Abstract
The current strategies for building 2D organic-inorganic heterojunctions involve mostly wet-chemistry processes or exfoliation and transfer, leading to interface contaminations, poor crystallizing, or limited size. Here we show a bottom-up procedure to fabricate 2D large-scale heterostructure with clean interface and highly-crystalline sheets. As a prototypical example, a well-ordered hydrogen-bonded organic framework is self-assembled on the highly-oriented-pyrolytic-graphite substrate. The organic framework adopts a honeycomb lattice with faulted/unfaulted halves in a unit cell, resemble to molecular “graphene”. Interestingly, the topmost layer of substrate is self-lifted by organic framework via strong interlayer coupling, to form effectively a floating organic framework/graphene heterostructure. The individual layer of heterostructure inherits its intrinsic property, exhibiting distinct Dirac bands of graphene and narrow bands of organic framework. Our results demonstrate a promising approach to fabricate 2D organic-inorganic heterostructure with large-scale uniformity and highly-crystalline via the self-lifting effect, which is generally applicable to most of van der Waals materials.
Introduction
Heterostructures have been widely used as a basic building block in the advanced semiconductor devices owing to their essential and attractive structural, interfacial, and electronic properties, especially for a comparatively better electrical and optical performance with respect to individual materials. In recent years, two-dimensional (2D) heterojunctions are vastly developed soon after the rise of graphene1 and other 2D materials2,3,4,5,6,7. The organic−inorganic heterostructures may take the advantages of both organic and inorganic materials, for example to make it flexible like an organic film and at the same time wearable like an inorganic film. The combination of their different properties and functionalities may broaden the device’s capabilities and endow special applications that neither one can achieve alone. By combining the organic layers with a dangling-bond-free surface of inorganic van der Waals (vdW) materials8,9,10,11, 2D organic-inorganic heterojunctions have emerged and become new paradigms with presenting unprecedented multifunctional application12,13,14,15,16 and novel device architectures17,18,19,20. Currently, the strategies for building 2D organic-inorganic heterojunctions include, i.e., solution processing21,22, mechanical exfoliation and transfer23,24,25,26, and vapor phase growth27. The first method involves inevitably the contamination from wet-chemistry while the second has limited the size of heterojunction (~micrometers). In contrast, organic vapor phase growth can grow a highly-ordered organic layer on the substrate surface and produce high-quality heterostructures28, such as the organic layers on the surface of graphene29,30, WS231, and MoSe232. However, the residuals at the interface from vapor phase growth strongly affect the quality of heterostructures33,34. Up to now, a rational bottom-up design of 2D high-quality organic-inorganic heterojunctions with the appealing properties of both organic and inorganic layers is rarely demonstrated.
Here, we develop an approach to bottom-up fabricate 2D large-scale organic-inorganic heterostructure with cleanest interface and highly-crystalline layer structure, all carried out in ultrahigh vacuum (UHV) environment. The heterostructure is composed of a monolayer 1,3,5-tris(4-hydroxyphenyl)benzene (THPB)-hydrogen-bonded organic framework (HOF) and the graphene layer made by self-lifting the topmost layer from highly-oriented-pyrolytic-graphite (HOPG) via strong interlayer coupling. By utilizing in-situ high resolution scanning tunneling microscopy/spectroscopy (STM/STS) and angle-resolved photoelectron spectroscopy (ARPES), we observed a honeycomb THPB-HOF lattice with faulted/unfaulted halves, Dirac bands near EF and a series of narrow bands at deeper energies. Dirac bands observed in the energy range of >1.0 eV below EF with high fermion velocity ≈4.83–5.25 eV·Å, can be attributed to the self-lifted graphene layer. In addition, narrow bands are originated from THPB-HOF lattice, as a unique form of molecular “graphene”35, in agreement with DFT calculated band structure consisting of topological flat bands. We also observed local spin states located slightly above the EF in the tunneling spectra, induced by removing pz orbitals in π-conjugated THPB systems. Our results demonstrate the feasibility of fabricating large-scale 2D organic framework/graphene heterostructure, with large-scale uniformity and long-range order. In short, we present a simple effective method to make freestanding 2D large-scale organic-inorganic heterostructure by a self-lifting effect, as confirmed by directly observing the coexistence of distinct Dirac bands with high carrier mobility from graphene and flattened bands of HOF due to enhanced organic-inorganic interaction. We also further demonstrated the generality of our method by growth on MOS2 substrate, where we observed the bandgap transition of MoS2 from bulk to monolayer via again the self-lifting effect induced by THPB-HOF monolayer.
Results
Self-lifting a large-scale graphene from graphite by molecular overlayer
A simple but effective approach for fabricating the large-scale 2D organic/graphene heterostructure is illustrated in Fig. 1a. First, the exfoliation of HOPG provides a clean, atomic flat surface; Second, the deposition of molecules, following with in-situ annealing, allows for the self-assembly of THPB molecules via hydrogen-bonded; At last, the formation of HOF monolayer provides extra force to lift the topmost graphite layer (graphene) from the substrate. All steps are conducted in UHV, giving a contamination-free interface and other notable advantages, i.e. large-scale uniformity, and high quality of both organic and graphene layers, as demonstrated below. The key procedure is the self-lifting of topmost graphite by a moderately-strong interlayer interaction between organic layer and HOPG.
a Schematic drawing to show three-step processes for the formation of 2D HOF and the lifting of topmost graphene layer from HOPG substrate. STM measurements of a large-scale uniform and highly ordered THPB-HOF monolayer and the height profiles measured for THPB-HOF/Gr/HOPG (b) and THPB-HOF/Gr (c), respectively. The image sizes in b and c are 125 × 125 nm2 and 50 × 50 nm2 with the setting parameters of VB = −2.0 V and IT = 10 pA. The slab calculation of the HOF monolayer on top of four graphite layers, showing the initial (d) and final optimized (e) structures. The color of atoms: dark gray (C in THPB), white (H), red (O) and blue (C in graphite), respectively. f The calculated band structure of the optimized HOF/graphene heterostructure within the BZ of THPB-HOF, in which the Dirac band from the lifted graphene layer (green) and narrow bands from THPB-HOF (blue) are seen to coexist.
To demonstrate the feasibility of this approach, we conducted both experiments and DFT calculations. A THPB-HOF monolayer is grown on HOPG substrate (see Methods for sample preparation), and STM images (Fig. 1b and Supplementary Fig. 4) display large-scale uniformity and long-range order of THPB-HOF layer. Height profile measurements in Fig. 1b, c show the distances of HOF/topmost (1st) layer and HOF/1st/second (2nd) layer of HOPG are about 2.65 and 6.48 Å, respectively, giving the distance between the 1st and 2nd layer of HOPG to be about 3.83 Å, significantly larger than the interlayer separation of HOPG (3.34 Å). This is also confirmed by the DFT calculation (Fig. 1d, e and Supplementary Fig. 14). Here the four-layered HOPG is used as a manifestation, but we emphasize that the self-lifting effect of THPB-HOF monolayer and the resultant exfoliation of graphene are robust regardless of the thickness of HOPG (see Supplementary Fig. 14). The optimized structure composed of THPB-HOF and four graphite layers, shows a reduced distance ≈2.71 Å between HOF and the 1st layer, and the enlarged distance ≈3.41 Å between the 1st layer and 2nd layer of HOPG, indicating a stronger coupling between HOF and 1st layer, as well as an effective self-lifting of graphene layer from HOPG substrate. The calculated band structure of the resultant HOF/graphene heterostructure (Fig. 1f) shows the coexistence of both Dirac band of graphene band-folded into the Brillouin zone (BZ) of HOF and narrow bands of THPB-HOF, which serve as the electronic evidence for validating the formation of large-scale floating 2D THPB-HOF/graphene heterostructure, in agreement with the ARPES measurements. We also tried deposit THPB molecule on in-situ-cleaved MoS2 surface. Supplementary Figs. 11 and 12 show the morphology of THPB molecules on MoS2 surface measured by STM. The thickness of monolayer THPB framework is measured about 2.94 Å, similar to 2.65–2.71 Å on HOPG substrate. High resolution STM image in Supplementary Fig. 12b shows the similar HOF structure with unit cell size about 2.67 nm, larger than the size of unit cell of THPB-framework on HOPG (16.5 Å). Most notably, we measured differential conductance spectroscopy (dI/dV) on both clean MoS2 surface and THPB molecule island (Supplementary Fig. 12c, d). The bandgap of MoS2 clean surface is measured about 1.46 eV, slightly smaller than the bandgap (1.78 eV) measured on THPB-framework, indicating the self-lifting effect of THPB-framework acts also on the MoS2 layer. The bulk MoS2 material is reported to have an indirect bandgap of 1.2 eV, whereas two-dimensional (2D) single-layer MoS2 nanosheets have a direct bandgap of 1.8 eV36,37. Our results are consistent with the reported bandgap transition of MoS2 from bulk to monolayer. These results evidently support the generality of our method.
Growth and characterization of large-scale uniform, highly-ordered 2D THPB-HOF on HOPG
The model in Fig. 2a gives the resulted THPB-HOF structure with the non-centrosymmetric space group P6 (No. 168). Previous studies showed that THPB molecules can form self-assembled superstructure on Au(111) and Ag(111) surfaces38,39,40. High resolution image (Fig. 2c) reveals a honeycomb lattice with two edge sharing THPB molecules per unit cell, distinct from the corner-sharing triangular lattice of THPB on Au(111)40. In Fig. 2b, d, each Shuriken-shaped feature is a single THPB molecule, in which three peripheral benzene rings show bright contrast while the central benzene is invisible in STM images. The images of a triangular defect (Fig. 2b, d) provide a hint for the proposed structure, where the size and shape of the black triangular defect resemble a missing THPB molecule.
a The stick models of single THPB molecule and THPB-HOF superstructure. THPB molecules are assembled via O…H-O hydrogen bonding between hydroxyl groups at the corners. Blue dotted lines show the hydrogen bonds. The dotted rhombus indicates the unit cell of THPB-HOF. b Topographic STM image show the large-scale self-assembled THPB-HOF on HOPG substrate. The image size is 50 × 50 nm2 with VB = −1.5 V and IT = 10 pA. c Zoom-in image shows the size of unit cell is about 16.5 Å. The image is 10 × 10 nm2 with VB = −1.0 V and IT = 10 pA. d High resolution image showing a single THPB vacancy. e Top (upper panel) and side (lower panel) view of the optimized structure of THPB-HOF on top of graphene. The white, red, gray and blue balls represent the hydrogen, oxygen, carbon atoms in THPB molecules and the carbon atoms in graphene, respectively. The dashed line indicates the unit cell. f High resolution STM image displaying the unit cell of THPB-HOF, overlaid with the ball-and-stick model of THPB molecules. Yellow dashed ovals indicate the hydrogen bond of O…H-O.
The optimized structure of THPB-HOF/graphene from ab initio DFT calculations is shown in Fig. 2e and Supplementary Fig. 2, which reveals that the constituting molecules with a planar conformation are linked to each other via O…H-O hydrogen bond between hydroxyl groups at the corners. The calculated unit-cell lattice constant is 17.23 Å, consistent with the experimental value of 16.5 Å. The distance between the THPB-HOF and the 1st carbon layer is 2.65 Å (Fig. 1c), indicating a moderately stronger interlayer coupling than vdW interaction. In the unit cell, four phenyl rings of a THPB sit on the top of carbon rings in the underneath graphene layer (Bernal stacking), named “unfaulted” half; while phenyl rings of another THPB are centered around a C atom of the underneath graphene layer (A-B or A-C stacking), named “faulted” half (Fig. 2e). By overlaying the relaxed model on top of the STM image (Fig. 2f), bright protrusions in the STM image correspond to the tilted corner phenyl rings of THPB with the resolved intermolecular structure. Similar contrast of THPB-HOF can be clearly visualized in STM images with different biases in Supplementary Fig. 5. More interestingly, we also observed two different kinds of chirality for H-bond hollow-ring in STM imaging of THPB-HOF, as shown in Supplementary Fig. 6a, b. Interestingly, by viewing each THPB as a “superatom”, the THPB-HOF structure has basically a graphene-like structure with hydrogen bonds connecting the THPBs, instead of covalent C-C bonds in graphene (left-lower panel of Fig. 2a). Two sublattices are attributed to THPB of the faulted and unfaulted halves, which breaks in principle the inversion symmetry and gives rises to an on-site energy difference. The in-situ Raman spectrum of THPB-HOF/HOPG displays the vibrational modes of H-bonds (Supplementary Fig. 15).
ARPES observation of Dirac and narrow bands in THPB-HOF/HOPG
The mesoscale ordered 2D THPB-HOF has enabled the ARPES characterization of its band structure. As a reference, the bare HOPG surface was measured firstly (Supplementary Note 3 and Fig. 7a). In the ranges of 0 ~ −2.0 eV and ±0.6 Å−1, the bare HOPG surface has no band, to provide a clean background for observing the THPB-HOF bands. Figure 3c shows high-resolution ARPES of nearly-full coverage THPB-HOF/HOPG measured at 77 K. Multiple linear dispersive bands can be clearly seen in the energy range from −1.2 eV to EF, which are better resolved in the second-derivative intensity plot (Fig. 3d), marked as λ1 to λ6, not presented in ARPES of bare HOPG. The slopes (Fermi velocity) of bands λ1 to λ6, are estimated to be ≈4.83–5.25 eVÅ (\({{\hslash }}{\nu }_{F}\,\)≈ 7.33–7.96 × 105 ms−1), comparable with that of graphene (1.0 × 106 ms−1)41. Each linear band expands about 0.25 Å−1 in momentum space. Note that the calculated lattice constant of THPB-HOF (17.23 Å) is about seven times of that of graphite (2.46 Å) and the lattice vectors a1 and a2 are aligned parallel with the underlying graphite lattice (Fig. 3a). Considering the size of the graphite BZ (1.7 Å−1 from Γ to K), the deduced BZ of THPB-HOF is about 0.243 Å−1. To explore the origin of these linear bands, the band structure of THPB-HOF/graphene was calculated in a range of −0.2 − 1.05 Å−1 along the ΓHOF-KHOF direction. The calculated result (Fig. 3e and Supplementary Fig. 3) shows multiple linear bands right below the Fermi level, matching nicely with the dispersion of observed linear bands. According to the component analysis of bands as shown in Fig. 1e, here the calculated linear bands are originated from the graphene layer of the THPB-HOF/graphene heterostructure. Instead, two π bands of HOPG, the upper (π1) and the lower π band (π2) with the splitting at the K point ≈0.5 eV, are distinct from the observed linear bands, and hence can be ruled out. Furthermore, the constant-energy contour (CEC) at −0.1 eV in Fig. 3b, signifies the presence of multiple linear bands. A hexagonal ring (band λ1) is clearly visible around the zone center and a series of bands (λ2 to λ6) extend from the center to the zone boundary with equally spacing about 0.24 Å−1. Based on these observations, the bands λ1 to λ6 can be assigned to the Dirac bands of topmost graphene, folded into the BZ of THPB-HOF.
a The relationship between the BZs of HOPG surface and THPB-HOF. Note, the lattice constant of THPB-HOF (17.0 Å) is about seven times of that of graphite (2.46 Å) and the lattice vectors a1 and a2 are aligned parallel with the graphite lattice. b The CEC measured at −0.1 eV and 77 K. The hexagonal-shaped linear bands, λ1 to λ6 of THPB-HOF are clearly visible. The blue dashed lines indicate the line-cut taken for measurement in c and d. High-resolution ARPES spectra (c) and second-derivative intensity plot (d), taken along Γ-K// direction from a nearly-full coverage of THPB-HOF. A series of linear dispersive bands can be clearly resolved, denoted as λ1 to λ6 in the momentum. e The calculated band structure of THPB-HOF/graphene along Γ-K direction from −0.21 to 1.05 Å−1. f The calculated band structure within the energy window from −2.0 eV to +4.0 eV. The optimized structure of THPB-HOF using the experimental lattice constants of a = b = 16.5 Å. The topmost two sets of valence bands are highlighted by the purple dashed rectangle, and a zoomed-in view is presented in i. The upper bands are dual topological flat bands in hexagonal lattice, while the lower bands are Dirac bands resembling the case of graphene. The blue, gray and olive bands are DFT, px,y-orbital and pz-orbital TB model results, respectively. The fitting NN hop** strengths for the px,y-orbital and pz-orbital TB models are 0.023 and 0.020 eV. The large energy scaled ARPES spectra (g) and second-derivative intensity plot (h), taken from −5.5 eV to 0 eV for a full-coverage THPB-HOF film. A series of non-dispersive bands can be clearly resolved at the energies below −2.1 eV. “H” and “L” in color scale is for high/low intensity of ARPES signal, respectively.
In addition, at deeper energies, various non-dispersive bands emerge in ARPES intensity (Fig. 3g) and the second-derivative (Fig. 3h) plot, namely bands δ1 to δ5 located at the energies of −2.2, −2.8, −3.4, −4.0 and −5.3 eV, respectively. Note that these narrow bands are not appearing in ARPES of bare HOPG surface (Supplementary Fig. 7a), so that they are attributed to THPB-HOF monolayer. Our previous work shows topological flat band40 in 2D HOF self-assembled on Au(111) substrate with large-scale uniformity and long-range order. By employing DFT-based calculations to calculate the band structure of the freestanding THPB-HOF monolayer (Fig. 3f), we find a number of narrow bands appearing in both conduction and valence states, in consistence with our ARPES observation. Among these bands, two topmost sets of valence bands can be identified as two kinds of topological bands with small bandwidth (Fig. 3f, i). One is dual topological flat bands42,43 in THPB-HOF hexagonal lattice. Another is Dirac bands resembling to the case of molecular “graphene”, indicating that the THPB-HOF is effectively a (px, py)-graphene44. The ARPES data and the calculated band structure of THPB-HOF are in a good agreement, despite the binding energy difference of these narrow bands, which is probably caused by the existence of long-range Coulomb in this system45. We also reproduce THPB-HOF on the surface of bilayer graphene (BLG) on SiC substrate. Similar Dirac bands from BLG and narrow bands from THPB-HOF can be observed in ARPES (Supplementary Fig. 16).
DFT calculations of topological flat bands and Dirac bands of THPB-HOF
Topological Dirac bands46,47,48,49,50 and flat bands51,52,53 have been predicted with specific lattice symmetries54,55,56,57, in 2D covalent organic frameworks (COFs)57,58,59 and metal−organic frameworks (MOFs)60,61,62,63,64,65,66. To explore the intrinsic electronic property of THPB-HOF, we performed DFT calculations to obtain its band structure in the freestanding form (see Methods). The geometric structure of THPB-HOF monolayer for DFT calculations is shown in Supplementary Fig. 14, where the experimental lattice constants (a = b = 16.5 Å) are adopted. The calculated band structure in Fig. 3f shows that THPB-HOF is a semiconductor with a large bandgap of 3.28 eV (by local density approximation method) and a series of nearly-flat bands with very narrow dispersion below the Fermi level (EF). Considering the charge transferring between HOPG substrate and THPB-HOF, the EF will locate around the midpoint of the bandgap; as a result, the energy positions of these calculated THPB-HOF bands will appear far below EF, corresponding to the bands δ1 to δ5 in ARPES. One salient feature of these THPB-HOF bands is the narrow bandwidth, especially for valence bands near the Fermi level, which is consistent with nearly non-dispersive bands experimentally observed in the ARPES. Surprisingly, we find that the topmost valence bands are exactly two kinds of topological bands (Fig. 3i), namely, the upper dual topological flat bands and the lower Dirac bands. The former and the latter can be captured by the px,y-orbital and pz-orbital tight-binding (TB) models in the hexagonal lattice respectively. By just considering the nearest-neighbor (NN) hop**, both TB models can well reproduce the DFT results as shown in Fig. 3i, validating the two sets of topological bands. Here, the velocity of Dirac bands is estimated to be 0.252 eV·Å (see Supplementary Fig. 8 for details), much smaller than that of graphene (≈6.6 eV·Å)67. The reduced carrier velocity and narrow bandwidth (0.122 eV) are attributed to the large cell size and weak hop** via hydrogen bonds of THPB-HOF. Narrow electronic energy bands provide an opportunity to explore many-body quantum phases of matter, resulting in a wealth of correlated, topological and broken-symmetry phases. For examples, the upper dual topological flat bands can give rise to exotic collective behaviors in the presence of Coulomb interactions when the bands are partially filled (Supplementary Note 8 and Fig. 10), like the emergence of magnetism and superconductivity in twisted bilayer systems68,69,70.
Tunneling spectra measured on THPB-HOF
The dI/dV spectroscopic measurements, proportional to local density of states, were performed on THPB-HOF at 77 K (Fig. 4a). As shown in Fig. 4b, the dI/dV spectra show a typical V-shaped density-of-state (DOS) with the neutrality point near EF at the locations of hollow sites, as blue-shaded area in Fig. 4c. When the tip approaching on the top of THPB molecule, a prominent DOS peak appears at the energy of +27 meV with the half-peak width of 60 meV in dI/dV spectra. A delicate, line dI/dV spectroscopic survey (Fig. 4d) measured within a unit cell of THPB-HOF along red line marked in Fig. 4a, shows that the emerging DOS peak is highly correlated with THPB-HOF. More interestingly, a double-peak feature appears occasionally, as shown in Fig. 4e, in which two DOS peaks lie at the energies of +16 and +64 meV, respectively, with the energy separation of about 48 meV. The line STS survey (Fig. 4f) also indicates that such double-peak feature is also observed exclusively on THPB molecules.
a Topographic image of THPB self-assembled structure. The image size is 5.5 × 5.5 nm2 with Vb = −1.0 V and It = 20 pA. White dashed diamond indicates a unit cell of THPB-HOF. Red arrow shows the trace of dI/dV spectroscopic survey. b Two representative dI/dV spectrum taken on the hollow sites (blue curve) and on the THPB molecule (red curve), respectively. c The ball-and-stick model shows the hollow sites in the top view. d A dI/dV spectroscopic line survey. e Another set of dI/dV spectrum taken on the THPB molecule with showing a double-peak feature located at +16 and +64 mV, respectively. f A dI/dV spectroscopic line survey with showing the double peaks evolving within the unit cell. All dI/dV spectra were measured with VB = 0.3 V, IT = 200 pA and a bias modulation of 7 mV at the temperature of 77 K.
Such DOS peaks near EF, has been observed previously in the chemisorption of single hydrogen71 or boron72 on graphene, indicating a local magnetic state introduced by removing pz orbitals in π-conjugated carbon systems. Despite pristine graphene is intrinsically nonmagnetic due to its π-conjugated electrons, Lieb73 proposed that the ground state of graphene may possess a total spin given by S = 1/2 × |NA − NB | , where NA and NB are the number of pz orbitals removed from each triangular sublattice. Single magnetic states close to EF can therefore be induced by removing pz orbitals from one of the sublattices74,75,76,77,78. The double occupation of such a magnetic state can be observed as the dual peaks with an energy splitting near EF, owing to Coulomb repulsion U71. In our THPB-HOF, the pz orbitals can be removed by unbalanced molecule-substrate interaction in faulted/unfaulted halves, resembling to two sublattices of graphene. In this regard, the single and double DOS peaks, closed to EF observed on THPB-HOF, could indicate the appearance of single and double-occupied local magnetic states, respectively. The energy separation of ≈48 meV between double peaks in Fig. 4e, is comparable to the 63 meV for boron-doped72 and 21 meV for hydrogen attached graphene71. The LDOS difference between “faulted halves” and “unfaulted halves” in differential conductance maps of THPB-HOF (Supplementary Note 7 and Fig. 9) indicates the interaction between the HOPG substrate and THPB monolayer. The LDOS of magnetic states is more prominent at the THPB molecule in “unfaulted half” and the edges of THPB molecule in “faulted half” than elsewhere, manifesting the internal spatial distribution of spin states for molecules.
In conclusion, large-scale floating HOF/graphene heterostructure has been successfully synthesized via the self-lifting procedure on HOPG surface by UHV molecule deposition. The unique HOF structure and highly dispersive linear bands are charactered by STM and ARPES. A number of non-dispersive bands appear at deeper binding energies, where the two topmost sets of valence bands are attributed to the upper dual topological flat bands and the lower Dirac bands from THPB-HOF lattice. The narrow bandwidth and the reduced carrier velocity are the results of the large cell size and weak hop** via hydrogen bonds. The observed DOS peaks in tunneling spectroscopy manifest the emergence of local magnetic states induced by removing pz orbitals from π-conjugated lattice, similar to the cases of hydrogen or boron chemisorbed graphene.
Methods
Sample preparation and STM/STS characterization
The HOPG substrates were cleaved in UHV to obtain a clean surface before deposition of THPB molecules. THPB molecules were subsequently dosed onto HOPG single-crystal surface held at a temperature of ≈300 K at a base pressure better than 2 × 10−10 Torr. The desired 2D HOF were obtained by maintaining the rate of evaporation of THPB molecules in the range of 0.06–0.07 monolayer (ML) per min and followed with the annealing of 1 h at room temperature.
STM experiments were carried out on an UHV commercial STM system (Unisoku) which can reach a low temperature of 400 mK by using a single-shot 3He cryostat. The base pressure was 2.0 × 10−10 Torr. The THPB samples were deposited at the preparation chamber and then transferred in situ into STM chamber. All the STM measurements were performed at the temperature of 77 K. A commercial Pt−Ir tip was carefully prepared by e-beam heating. The STS and dI/dV map** were obtained by the standard lock-in method by applying an additional small AC voltage with a frequency of 973.0 Hz. The dI/dV spectra were collected by disrupting the feedback loop and swee** the DC bias voltage. WSxM software was used for post processing of all STM data79.
ARPES measurement
The ARPES measurements were performed at the Vacuum Interconnected Nanotech Workstation of Suzhou Institute of Nano-Tech and Nano-Bionics (SINANO) with a ScientaOmicron DA30L analyzer and monochromatized He Iα (hν = 21.218 eV) light source. The samples were grown in situ and measured at T = 77 K (unless otherwise specified) with a background vacuum better than 5 × 10−11 mbar.
In-situ Raman measurement
In-situ Raman measurements were performed by transferring the samples via the UHV tubes (base pressure better than 2 × 10−10 mbar) in Nano-X at room temperature. And the Raman spectra were obtained under the back-scattering geometry by a confocal micro-Raman system (Horiba IHR550 system) with 532 nm excitation.
DFT calculations
Our first-principles DFT calculations were performed with local-density-approximation (LDA)80 using Vienna ab initio Simulation Package81 code. An energy cutoff of 520 eV and a 4 × 4 × 1 Monkhorst–Pack k-point grid were used82. The THPB-HOF monolayer contains 90 atoms per unit cell. For structural optimization calculation of the freestanding THPB-HOF monolayer, we fixed the lattice constants to experimental confirmed values (a = b = 16.5 Å) and only relaxed atomic positions. The structure was optimized until the atomic forces are smaller than 0.001 eVÅ−1 and the change of total energy per cell is smaller than 10−5 eV. For calculations of THPB-HOF on top of graphene and four graphite layers, the structure was fully relaxed without any restriction. To account for the van der Waals interaction, the optB88-vdW method83 was adopted. The energy and force convergence criteria for THPB-HOF/graphene (graphite) were set to 10−4 eV and 0.01 eVÅ−1 respectively.
Data availability
The data that support the findings of this study are available from the corresponding authors upon request. The optimized structure of the THPB-HOF monolayer on top of the eight-layered HOPG substrate (OSHOF/HOPG) Data sets. figshare https://figshare.com/s/4c8ad015173911c5fddc (2024)
References
Geim, A. K. & Novoselov, K. S. The rise of graphene. Nat. Mater. 6, 183–191 (2007).
Novoselov, K. S., Mishchenko, A., Carvalho, A. & Castro Neto, A. H. 2D materials and van der Waals heterostructures. Science 353, aac9439 (2016).
Manzeli, S., Ovchinnikov, D., Pasquier, D., Yazyev, O. V. & Kis, A. 2D transition metal dichalcogenides. Nat. Rev. Mater. 2, 17033 (2017).
Duan, X., Wang, C., Pan, A., Yu, R. & Duan, X. Two-dimensional transition metal dichalcogenides as atomically thin semiconductors: opportunities and challenges. Chem. Soc. Rev. 44, 8859–8876 (2015).
Gupta, A., Sakthivel, T. & Seal, S. Recent development in 2D materials beyond graphene. Prog. Mater. Sci. 73, 44–126 (2015).
Hantanasirisakul, K. & Gogotsi, Y. Electronic and optical properties of 2D transition metal carbides and nitrides (MXenes). Adv. Mater. 30, e1804779 (2018).
Song, L. et al. Large scale growth and characterization of atomic hexagonal boron nitride layers. Nano Lett. 10, 3209–3215 (2010).
Haojie, G., Antonio, J. M. G. & Jose, M. G. R. Self-Guided Growth of Electronically Decoupled C60 on Graphene on Rh(110). Adv. Mater. Interfaces 10, 2202483 (2023).
Xu, R. et al. Unveiling the structural origin of the high carrier mobility of a molecular monolayer on boron nitride. Phys. Rev. B 90, 224106 (2014).
Wang, Q. H. & Hersam, M. C. Room-temperature molecular-resolution characterization of self-assembled organic monolayers on epitaxial graphene. Nat. Chem. 1, 206–211 (2009).
Ojeda-Aristizabal, C. et al. Molecular Arrangement and Charge Transfer in C60/Graphene Heterostructures. ACS Nano 11, 4686–4693 (2017).
He, D. et al. Two-dimensional quasi-freestanding molecular crystals for high-performance organic field-effect transistors. Nat. Commun. 5, 5162 (2014).
Nawaz, A., Merces, L., de Andrade, D. M., de Camargo, D. H. S. & Bof Bufon, C. C. Edge-driven nanomembrane-based vertical organic transistors showing a multi-sensing capability. Nat. Commun. 11, 841 (2020).
Wang, J. et al. Probing the crystallographic orientation of two-dimensional atomic crystals with supramolecular self-assembly. Nat. Commun. 8, 377 (2017).
Takimiya, K., Shinamura, S., Osaka, I. & Miyazaki, E. Thienoacene-based organic semiconductors. Adv. Mater. 23, 4347–4370 (2011).
Khan, J. et al. Recent advances in 2D organic−inorganic heterostructures for electronics and optoelectronics. SmartMat 4, e1156 (2023).
Winkler, C., Harivyasi, S. S. & Zojer, E. Controlling the electronic properties of van der Waals heterostructures by applying electrostatic design. 2D Mater. 5, 035019 (2019).
Pei, K. & Zhai, T. Y. Emerging 2D Organic-Inorganic Heterojunctions. Cell Rep. Phys. Sci. 1, 100166 (2021).
Sun, J. et al. 2D–Organic Hybrid Heterostructures for Optoelectronic Applications. Adv. Mater. 31, 1803831 (2019).
Khan, J. et al. Recent advances in 2D organic−inorganic heterostructures for electronics and optoelectronics. SmartMat 4, e1156 (2022).
Wu, H. et al. All-inorganic perovskite quantum dot-monolayer MoS2 mixed-dimensional van der Waals heterostructure for ultrasensitive photodetector. Adv. Sci. 5, 1801219 (2018).
Li, D. W. et al. Solution-Processed Organic–Inorganic Semiconductor Heterostructures for Advanced Hybrid Phototransistors. ACS Appl. Electron. Mater. 5, 578–592 (2023).
Liu, F. Mechanical exfoliation of large area 2D materials from vdW crystals. Prog. Surf. Sci. 96, 100626 (2021).
Zhou, X. et al. Tunneling diode based on WSe2/SnS2 heterostructure incorporating high detectivity and responsivity. Adv. Mater. 30, 1703286 (2018).
Jariwala, D., Marks, T. J. & Hersam, M. C. Mixed-dimensional van der Waals heterostructures. Nat. Mater. 16, 170–181 (2017).
Cao, Y. et al. Phonon modes and photonic excitation transitions of MoS2 induced by top deposited graphene revealed by Raman spectroscopy and photoluminescence. Appl. Phys. Lett. 114, 133103 (2019).
Liu, H. et al. Van der Waals epitaxial growth of vertically stacked Sb2Te3/MoS2 p–n heterojunctions for high performance optoelectronics. Nano Energy 59, 66–74 (2019).
Yang, J. & Yan, D. Weak epitaxy growth of organic semiconductor thin films. Chem. Soc. Rev. 38, 2634–2645 (2009).
Li, W. et al. Uniform and ultrathin high-k gate dielectrics for two-dimensional electronic devices. Nat. Electron. 2, 563–571 (2019).
Chen, X. et al. Improving the performance of graphene phototransistors using a heterostructure as the light-absorbing layer. Nano Lett. 17, 6391–6396 (2017).
Liu, X. et al. Photoresponse of an organic semiconductor/two-dimensional transition metal dichalcogenide heterojunction. Nano Lett. 17, 3176–3181 (2017).
He, X. et al. Selective self-assembly of 2,3-diaminophenazine molecules on MoSe2 mirror twin boundaries. Nat. Commun. 10, 2847 (2019).
Kim, S. Y., Kwak, J. S., Ciobanu, C. V. & Kwon, S. Y. Recent Developments in Controlled Vapor-Phase Growth of 2D Group 6 Transition Metal Dichalcogenides. Adv. Mater. 31, 20 (2019).
Zhao, B. L. et al. 2D van der Waals Heterojunction of Organic and Inorganic Monolayers for High Responsivity Phototransistors. Adv. Funct. Mater. 31, 42 (2021).
Zhou, Y., Sethi, G., Liu, H., Wang, Z. & Liu, F. Excited quantum anomalous and spin Hall effect: dissociation of flat-bands-enabled excitonic insulator state. Nanotech 33, 415001 (2022).
Splendiani, A. et al. Emerging photoluminescence in monolayer MoS2. Nano Lett. 10, 1271–1275 (2010).
Mak, K. F., Lee, C., Hone, J., Shan, J. & Heinz, T. F. Atomically thin MoS2: a new direct-gap semiconductor. Phys. Rev. Lett. 105, 136805 (2010).
Qing, L. et al. Surface-Controlled Mono/Diselective ortho C−H Bond Activation,. J. Am. Chem. Soc. 138, 2809–2814 (2016).
Antonela et al. Some Pictures of Alcoholic Dancing: From Simple to Complex Hydrogen-Bonded Networks Based on Polyalcohols. J. Phys. Chem. C. 117, 4680–4690 (2013).
Pan, M. H. et al. Growth of Mesoscale Ordered Two-Dimensional Hydrogen-Bond Organic Framework with the Observation of Flat Band. Phys. Rev. Lett. 130, 036203 (2023).
Zhou, S. et al. First direct observation of Dirac fermions in graphite. Nat. Phys. 2, 595–599 (2006).
Wu, C. J., Bergman, D., Balents, L. & Sarma, S. D. Flat Bands and Wigner Crystallization in the Honeycomb Optical Lattice. Phys. Rev. Lett. 99, 070401 (2007).
Liu, H., Sethi, G., Meng, S. & Liu, F. Orbital design of flat bands in non-line-graph lattices via line-graph wave functions. Phys. Rev. B 105, 085128 (2022).
Wu, C. J. & Sarma, S. D. px,y-orbital counterpart of graphene: Cold atoms in the honeycomb optical lattice. Phys. Rev. B 77, 235107 (2008).
Wen, C. H. P. et al. Unveiling the Superconducting Mechanism of Ba0.51K0.49BiO3. Phys. Rev. Lett. 121, 117002 (2018).
Gutzler, R. & Perepichka, D. F. π-Electron conjugation in two dimensions. J. Am. Chem. Soc. 135, 16585 (2013).
Gutzler, R. Band-structure engineering in conjugated 2D polymers. Phys. Chem. Chem. Phys. 18, 29092 (2016).
Adjizian, J.-J. et al. Dirac Cones in two-dimensional conjugated polymer networks. Nat. Commun. 5, 5842 (2014).
Alcon, I. et al. Existence of multi-radical and closed-shell semiconducting states in post-graphene organic Dirac materials. Nat. Commun. 8, 1957 (2017).
**g, Y. & Heine, T. Two-dimensional kagome lattices made of hetero triangulenes are Dirac semimetals or single-band semiconductors. J. Am. Chem. Soc. 141, 743 (2019).
Zhu, P. & Meunier, V. Electronic properties of two-dimensional covalent organic frameworks. J. Chem. Phys. 137, 244703 (2012).
Liu, Z., Liu, F. & Wu, Y.-S. Exotic electronic states in the world of flat bands: From theory to material. Chin. Phys. B 23, 077308 (2014).
Barreteau, C., Ducastelle, F. & Mallah, T. A bird’s eye view on the flat and conic band world of the honeycomb and Kagome lattices: Towards an understanding of 2D metal-organic frameworks electronic structure. J. Phys.: Condens. Matter 29, 465302 (2017).
Thomas, S. et al. Electronic Structure of Two-Dimensional π-Conjugated Covalent Organic Frameworks. Chem. Mater. 31, 3051–3065 (2019).
Rizzo, D. J. et al. Revealing the Local Electronic Structure of a Single-Layer Covalent Organic Framework through Electronic Decoupling. Nano Lett. 20, 963–970 (2020).
Jiang, W., Huang, H. & Liu, F. A Lieb-like lattice in a covalent-organic framework and its Stoner ferromagnetism. Nat. Commun. 10, 2207 (2019).
Cui, B. et al. Realization of Lieb lattice in covalent-organic frameworks with tunable topology and magnetism. Nat. Commun. 11, 66 (2020).
Zhang, L. Z. et al. Intrinsic Two-Dimensional Organic Topological Insulators in Metal-Dicyanoanthracene Lattices. Nano Lett. 16, 2072 (2016).
Ni, X., Li, H., Liu, F. & Bredas, J.-L. Engineering of flat bands and Dirac bands in two-dimensional covalent organic frameworks (COFs): relationships among molecular orbital symmetry, lattice symmetry, and electronic-structure characteristics. Mater. Horiz. 9, 88 (2022).
Wang, Z. F., Liu, Z. & Liu, F. Organic topological insulators in organometallic lattices. Nat. Commun. 4, 1471 (2013).
Liu, Z., Wang, Z.-F., Mei, J.-W., Wu, Y.-S. & Liu, F. Flat Chern Band in a Two-Dimensional Organometallic Framework. Phys. Rev. Lett. 110, 106804 (2013).
Wang, Z. F., Su, N. & Liu, F. Prediction of a two-dimensional organic topological insulator. Nano Lett. 13, 2842 (2013).
Gao, Y. et al. Quantum anomalous Hall effect in two-dimensional Cu-dicyanobenzene coloring-triangle lattice. Nano Res 13, 1571–1575 (2020).
Ni, X., Zhou, Y., Sethi, G. & Liu, F. p-Orbital Yin–Yang Kagome bands in anilato-based metal–organic frameworks. Phys. Chem. Chem. Phys. 22, 25827 (2020).
Zhou, Y., Sethi, G., Zhang, C., Ni, X. & Liu, F. Giant intrinsic circular dichroism of enantiomorphic flat Chern bands and flatband devices. Phys. Rev. B 102, 125115 (2020).
Jiang, W., Ni, X. & Liu, F. Exotic Topological Bands and Quantum States in Metal-Organic and Covalent-Organic Frameworks. Acc. Chem. Res. 54, 416 (2021).
Feng, B. J. et al. Dirac Fermions in Borophene. Phys. Rev. Lett. 118, 096401 (2017).
Cao, Y. et al. Correlated insulator behaviour at half-filling in magic-angle graphene superlattices. Nature 556, 80–84 (2018).
Cao, Y. et al. Unconventional superconductivity in magic-angle graphene superlattices. Nature 556, 43–50 (2018).
Aaron et al. Emergent ferromagnetism near three-quarters filling in twisted bilayer graphene. Science 365, 605–608 (2019).
Gonzalez-Herrero, H. et al. Atomic-scale control of graphene magnetism by using hydrogen atoms. Science 352, 437–439 (2016).
Qing, L. et al. Locally Induced Spin States on Graphene by Chemical Attachment of Boron Atoms. Nano Lett. 18, 5482–5487 (2018).
Lieb, E. H. Two theorems on the Hubbard model. Phys. Rev. Lett. 62, 1201–1204 (1989).
Yazyev, O. V. & Helm, L. Defect-induced magnetism in graphene. Phys. Rev. B 75, 125408 (2007).
Fernández-Rossier, J. & Palacios, J. J. Magnetism in graphene nano-islands. Phys. Rev. Lett. 99, 177204 (2007).
Palacios, J. J., Fernández-Rossier, J. & Brey, L. Electronic structure of gated graphene and graphene ribbons. Phys. Rev. B 77, 195428 (2008).
Yazyev, O. V. Emergence of magnetism in graphene materials and nanostructures. Rep. Prog. Phys. 73, 056501 (2010).
Pereira, V. M., Guinea, F., Lopes dos Santos, J. M. B., Peres, N. M. R. & Castro Neto, A. H. Disorder Induced Localized States in Graphene. Phys. Rev. Lett. 96, 036801 (2006).
Horcas, I. et al. WSXM: a software for scanning probe microscopy and a tool for nanotechnology. Rev. Sci. Instrum. 78, 013705 (2007).
Perdew, J. P. & Zunger, A. Self-interaction correction to density-functional approximations for many-electron systems. Phys. Rev. B 23, 5048 (1981).
Kresse, G. & Furthmüller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169 (1996).
Methfessel, M. & Paxton, A. T. High-precision sampling for Brillouin-zone integration in metals. Phys. Rev. B 40, 3616 (1989).
Klimeš, J. et al. Chemical accuracy for the van der Waals density functional. J. Phys. Condens. Matter 22, 022201 (2010).
Acknowledgements
Sample growth and ARPES measurements were conducted at the Vacuum Interconnected Nanotech Workstation (Nano-X) in SINANO, Suzhou. STM work was conducted at School of Physics, Huazhong University of Science and Technology in Wuhan. The calculation was done on the CHPC at the University of Utah and US-DOE-NERSC. X.Z, M.H.P. and F.-S.L. acknowledge financial support from the National Natural Science Foundation of China (22372096, 11574095, 91745115, 22102129 and 12134008). X.Y.L. and F.L. acknowledge financial support from DOE-BES (No. DE-FG02-04ER46148). F.-S.L. also acknowledge financial support from the Suzhou Science and Technology Program (Grant No. SJC2021009) and the Youth Innovation Promotion Association of Chinese Academy of Sciences (2017370). J.Z.G. acknowledge the support program for young top-notch talents in Shaanxi Province (1511000066) and the National Development and Reform Commission (NDRC) of the People's Republic of China special subsidy for the preliminary work of the Western Development. X.L. acknowledges also the National Science Foundation (No. 2326228).
Author information
Authors and Affiliations
Contributions
X. Zhang, X. Y. Li, Z. W. Cheng, A. X. Chen and P. D. Wang contributed equally to this work. F.-S. Li, F. Liu and M. H. Pan conceived and designed the experiment. X. Zhang, Q. Bian and X. Y. Wang grew the samples. Z. W. Cheng, S. J. Li, B. Qi and J. Gao performed the STM experiments. A. X. Chen, X. X. Lei, P. D. Wang and F.-S. Li performed the ARPES measurements. X. Y. Li carried out the calculations. B. K. Yuan performed the measurement on MoS2 substrate. M. H. Pan and F. Liu wrote the manuscript with inputs from all other authors.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Peer review
Peer review information
Nature Communications thanks Libo Gao, Bilu Liu and the other, anonymous, reviewer(s) for their contribution to the peer review of this work. A peer review file is available.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Zhang, X., Li, X., Cheng, Z. et al. Large-scale 2D heterostructures from hydrogen-bonded organic frameworks and graphene with distinct Dirac and flat bands. Nat Commun 15, 5934 (2024). https://doi.org/10.1038/s41467-024-50211-5
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-024-50211-5
- Springer Nature Limited