11664_2022_9601_Fig7_HTML.jpg)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs11664-022-09601-y/MediaObjects/11664_2022_9601_Fig8_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs11664-022-09601-y/MediaObjects/11664_2022_9601_Fig9_HTML.png)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs11664-022-09601-y/MediaObjects/11664_2022_9601_Fig10_HTML.jpg)
Similar content being viewed by others
References
X.K. Zhu, H.H. Lou, X. Qu, J.J. Wang, L. Taekoo, and H. Wang, The Challenge of changeover to lead-free in electronic packaging. Electron. Packag. 05, 2 (2005).
Z.D. **a, Y.P. Lei, and Y.W. Shi, Research and development of advanced environmental-friendly lead-free solder. Electron. Process. Technol. 05, 185 (2002).
P.L. Liu, and J.K. Shang, Interfacial segregation of bismuth in copper tin-bismuth solder interconnect. Scr. Mater. 44, 1019 (2001).
O. Mokhtari, and H. Nishikawa, Effects of In and Ni addition on microstructure of Sn-58Bi solder joint. Electron. Mater. 43, 4158 (2014).
X.Y. Liu, M.L. Huang, C.M.L. Wu, and L. Wang, Effect of Y2O3 particles on microstructure formation and shear properties of Sn-58Bi solder. Mater. Sci. Mater. Electron. 21, 1046 (2010).
Z.M. Lai, and D. Ye, Microstructure and properties of Sn-10Bi-xCu solder alloy joint. Electron. Mater. 45, 3702 (2016).
F.Q. Hu, Q.K. Zhang, J.J. Jiang, and Z.L. Song, Influences of Ag addition to Sn-58Bi solder on SnBi/Cu interfacial reaction. Mater. Lett. 214, 142 (2018).
H.Y. Sun, Y.C. Chan, and F.S. Wu, Effect of CNTs and Ni coated CNTs on the mechanical performance of Sn57.6Bi0.4Ag BGA. Mater. Sci. Eng. A. 656, 249 (2016).
C. Zhang, S.D. Liu, G.T. Qian, J. Zhou, and F. Xue, Effect of Sb content on properties of Sn-Bi solders. Trans. Nonferrous Met. Soc. China. 24, 184 (2014).
B. Yang, J.M. Chen, S.J. Wu, M.M. Li, and J.B. Zhang, Study on wetting shearing properties and interface compounds of Sn-58Bi-(0–3)Ga/Cu. Mater. Rev. 31, 92 (2017).
Q. Li, J.H. Huang, H. Zhang, X.K. Zhao, and L.H. Qi, Influence of Al on microstructure and mechanical properties of the Sn-58Bi lead-free solder. Electron. Process. Technol. 29, 1 (2008).
L.K. Gong, J.F. Liao, J.H. Yuan, G.H. Li, and H.M. Chen, Effect of rare earth Y on microstructure and properties of Sn-58Bi solder alloy. J. Aeronaut. Mater. 38, 101 (2018).
H. Takao, A. Yamada, and H. Hasegawa, Mechanical properties and solder joint reliability of low-melting Sn-Bi-Cu lead free solder alloy. R&D Rev. Toyota. CRDL 39, 49 (2004).
L.K. Zang, Z.F. Yuan, H.X. Zhao, and X.R. Zhang, Wettability of molten Sn-Bi-Cu solder on Cu substrate. Mater. Lett. 63, 2067 (2009).
H.Y. Sun, Q.Q. Li, and Y.C. Chan, A study of Ag additive methods by comparing mechanical properties between Sn-57.6Bi-0.4Ag and 0.4 wt.% nano-Ag-doped Sn-58Bi BGA solder joints. Mater. Sci. Mater. Electron. 25, 4380 (2014).
L.Z. Yang, W. Zhou, Y. Ma, X.Z. Li, Y.H. Liang, W.Q. Cui, and P. Wu, Effects of Ni addition on mechanical properties of Sn58Bi solder alloy during solid-state aging. Mater. Sci. Eng. A. 667, 368 (2016).
L.Y. Xu, L.X. Wang, H.Y. **g, X.D. Liu, and Y.D. Han, Effects of graphene nano sheets on interfacial reaction of Sn-Ag-Cu solder joints. J. Alloy. Compd. 650, 475 (2015).
T.H. Chuang, and H.F. Wu, Effects of Ce addition on the microstructure and mechanical properties of Sn-58Bi solder joints. Electron. Mater. 40, 71 (2011).
P. He, X.C. Lv, B.B. Zhang, X. Ma, and Y.Y. Qian, Effect of alloy element on microstructure and impact toughness of Sn-57Bi lead-free solders. J. Mater. Eng. 10, 13 (2010).
Acknowledgments
This work was supported by the National Natural Science Foundation of China (No. 52175288), Graduate Science and Technology Innovation Program of Chongqing University of Science and Technology (YKJCX2020227), and Key Laboratory of Jiangxi Province for Aeronautical Component Forming and Connection (HKGJ-2001).
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Conflict of interest
We declare that we have no financial or personal relationships with other people or organizations that can inappropriately influence our work, and there is no professional or other personal interest of any nature or kind in any product, service, and/or company that could be construed as influencing the position presented in, or the review of, the manuscript entitled.
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
About this article
Cite this article
Yao, Z., Ling, D., Liu, Y. et al. Effect of Cu Addition on the Microstructure and Mechanical Properties of Sn-58Bi-0.5Ag Solder Alloys. J. Electron. Mater. 51, 3552–3559 (2022). https://doi.org/10.1007/s11664-022-09601-y
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11664-022-09601-y