Abstract
(La1−xGdx)0.94PO4:Tb0.06 (0 ≤ x ≤ 1.0) green phosphors were synthesized by an ultrasonic spray pyrolysis process. The annealed (La1−xGdx)0.94PO4:Tb0.06 phosphors exhibited the formation of a single-phase oxide with the monoclinic monazite structure. Higher Gd3+ content yielded a smaller lattice parameter. The phosphors emitted green light due to the 5D4→7FJ (J = 3, 4, 5, and 6) transition of Tb3+ at 489 nm, 543 nm, 585 nm, and 621 nm, respectively. The predominant peak at 543 nm was nearly a single peak, which was responsible for the green color emission. Among the (La1−xGdx)0.94PO4:Tb0.06 phosphors, the strongest emission intensity was obtained for (La0.25Gd0.75)0.94PO4:Tb0.06.
Similar content being viewed by others
References
R. P. Rao and D. J. Devine, J. Lumin. 87, 1260 (2000).
C. J. Kim and M. S. Kwon, Electronic Materials Letters 5(3), 113 (2009).
W. Di, X. Wang, B. Chen, H. Lai, and X. Zhao, Optical Materials 27, 1386 (2005).
Y. Wang, C. Wu, and J. Wei, J. Lumin. 126, 503 (2007).
T. Jüstel, J.-C. Krupa, and D. U. Wiechert, J. Lumin. 93, 179 (2001).
X. Wu, H. You, H. Cui, X. Zeng, G. Hong, C.-H. Kim, C.-H. Pyun, B.-Y. Yu, and C.-H. Park, Mater. Res. Bull. 37, 1531 (2002).
C. Wu, Y. Wang, and W. Jie, J. Alloys Compd. 436, 383 (2007).
U. Rambabu, N. R. Munirathnam, T. L. Prakash, and S. Buddhudu, Mater. Chem. Phys. 78, 160 (2002).
D. Wang and Y. Wang, Mater. Res. Bull. 42, 2163 (2007).
W. D. Kingery, H. K. Bowen, and D. R. Uhlmann, Introduction to Ceramics, 2nd ed, John Wiely and Sons, New York (1976).
M. E. G. Valerio, V. G. Ribeiro, A. C. S. de Mello, M. A. C. dos Santos, S. L. Baldochi, V. L. Mazzocchi, C. B. R. Parente, R. A. Jackson, J. B. Amaral, Optical Materials 30, 184 (2007).
H.-S. Nalwa and L. S. Rohwer, Handbook of Luminescence, Display Materials, and Devices, American Scientific Publishers, California (2003).
Z.-J. Zhang, J.-L. Yuan, S. Chen, H.-H. Chen, X.-X. Yang, J.-T. Zhao, G.-B. Zhang, and C.-S. Shi, Optical Materials 30, 1848 (2008).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Park, K., Kim, K.Y. VUV photoluminescence of La1−xGdxPO4:Tb3+ green phosphors synthesized by ultrasonic spray pyrolysis. Met. Mater. Int. 17, 797–800 (2011). https://doi.org/10.1007/s12540-011-1016-0
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12540-011-1016-0