Abstract
In as-delivery state, duplex stainless steels have between 35 to 60 % of ferrite with the rest consisting of austenite. This balance is known to be a good compromise for the maximal corrosion resistance and mechanical properties. When the duplex is heat affected by welding, the phase balance changes close to the fusion line. In this Heat Affected Zone (HAZ), the ferrite content is increased significantly, leading to a reduction in the use properties. It is also important to understand the ferrite content issues and to manage them.
As a first approach, this paper will underline the main influential parameters changing the ferrite content and will show how it can be predicted. Additionally, ferrite contents achievable on duplex hot rolled plate, HAZ, and weld metal will be highlighted and discussed in relation to standards from the oil and gas industry.
Zusammenfassung
Im Auslieferungszustand haben Duplex-Edelstähle zwischen 35 bis 60 % Ferrit; der Rest besteht aus Austenit. Dieses Gleichgewicht ist bekannt als ein guter Kompromiss für maximale Korrosionsbeständigkeit und gute mechanische Eigenschaften. Wenn das Duplexgefüge durch Schweißen wärmebeeinflusst wird, ändern sich die Phasenanteile in der Nähe der Fusionslinie. In dieser Wärmeeinflusszone (WEZ) wird der Ferrit-Gehalt deutlich erhöht, was zu einer Verminderung der Gebrauchseigenschaften führt. Ebenfalls ist es wichtig, den Einfluss des Ferrit-Gehalts zu verstehen und einzustellen.
In einem ersten Ansatz unterstreicht dieser Beitrag die wichtigsten Einflussfaktoren bezüglich Änderung des Ferrit-Gehalts und zeigt auf, wie dieser vorhergesagt werden kann.
Zusätzlich wird der erzielbare Ferrit-Gehalt in warmgewalzten Platten, der WEZ und im Schweißgut aufgezeigt und in Bezug auf Standards in der Öl- und Gasindustrie diskutiert.
Similar content being viewed by others
References
API 582-09, Welding guidelines for the chemical, oil, and gas industries
ASTM A240-13, Standard Specification for Chromium and Chromium-Nickel Stainless Steel Plate, Sheet, and Strip for Pressure Vessels and for General Applications
ASTM E562-08, Standard Test Method for Determining Volume Fraction by Systematic Manual Point Count
Bonnefois, B.; Soulignac, P.: Statistical system of prediction for duplex and superduplex weld properties, In: Proc. Duplex stainless steel 97, 5th world conference, 21–23 October 1997, Maastricht, The Netherlands, 1997
EN 10088-05, Stainless steels — Part 2: Technical delivery conditions for sheet/plate and strip of corrosion resisting steels for general purposes
Fanica, A.; Bonnefois, B.; Gagnepain, J-C.: Welding duplex stainless steels: recent improvements, Duplex 2007, Grado, Italy, 2007
Fanica, A.: Forming and Stress Relieving of welded superduplex, Stainless Steel World Conference & Expo, 29 November – 1 December 2011, Maastricht, The Netherlands, 2011
Hertzman, S.; Charles, J.: On the effect of nitrogen on DSS”, Duplex stainless steel 2010, International Conference & Exhibition, 13–15 October 2010, Beaune, France, 2010, p. 355
Norsok M-630, Edition 6, October 2013, Material data sheets and element data sheets for pi**
Robineau, R.: Lean duplex grades: weldability and properties of welded joint, Duplex stainless steel 2010, International Conference & Exhibition 13–15 October 2010, Beaune, France, 2010
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Corolleur, A., Fanica, A. & Passot, G. Ferrite Content in the Heat Affected Zone of Duplex Stainless Steels. Berg Huettenmaenn Monatsh 160, 413–418 (2015). https://doi.org/10.1007/s00501-015-0408-8
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00501-015-0408-8