Abstract
A simplified one-diode one-resistor (1D1R) resistive switching memory cell that uses only four layers of TaN/ZrTiO x /Ni/n+-Si was proposed to suppress sneak current where TaN/ZrTiO x /Ni can be regarded as a resistive-switching random access memory (RRAM) device while Ni/n+-Si acts as an Schottky diode. This is the first RRAM cell structure that employs metal/semiconductor Schottky diode for current rectifying. The 1D1R cell exhibits bipolar switching behavior with SET/RESET voltage close to 1 V without requiring a forming process. More importantly, the cell shows tight resistance distribution for different states, significantly rectifying characteristics with forward/reverse current ratio higher than 103 and a resistance ratio larger than 103 between two states. Furthermore, the cell also displays desirable reliability performance in terms of long data retention time of up to 104 s and robust endurance of 105 cycles. Based on the promising characteristics, the four-layer 1D1R structure holds the great potential for next-generation nonvolatile memory technology.
Avoid common mistakes on your manuscript.
Background
As conventional flash memory is approaching its scaling limits, resistive-switching random access memory (RRAM), one of the most promising emerging nonvolatile memories, holds the potential to replace it for future memory-hungry applications because of superior speed, higher density, and complementary metal-oxide-semiconductor (CMOS) compatibility [1–4]. For the last decade, although many dielectrics have shown resistive switching characteristics, undesirable cross-talk through neighboring cells due to sneak current leads to read disturbance and limits the array size. To circumvent the issue, series connection of one diode (1D) with one RRAM (1R) to form the so-called 1D1R cell has been proposed since the sneak current can be suppressed by the rectifying the characteristics without sacrificing the storage density. The requirements of the diode include large ratio between forward and reverse current (F/R ratio) under read operation, fab-friendly process, and many types of diodes were discussed in the literature. Metal-insulator-metal (MIM)-based diodes such as Pt/TiO2/Ti [5, 6], Pt/CoO/IZO/Pt [7], and Pt/TiO x /Pt [8] meet the requirement of high F/R ratio, however, the implementation of these diodes necessitates at least three layers and the adoption of high-work function Pt, increasing the complexity of integration and process cost respectively. Besides aforementioned diodes, W/TiO x /Ni-based MIM diode [9] is promising since it achieves F/R ratio larger than 1,000 without using Pt and successfully demonstrates the integration with bipolar RRAM. Nevertheless, three layers are still required to implement the diodes. Other types of diode include p-type/n-type oxide-based diodes such as NiO x /TiO x [10], CuO x /InZnO x [11], and NiO x /ITO x [12], or polymer film such as P3HT/n-ZnO [13]. Even though high F/R ratio is achieved, most oxides are not compatible with incumbent ultra large scale integration (ULSI) technology. Diode based on p-type/n-type Si is another viable technology; although it has been integrated with phase change memory [14], related research on RRAM has not been reported. In addition, with top and bottom electrodes, these diodes require four layers to be implemented; thus, the issue of process complexity still remains. By integrating the aforementioned diodes with RRAM devices, process that needs more than four layers is indispensable.
Recently, without the need of a diode, RRAM devices with self-rectifying behavior have been widely developed because of the simpler process. For self-rectifying RRAM devices, dielectric and electrode should be carefully selected to concurrently meet the requirement of large F/R ratio for diode and high RHRS/RLRS ratio for RRAM where RHRS and RLRS respectively denote the resistance at high-resistance state (HRS) and low-resistance state (LRS). Most device structures with self-rectifying behavior such as Cu/a-Si/WO3/Pt [15], Pt/Al/PCMO/Pt [16], and Pt/ZrO x /HfO x /TiN/HfO x /ZrO x /Pt [17] still possess unsatisfactory RHRS/RLRS ratio (approximately 10) and F/R ratio (approximately 100). In addition, it usually requires at least four layers to implement self-rectifying characteristics for aforementioned RRAM devices and the structure compromises the advantage of simple process of self-rectifying devices. Ni/AlO x /n+-Si [18], a simpler structure with self-rectifying characteristics, exhibits desirable RHRS/RLRS and F/R ratio. However, forming voltage larger than 5 V is required, and there is room to improve the operation voltage which is higher than 2 V. In this work, a novel 1D1R cell structure based on TaN/ZrTiO x /Ni/n+-Si was proposed where TaN/ZrTiO x /Ni was employed as the resistive switching element and Ni/n+-Si played the role of Schottky diode. The reason to adopt ZrTiO x is that it has been shown to have desirable RRAM characteristics [19]. Compared to those published in the literature, the intriguing points of this work lie in four aspects: (1) This is the first structure that uses metal/semiconductor Schottky diodes to rectify current characteristics and the whole structure requires only four layers which are much simpler than other 1D1R structures and even comparable to self-rectifying devices. (2) This 1D1R cell displays desirable electrical characteristics in terms of forming-free property, RHRS/RLRS ratio higher than 103, F/R ratio larger than 103, operation voltage close to 1 V, negligible resistance change up to 104 s retention time at 125°C, and robust endurance of 105 cycles. (3) Unlike some 1D1R structures that use special materials as diode, all the layers used in this work are fab-friendly and can be fully integrated with existing ULSI process.
Methods
N-type Si wafer with do** concentration of 2 × 1017 cm−3 was used as the starting material for 1D1R cell fabrication. A 35-nm Ni was initially deposited on the Si wafer as the bottom electrode of MIM-based RRAM device. Note that the Ni layer on the n-type Si substrate also formed the Schottky diode because of the metal/semiconductor junction. Next, a 10-nm oxygen-deficient ZrTiO x film was deposited by e-beam evaporation from a pre-mixed source that contains ZrO2 and Ti at room temperature as the resistance switching dielectric. TaN of 35 nm was then deposited and patterned by shadow mask as the top electrode. Finally, complete 1D1R cells with the structure of TaN/ZrTiO x /Ni/n+-Si were formed. For electrical characterization, voltage was applied on the top electrode with the grounded Si substrate. Separate RRAM (TaN/ZrTiO x /Ni) and Schottky diode (Ni/n+-Si) were also formed to evaluate the behavior of single device. Note that single RRAM devices were fabricated on SiO2 rather than Si substrate for better isolation so that pure RRAM performance can be measured. All the electrical data were measured by devices with the area of 250 μm × 250 μm. In addition to electrical analysis, transmission electron microscopy (TEM) and x-ray diffraction (XRD) were respectively used to characterize the interface property between Ni/n+-Si and to study the crystallinity of the switching dielectric ZrTiO x .
Results and discussion
Physical analysis of 1D and 1R structure
Figure 1 shows the XRD spectrum for ZrTiO x film prior to the deposition of top electrode TaN. No diffraction peaks are observed and it implies that the film is amorphous phase. In fact, it has been reported that ZrTiO4 can be crystallized in orthorhombic phase at 600°C [20]. Without any thermal treatment in this work, it is reasonable for the ZrTiO x film to be amorphous. The inset shows the cross-sectional TEM image for the interface between Ni and n+-Si. Besides the clear single-crystal Si structure, the Ni film is found to be amorphous without observing any crystalline layer near Si interface. This phenomenon suggests that no nickel silicide was formed in the device since the formation of nickel silicide will result in crystalline layer. Nickel silicide is a commonly used material to improve contact resistance and has been well studied in the literature [21] from which Ni2Si, NiSi, and NiSi2 can be respectively formed at 250°C, 350°C, and 700°C. Again, since no thermal treatment was employed in this work, the Ni film of amorphous phase without forming any silicide is expected.
DC behavior for 1D, 1R, and 1D1R devices
Figure 2 shows the current-voltage (I-V) curves for Ni/n+-Si based diode and it was measured with grounded n+-Si, and a typical Schottky diode curve is demonstrated because of the metal/semiconductor junction. The F/R ratio for this diode measured at ±0.2 V is about 103 which proves good rectifying properties. In fact, from the exponential forward bias region, the barrier height for Ni/n+-Si junction is extracted to be 0.66 eV with the consideration of image force-lowering effect. To further enhance the F/R ratio, the do** concentration of Si can be modulated to be lower so that the effect of image force lowering and tunneling can be suppressed. Figure 3 shows the switching behavior for TaN/ZrTiO x /Ni-based RRAM devices and it demonstrates self-compliance, forming-free characteristics with SET/RESET voltage lower than 1 V, and RHRS/RLRS ratio of 9 × 103 at read voltage of +0.1 V. The initial LRS can be ascribed to the existence of a pre-existed filament that is composed of oxygen vacancies in the nonstoichiometric ZrTiO x . As a negative bias is applied on the top electrode TaN (positive bias applied on bottom electrode Ni), it will build an electric field that drives oxygen vacancies to move toward the top electrode TaN and therefore the filament will be ruptured, making devices switch to HRS. In fact, the voltage-driven oxygen vacancies movement has been proposed in the literature as the switching mechanism for other dielectrics [22, 23]. On the other hand, applying a positive bias on the top electrode TaN (negative bias applied on bottom electrode) under HRS would repel the oxygen vacancies near the top electrode toward the bottom electrode and re-align the oxygen vacancies to form conducting filaments because of the downward electric field, switching devices from HRS to LRS. In addition, the current conduction mechanism at HRS and LRS is respectively extracted to be Schottky emission and ohmic conduction (not shown). Because the current conduction mechanism at LRS is extracted to be ohmic conduction, the LRS current at both polarities is similar. Since individual diode and RRAM have shown good electrical properties, the performance of device formed by stacking RRAM and diode (TaN/ZrTiO x /Ni/n+-Si) was analyzed and the hysteresis I-V curve is shown in Figure 4. The stacked device (1D1R) still represents resistive switching behavior. Represented in Figure 5 is the statistical distribution of resistance and RHRS/RLRS ratio for 1R and 1D1R devices. Even with the integration of a diode, the resistance distribution does not degrade and the tight distribution is advantageous for cell integration. The major differences from 1R cell are summarized as follows:
-
1.
The RESET current decreases to be around 10−5 A which is two orders lower than that of 1R cell. This improvement mainly comes from the connected reverse-biased diode which limits the current flowing through it. The phenomenon is similar to other 1D1R structure reported in [9, 10].
-
2.
The current level at LRS demonstrates significant rectifying characteristics for both polarities. At ±0.1 V, the F/R ratio can be up to 103, which resulted from the series connection of the diode and capable of suppressing the sneak current effect.
-
3.
The operation current becomes lower while R HRS/R LRS ratio degrades to approximately 2,300 at +0.1 V. Nevertheless, the ratio is still large enough to distinguish logic ‘1’ and ‘0’. The lower current level can be explained by the fact that for a given applied voltage, there is voltage drop on the diode, and therefore the effective voltage drop on the RRAM is smaller than that of 1R cell. In addition, for positive bias which corresponds to diode operated under forward region because the effective voltage drop on the RRAM directly depends on its resistance state and the nonlinear I-V characteristics of the diode, the R HRS/R LRS ratio becomes degraded.
-
4.
SET/RESET voltage slightly increases. This is attributed to voltage drop across the diode and therefore a larger voltage is required to form equivalent voltage on the RRAM. Nevertheless, the SET/RESET voltage is still close to 1 V which is beneficial for low-power operation.
Conduction mechanism and retention characteristics
Figure 6 explores the conduction mechanism for LRS and HRS at positive bias by analyzing the correlation between current and voltage for 1D1R cell. The same as the case of 1R cell, for positive bias, it can be found that ohmic conduction and Schottky emission correspond to LRS and HRS respectively. The reason why conduction mechanism remains unchanged can be explained as follows. Under positive bias, the Schottky diode operates in forward region. For LRS, a relatively large voltage drop across the diode is expected, and the fully conducting diode can be regarded as the series connection of an ideal diode with cut-in voltage VD0 and a dynamic resistor (rd), according to piecewise linear diode model. Based on this model, the ohmic conduction for LRS is reasonable since there are two resistors (from RRAM and diode) connected in series in the equivalent circuit. On the other hand, for HRS, the voltage drop across the diode is small which may make its operating point less than the cut-in voltage and therefore the conduction mechanism for the diode is dominated by Schottky emission. Combined with the Schottky emission conduction for single RRAM at HRS, the same conduction mechanism is expected for 1D1R cell. To assess the ability to maintain the stored data for 1D1R cell, retention performance was measured at 125°C with a read voltage of 0.1 V and the result is shown in Figure 7 which demonstrates RHRS/RLRS ratio over 2,000 with negligible degradation up to 104 s. Figure 8 shows the switching endurance for 1D1R cell by applying continuous ±1.4 V pulse of 250 ns and the current was read at 0.1 V. The sensing margin can achieve 2,286 times initially and then slightly degrade to 2,105 times after 105 cycles. This stable endurance performance implies that the 1D1R cell is robust enough to be used for practical memory applications.
Conclusions
A simplified 1D1R cell with only four layers was proposed by adopting TaN/ZrTiO x /Ni/n+-Si structure. Table 1[8, 10, 15, 16, 24] summarizes the main device characteristics of this work, and other RRAM structures with rectifying properties are also listed for comparison. The 1D1R cell developed in this work shows promising characteristics in terms of low operation voltage close to 1 V, tight resistance distribution for different states, large F/R ratio of 103, high RHRS/RLRS ratio of approximately 2,300, long retention time up to 104 s, and robust endurance up to 105 cycles, which are beneficial for lower power consumption, sneak current suppression, and data storage. Further optimization of the diode process is required to enhance rectifying performance which could further suppress the sneak current and make a larger array size possible.
References
Liu CY, Huang JJ, Lai CH, Lin CH: Influence of embedding Cu nano-particles into a Cu/SiO2/Pt structure on its resistive switching. Nanoscale Res Lett 2013, 8: 156. 10.1186/1556-276X-8-156
Chang KC, Huang JW, Chang TC, Tsai TM, Chen KH, Young TF, Chen JH, Zhang R, Lou JC, Huang SY, Pan YC, Huang HC, Syu YE, Gan DS, Bao DH, Sze SM: Space electric field concentrated effect for Zr:SiO2 RRAM devices using porous SiO2 buffer layer. Nanoscale Res Lett 2013, 8: 523. 10.1186/1556-276X-8-523
Prakash A, Jana D, Maikap S: TaOx-based resistive switching memories: prospective and challenges. Nanoscale Res Lett 2013, 8: 418. 10.1186/1556-276X-8-418
Ismail M, Huang CY, Panda D, Hung CJ, Tsai TL, Jieng JH, Lin CA, Chand U, Rana AM, Ahmed E, Talib I, Nadeem MY, Tseng TY: Forming-free bipolar resistive switching in nonstoichiometric ceria films. Nanoscale Res Lett 2014, 9: 45. 10.1186/1556-276X-9-45
Huang JJ, Kuo CW, Chang WC, Hou TH: Transition of stable rectification to resistive-switching in Ti/TiO2 Pt oxide diode. Appl Phys Lett 2010, 96: 262901. 10.1063/1.3457866
Park WY, Kim GH, Seok JY, Kim KM, Song SJ, Lee MH, Hwang CS: A Pt/TiO2/Ti Schottky-type selection diode for alleviating the sneak current in resistance switching memory arrays. Nanotechnology 2010, 21: 195201. 10.1088/0957-4484/21/19/195201
Lee DY, Tsai TL, Tseng TY: Unipolar resistive switching behavior in Pt/HfO2/TiN device with inserting ZrO2 layer and its 1 diode-1 resistor characteristics. Appl Phys Lett 2013, 103: 032905. 10.1063/1.4816053
Shima H, Takano F, Muramatsu H, Akinaga H, Inoue IH, Takagi H: Control of resistance switching voltages in rectifying Pt/TiOx/Pt trilayer. Appl Phys Lett 2008, 92: 043510. 10.1063/1.2838350
Li YT, Long SB, Lv HB, Liu Q, Wang M, **e HW, Zhang KW, Yang XY, Liu M: Novel self-compliance bipolar 1D1R memory device for high-density RRAM application. In IMW IEEE International Memory Workshop: May 26–29 2013; Monterey. USA: IEEE; 2013:184–187.
Lee MJ, Seo S, Kim DC, Ahn SE, Seo DH, Yoo IK, Baek IG, Kim DS, Byun IS, Kim SH, Hwang IR, Kim JS, Jeon SH, Park BH: A low‒temperature‒grown oxide diode as a new switch element for high‒density nonvolatile memories. Adv Mater 2007, 19: 73–76. 10.1002/adma.200601025
Kang BS, Ahn SE, Lee MJ, Stefanovich G, Kim KH, **anyu WX, Lee CB, Park Y, Baek IG, Park BH: High‒current‒density CuOx/InZnOx thin‒film diodes for cross‒point memory applications. Adv Mater 2008, 20: 3066–3069. 10.1002/adma.200702932
Lee WY, Mauri D, Hwang C: High-current-density ITOx/NiOx thin-film diodes. Appl Phys Lett 1998, 72: 1584. 10.1063/1.121122
Katsia E, Huby N, Tallarida G, Kutrzeba-Kotowska B, Perego M, Ferrari S, Krebs FC, Guziewicz E, Godlewski M, Osinniy V: Poly(3-hexylthiophene)/ZnO hybrid pn junctions for microelectronics applications. Appl Phys Lett 2009, 94: 143501. 10.1063/1.3114442
Oh JH, Park JH, Lim YS, Lim HS, Oh YT, Kim JS, Shin JM, Song YJ, Ryoo YC, Lim DW, Park SS, Kim JI, Kim JH, Yu J, Yeung F, Jeong CW, Kong JH, Kang DH, Koh GH, Jeong GT, Jeong HS, Kinam K: Full integration of highly manufacturable 512 Mb PRAM based on 90 nm technology. In IEDM Technical Digest IEEE International Electron Devices Meeting: December 11–13 2006; San Francisco. USA: IEEE; 2006:1–4.
Lv H, Li Y, Liu Q, Long S, Li L, Liu M: Self-rectifying resistive-switching device with a-Si/WO3 bilayer. IEEE Electron Device Lett 2013, 32: 229–231.
Minseok J, Dong-jun S, Seonghyun K, Joonmyoung L, Wootae L, Ju-Bong P, Sangsoo P, Seungjae J, Jungho S, Daeseok L, Hyunsang H: Novel cross-point resistive switching memory with self-formed Schottky barrier. In VLSI Technology Symposium: June 15–17 2010; Honolulu. USA: IEEE; 2010:53–54.
Linn E, Rosezin R, Kügeler C, Waser R: Complementary resistive switches for passive nanocrossbar memories. Nature Mater 2010, 9: 403–406. 10.1038/nmat2748
Tran XA, Zhu W, Liu WJ, Yeo YC, Nguyen BY, Yu HY: A self-rectifying AlOy bipolar RRAM with sub-50-μA set/reset current for cross-bar architecture. IEEE Electron Device Lett 2012, 33: 1402–1404.
Wu YH, Wu JR, Hou CY, Lin CC, Wu ML, Chen LL: ZrTiOx-based resistive memory with MIS structure formed on Ge layer. IEEE Electron Device Lett 2012, 33: 435–437.
Wu ML, Wu YH, Chao CY, Lin CC, Wu CY: Crystalline ZrTiO4-gated Ge meta-oxide-semiconductor devices with amorphous Yb2O3 as a passivation layer. IEEE Trans Nanotechnology 2013, 12: 1018–1021.
Deng F, Johnson RA, Asbeck PM, Lau SS, Dubbelday WB, Hsiao T, Woo J: Salicidation process using NiSi and its device application. J Appl Phys 1997, 81: 8047–8051. 10.1063/1.365410
Wang Q, Itoh Y, Hasegawa T, Tsuruoka T, Yamaguchi S, Watanabe S, Hiramoto T, Aono M: Nonvolatile three-terminal operation based on oxygen vacancy drift in a Pt/Ta2O5-x/Pt. Pt structure. Appl Phys Lett 2013, 102: 233508. 10.1063/1.4811122
Tang G, Zeng F, Chen C, Liu H, Gao S, Song C, Lin Y, Chen G, Pan F: Programmable complementary resistive switching behaviours of a plasma-oxidised titanium oxide nanolayer. Nanoscale 2013, 5: 422–428. 10.1039/c2nr32743k
Tran X, Gao B, Kang J, Wu X, Wu L, Fang Z, Wang Z, Pey K, Yeo Y, Du A, Liu M, Nguyen BY, Li MF, Yu HY: Self-rectifying and forming-free unipolar HfOx based-high performance RRAM built by fab-available materials. In IEDM Technical Digest IEEE International Electron Devices Meeting: December 5–7 2011; Washington, DC. USA: IEEE; 2011:713–716.
Acknowledgements
This work was supported by the National Science Council of Taiwan under Contracts NSC 101-2628-E-007-012-MY3 and NSC 101-2120-M-009-004.
Author information
Authors and Affiliations
Corresponding author
Additional information
Competing interests
The authors declare that they have no competing interests.
Authors’ contributions
CCL made contributions to analysis and interpretation of data. YHW conceived of the study, participated in the coordination, and involved in drafting the manuscript. YTC designed and set up the experimental procedure, fabricated the devices, and acquired the data. CES conducted the electrical measurement of the devices. All authors read and approved the final manuscript.
Authors’ original submitted files for images
Below are the links to the authors’ original submitted files for images.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made.
The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder.
To view a copy of this licence, visit https://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Lin, CC., Wu, YH., Chang, YT. et al. Simplified ZrTiO x -based RRAM cell structure with rectifying characteristics by integrating Ni/n + -Si diode. Nanoscale Res Lett 9, 275 (2014). https://doi.org/10.1186/1556-276X-9-275
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/1556-276X-9-275