Abstract
Epitaxial potassium niobate films have been deposited by metalorganic chemical vapor deposition (MOCVD). X-ray diffraction of the films deposited on (100) spinel substrates shows (110) and (001) reflections, indicating a multidomain structure. The electro-optic properties of the thin films were measured using a transmission technique. Effective electro-optic coefficients as large as 470 pm/V were observed. The observed electro-optic response was dominated by domain reorientation effects.
Similar content being viewed by others
References
O. Mitomi, K. Noguchi, and H. Miyazawa, 8th Annual Lasers and Electro Optics Meeting (LEOS), San Francisco, 1995.
D. K. Fork, F. Armani-Lepplingard, J. J. Kingston et al., Proceedings of the Materials Research Society, Vol.392, pp.189 (1995).
V. Gopalan and R. Raj, Appl. Phys. Lett. 68 (10), 1323 (1996).
M. J. Nystrom, B. W. Wessels, D. B. Studebaker et al., Applied Physics Letters 67, 365 (1995).
Y. Uematsu, Japanese Journal of Applied Physics 13 (9), 1362 (1974).
M. J. Nystrom, Ph.D. Thesis, Northwestern University, 1996.
H. **e, W.-Y. Hsu, and R. Raj, J. Appl. Phys. 77 (7), 3420 (1995).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Nystrom, M.J., Wessels, B.W. The Effects of Domain Structure on the Electro-Optic Response of Potassium Niobate Thin Films. MRS Online Proceedings Library 453, 259–264 (1996). https://doi.org/10.1557/PROC-453-259
Published:
Issue Date:
DOI: https://doi.org/10.1557/PROC-453-259