Effects of sputtering conditions on the photovoltaic properties of Al-doped zinc oxide films for Cu(In,Ga)Se2 thin-film solar cells
This study aimed to elucidate the effects of sputtering conditions on the optical and electrical properties of AZO films prepared via a RF-magnetron sputtering. A rise in the substrate temperatures promoted th...
-
Article
Influence of the selenium-vapor flow-rate in the photovoltaic properties of Cu(In, Ga)Se2 thin films prepared via a solution coating process
The influence of selenium-vapor flow-rates in the microstructure and photovoltaic characteristics of Cu(In, Ga)Se2 films prepared using a solution coating process was investigated in this study. An increase in th...
-
Article
Characterization of Cu2ZnSnSe4 (CZTSe) nanoparticles synthesized via solvothermal method for solar cell applications
Stannite Cu2ZnSnSe4 (CZTSe) nanoparticles were synthesized using a simple solvothermal process at low temperatures using ethylenediamine as a solvent. The structures and morphologies of CZTSe nanoparticles were ...
-
Article
Effects of CBD-derived CdS film thickness on the photovoltaic properties of Cu(In,Ga)Se2 solar cells
This study investigates the effects of the thickness of CdS buffer layers on the photovoltaic properties of Cu(In,Ga)Se2 solar cells. Continuous and dense CdS films were formed with a thickness of 103.7 nm. Incre...
-
Article
Preparation and characterization of Cu(In,Ga)Se2 films from nanosized alloy precursors
CuInSe2 films were successfully prepared from the nanoparticles that were synthesized via the chemical reduction reaction. In the chemical reduction process using ethylene glycol as the solvent and NaBH4 as a red...
-
Article
Preparation of AgIn1−xGaxSe2 films from sol–gel derived precursors via a coating method
AgIn1−xGaxSe2 films were prepared via coating the pastes that contained sol–gel derived precursors and selenium powders, followed by the normal heating process without using H2Se. Pure-phased AgIn1−xGaxSe2 films ...