Abstract
The aim of this study is to investigate the effect of water migration from cracks into the bulk paste on autogenous self-healing. Nuclear magnetic resonance (NMR) technique was utilized to monitor water migration from cracks into the bulk paste during the process of autogenous self-healing. NMR results show that initially the water in the crack migrates into the bulk paste and the water content of the bulk paste increases significantly. However, after 5-h autogenous self-healing, the amount of non-chemically bound water in the bulk paste (adjacent to the crack surfaces) determined by NMR decreased instead. It indicates that some of the water coming from the crack was used for additional hydration of unhydrated cement particles in the bulk paste (during the process of autogenous self-healing). Before this study, in term of autogenous self-healing only the recoveries that related to the filling of cracks were concerned. The observation and quantification of densification of cement paste adjacent to the crack surfaces provides a new insight into autogenous self-healing.
Similar content being viewed by others
References
van Breugel K (2012) Self-healing material concepts as solution for aging infrastructure. In 37th conference on our world in concrete & structures, Singapore
Dry CM (2000) Three designs for the internal release of sealants, adhesives, and waterproofing chemicals into concrete to reduce permeability. Cem Concr Res 30(12):1969–1977
Ramachandran SK, Ramakrishnan V, Bang SS (2001) Remediation of concrete using micro-organisms. ACI Mater J 98:3–9
Ahn TH, Kishi T (2010) Crack self-healing behavior of cementitious composites incorporating various mineral admixtures. J Adv Concr Technol 8(2):16
Joseph C, Jefferson A, Isaacs B, Lark R, Gardner D (2010) Experimental investigation of adhesive-based self-healing of cementitious materials. Mag Concr Res 62(11):831–843
Van Tittelboom K, De Belie N, Van Loo D, Jacobs P (2011) Self-healing efficiency of cementitious materials containing tubular capsules filled with healing agent. Cem Concr Compos 33(4):497–505
Wiktor V, Jonkers HM (2011) Quantification of crack-healing in novel bacteria-based self-healing concrete. Cem Concr Compos 33(7):763–770
Wang J, Van Tittelboom K, De Belie N, Verstraete W (2012) Use of silica gel or polyurethane immobilized bacteria for self-healing concrete. Constr Build Mater 26(1):532–540
de Rooij MK, Tittelboom Van, De Belie N, Schlangen E (2013) Self-healing phenomena in cement-based materials. Springer, New York
Soroker VJ, Denson AJ (1926) Autogenous healing of concrete. Zement 25(30):76
Brandeis F (1937) Autogenous healing of concrete. Beton u Eisen 36(12):11
Hearn N (1998) Self-sealing, autogenous healing and continued hydration: what is the difference? Mater Struct 31(8):563–567
Hyde GW, Smith WJ (1889) Results of experiments made to determine the permeability of cements and cement mortars. J Frankl Inst Phila 128:199–207
Glanville WH (1931) The permeability of Portland cement concrete. Build Res Tech Pap 3:1–61
Sahmaran M, Keskin SB, Ozerkan G, Yaman IO (2008) Self-healing of mechanically-loaded self consolidating concretes with high volumes of fly ash. Cem Concr Compos 30(10):872–879
Van Tittelboom K, Gruyaert E, Rahier H, De Belie N (2012) Influence of mix composition on the extent of autogenous crack healing by continued hydration or calcium carbonate formation. Constr Build Mater 37:349–359
Lv Z, Chen H (2013) Self-healing efficiency of unhydrated cement nuclei for dome-like crack mode in cementitious materials. Mater Struct 46:1–12
Yang Y, Lepech MD, Yang E-H, Li VC (2009) Autogenous healing of engineered cementitious composites under wet-dry cycles. Cem Concr Res 39(5):382–390
Qian S, Zhou J, de Rooij MR, Schlangen E, Ye G, van Breugel K (2009) Self-healing behavior of strain hardening cementitious composites incorporating local waste materials. Cem Concr Compos 31(9):613–621
Granger S, Loukili A, Pijaudier-Cabot G, Chanvillard G (2007) Experimental characterization of the self-healing of cracks in an ultra high performance cementitious material: mechanical tests and acoustic emission analysis. Cem Concr Res 37(4):519–527
Ter Heide N (2005) Crack healing in hydrating concrete. Msc, Delft University of Technology, Delft
Edvardsen C (1999) Water permeability and autogenous healing of cracks in concrete. ACI Mater J 96(4):448–454
Reinhardt H-W, Jooss M (2003) Permeability and self-healing of cracked concrete as a function of temperature and crack width. Cem Concr Res 33(7):981–985
Hearn N, Morley C (1997) Self-sealing property of concrete-experimental evidence. Mater Struct 30(7):404–411
Schlangen E, Ter Heide N, van Breugel K (2006) Crack healing of early age cracks in concrete. In: Konsta-Gdoutos MS (ed) Measuring, monitoring and modeling concrete properties. Springer, Netherlands
Huang H, Ye G, Damidot D (2013) Characterization and quantification of self-healing behaviors of microcracks due to further hydration in cement paste. Cem Concr Res 52:71–81
Jacobsen S, Sellevold EJ (1996) Self healing of high strength concrete after deterioration by freeze/thaw. Cem Concr Res 26(1):55–62
Li VC, Yang E-H (2007) Self-healing in concrete materials. In: van der Zwaag S (ed) Self healing materials an alternative approach to 20 centuries of materials science. Springer, Dordrecht
Huang H, Ye G, Damidot D (2014) Effect of blast furnace slag on self-healing of microcracks in cementitious materials. Cem Concr Res 60:68–82
Callaghan PT (1991) Principles of nuclear magnetic resonance microscopy. Clarendon Press, Oxford
Blumich B (2000) NMR imaging of materials. Oxford Science Publications, New York
Hazrati K, Pel L, Marchand J, Ko**a K, Pigeon M (2002) Determination of isothermal unsaturated capillary flow in high performance cement mortars by NMR imaging. Mater Struct 35(10):614–622
Valckenborg R, Pel L, Hazrati K, Ko**a K, Marchand J (2001) Pore water distribution in mortar during drying as determined by NMR. Mater Struct 34(10):599–604
Friedemann K, Stallmach F, Kärger J (2006) NMR diffusion and relaxation studies during cement hydration—a non-destructive approach for clarification of the mechanism of internal post curing of cementitious materials. Cem Concr Res 36(5):817–826
Kimmich R (1997) NMR tomography, diffusometry, relaxometry. Springer, Heidelberg
McDonald PJ, Mitchell J, Mulheron M, Monteilhet L, Korb JP (2007) Two-dimensional correlation relaxation studies of cement pastes. Magn Reson Imaging 25(4):470–473
Ko**a K, Pel L (1994) One-dimensional scanning of moisture in porous materials with NMR. Rev Sci Instrum 65(12):3673–3681
Pel L (1995) Moisture transport in porous building materials. Ph.D, Eindhoven University of Technology
Powers TC, Brownyard TL (1948) Studies of the physical properties of hardened Portland cement paste (9 parts), J Am Concr Inst 43, Bulletin 22, Chicago
Parrot LJ, Killoh DC (1984) Prediction of cement hydration. Br Ceram Proc 35:41–53
Taylor HFW (1997) Cement chemistry. Thomas Telford Publishing, London
Ye G (2003) Experimental study and numerical simulation of the development of the microstructure and permeability of cementitious materials. PhD, Delft University of Technology
van der Lee J, de Windt L (1999) “CHESS.” from http://chess.geosciences.ensmp.fr/
Liu J, **ng F, Dong B, Ma H, Pan D (2014) Study on water sorptivity of the surface layer of concrete. Mater Struct 47(11):1941–1951
Bogue RH (1955) The chemistry of Portland cement. Reinhold Pub. Corp, New York
Acknowledgments
The authors would like to thank the National Basic Research Program of China (973 Program: 2011CB013800), National Nature Science Fund (51178104) and the China Scholarship Council (CSC) for the financial support. Mrs **g** Han’s help on the NMR experiments is also appreciated.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Huang, H., Ye, G. & Pel, L. New insights into autogenous self-healing in cement paste based on nuclear magnetic resonance (NMR) tests. Mater Struct 49, 2509–2524 (2016). https://doi.org/10.1617/s11527-015-0664-9
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1617/s11527-015-0664-9