Abstract
The hierarchical crystalline morphologies and orientation structures across the thickness direction in high-density polyethylene (HDPE) molded bars were investigated via a novel melt-penetrating processing method named multi-melt multi-injection molding (M3IM). The samples with various mold temperatures (20, 40 and 60 °C) were prepared, and the effects of the external temperature profile on the evolution of crystalline microstructures were studied. With scanning electron microscopy (SEM), the transition of crystalline morphology from ring-banded structure to oriented lamellae was observed with decreasing mold temperature, and the oriented lamellae were formed at the sub-skin layer of the samples at the lowest mold temperature, which was further testified by differential scanning calorimetry (DSC). With the decline of mold temperature, the degree of orientation, obtained from two-dimensional small angle X-ray scattering (2D-SAXS), was increased and long periods rose a little. Thus, decreasing mold temperature was beneficial to the formation of orientation structures because the relaxation of chains was weakened.
Similar content being viewed by others
References
Callister, W.D. and Rethwisch, D.G. "Materials science and engineering: an introduction" (in U.S.), Wiley, New York, 2007, p. 51
Wang, Y., **ao, Y., Zhang, Q., Gao, X.L. and Fu, Q., Polymer, 2003, 44(5): 1469
Liu, R.Y., **, Y., Hiltner, A. and Baer, E., Macromol. Rapid Commun., 2003, 24(16): 943
Allan, P.S. and Bevis, M.J., 1990, U.S. Pat., 4,925,161.15
Wang, K., Chen, F., Zhang, Q. and Fu, Q., Polymer, 2008, 49(22): 4745
Liedauer, S., Eder, G., Janeschitz-Kriegl, H., Jerschow, P., Geymayer, W. and Ingolic, E., Intern. Polym. Proc., 1993, 8(3): 236
Nogales, A., Hsiao, B.S., Somani, R.H., Srinivas, S., Tsou, A.H., Balta-Calleja, F.J. and Ezquerra, T.A., Polymer, 2001, 42(12): 5247
Zhang, R.Y., Yang, W., Wu, J.J., Feng, J., Feng, J.M., **e, B.H. and Yang, M.B., RSC Adv., 2014, 4(60): 31960
Zhang, K., Liu, Z., Yang, B., Yang, W., Lu, Y., Wang, L., Sun, N. and Yang, M., Polymer, 2011, 52(17): 3871
Zhang, R.Y., Yang, W., Zhang, K., Feng, J., Zhu, C.X., **a, X.C., He, S., Feng, J.M., Liu, Z.Y. and Yang, M.B., RSC Adv., 2015, 5(28): 21640
Zheng, G., Yang, W., Yin, B., Yang, M., Liu, C. and Shen, C., J. Appl. Polym. Sci., 2006, 102(3): 3069
Huang, H.X. and Zhou, R.H., Polym. Test., 2010, 29(2): 235
Zheng, G.Q., Huang, L., Yang, W., Yang, B., Yang, M.B., Li, Q. and Shen, C.Y., Polymer, 2007, 48(19): 5486
Huang, L., Yang, W., Yang, B., Yang, M., Zheng, G. and An, H., Polymer, 2008, 49(19): 4051
Feng, J., Yang, W., Zhang, R.Y., Wu, J.J., Wang, L., Zhang, C.L. and Yang, M.B., Polym. Plas. Technol. Eng., 2014, 53(12): 1272
Somani, R.H., Hsiao, B.S., Nogales, A., Fruitwala, H., Srinivas, S. and Tsou, A.H., Macromolecules, 2001, 34(17): 5902
Yang, L., Somani, R.H., Sics, I., Hsiao, B.S., Kolb, R., Fruitwala, H. and Ong, C., Macromolecules, 2004, 37(13): 4845
Lian, F., Ma, Z.K. and Liang, J.Y., Chinese J. Polym. Sci., 2012, 30(6): 786
Wang, L., Yang, W., Huang, L., Yang, B., Sun, N. and Yang, M.B., Plas. Rub. Compos., 2010, 39(9): 385
**a, X.C., Zhang, Q.P., Wang, L., He, S., Feng, J.M. and Yang, M.B., Polym. Int., 2014, 63(12): 1997
Wang, L., Yang, M.B., Zhang, Q.P., Zhang, R.Y., Wu, J.J. and Feng, J.M., Polym. Adv. Technol., 2013, 24(6): 541
Wang, L., Yang, B., Sun, N., Zhang, K., Feng, J.M. and Yang, M.B., Colloid Polym. Sci., 2012, 290(12): 1133
Wu, J.J., Yang, W., Zhang, K., Zhang, R.Y., Feng, J., Liu, Z.Y., **e, B.H., Zhang, C.L. and Yang, M.B., Polym. Eng. Sci., 2014, 54(10): 2345
Wu, J., Yang, W. and Yang, M., Interface, 2014, 300(400): 500
Feng, J., Wang, L., Zhang, R.Y., Wu, J.J., Wang, C.Y., Yang, M.B. and Fu, X.R., J. Polym. Res., 2014, 21(5): 432
Chen, S.C., Lin, Y.W., Chien, R.D. and Li, H.M., Adv. Polym. Technol., 2008, 27(4): 224
Yalcin, B. and Cakmak, M., Polymer, 2004, 45(8): 2691
Yang, B., Fu, X.R., Yang, W., Liang, S.P., Sun, N., Hu, S. and Yang, M.B., Macromol. Mat. Eng., 2009, 294(5): 336
Van Meerveld, J., Peters, G.W.M. and Hütter, M., Rheol. Act., 2004, 44(2): 119
Balzano, L., Cavallo, D., van Erp, T.B., Ma, Z., Housmans, J.W., Fernandez-Ballester, L. and Peters, G.W.M., Mat. Sci. Eng., 2010, 14: 012005
Bird, R.B. and Carreau, P.J., Chem. Eng. Sci., 1968, 23(5): 427
Carreau, P.J., MacDonald, I.F. and Bird, R.B., Chem. Eng. Sci., 1968, 23(8): 901
Nakamura, K., Watanabe, T., Katayama, K. and Amano, T., J. Appl. Polym. Sci., 1972, 16(5): 1077
Rosenthal, M., Portale, G., Burghammer, M., Bar, G., Samulski, E.T. and Ivanov, D.A., Macromolecules, 2012, 45(18): 7454
Bassett, D., J. Macromol. Sci. Part B., 2003, 42(2): 227
Chu, B. and Hsiao, B.S., Chem. Rev., 2001, 101(6): 1727
Heeley, E., Gough, T., Hughes, D.J., Bras, W., Rieger, J. and Ryan, A., Polymer, 2013, 54(24): 6580
Ogino, Y., Fukushima, H., Matsuba, G., Takahashi, N., Nishida, K. and Kanaya, T., Polymer, 2006, 47(15): 5669
Zhu, C.Z., Yu, X.L., Liu, X.F., Mao, Y.Z., Liu, R.G. and Zhang, X.L., Chinese J. Polym. Sci., 2013, 31(5): 823
Hsiao, B.S., Gardner, K.H., Wu, D.Q. and Chu, B., Polymer, 1993, 34(19): 3986
Wang, Z.G., Hsiao, B., Fu, B., Liu, L., Yeh, F., Sauer, B., Chang, H. and Schultz, J., Polymer, 2000, 41(5): 1791
Peterlin, A. and Corneliussen, R., J. Polym. Sci., Part A: Polym. Chem., 1968, 6(7): 1273
Keum, J.K., Burger, C., Zuo, F. and Hsiao, B.S., Polymer, 2007, 48(15): 4511
Somani, R.H., Yang, L. and Hsiao, B.S., Polymer, 2006, 47(15): 5657
Sauer, B., Kampert, W., Blanchard, E.N., Threefoot, S. and Hsiao, B., Polymer, 2000, 41(3): 1099
Wang, L., Yang, B., Yang, W., Sun, N., Yin, B., Feng, J.M. and Yang, M.B., Colloid Polym. Sci., 2011, 289(15-16): 1661
Janeschitz-Kriegl, H., Ratajski, E. and Wippel, H., Colloid Polym. Sci., 1999, 277(2-3): 217
Author information
Authors and Affiliations
Corresponding author
Additional information
This work was financially supported by the National Natural Science Foundation of China (Nos. 21174092, 51473105 and 51421061) and the Major State Basic Research Development Program of China (973 program) (No. 2012CB025902).
Rights and permissions
About this article
Cite this article
Zhu, Cx., Zhang, Ry., Huang, Yh. et al. Hierarchical crystalline structures induced by temperature profile in HDPE bars during melt penetration process. Chin J Polym Sci 35, 108–122 (2017). https://doi.org/10.1007/s10118-017-1880-2
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10118-017-1880-2