Abstract
Using methyl methacrylate (MMA), butyl acrylate(BA) and hexafluorobutyl acrylate(HFBA) as main raw materials, we prepared self-crosslinked fluorocarbon polymer emulsion with core-shell structure via soap-free emulsion polymerization when the conception of particle design and polymer morphology was adopted. Moreover, the influence of mole ratio of BA to MAA, pH value on the oligomer was studied. And the effects of the added amount of oligomer, self-crosslinked monomer and HFBA, mass ratio of BA to MMA, reaction temperature and the initiator on the polymerization technology and the performance of the product, were investigated and optimized. The structure and performance of the fluorocarbon polymer emulsion were characterized and tested with FTIR, TEM, MFT and contact angle and water absorption of the latex film. The experimental results show that the optimal conditions for preparing fluorocarbon polymer emulsion are as follows: for preparing the oligomer, mol ratio of BA to MAA is equal to 1.0: 1.60, and pH value is controlled within the range of 8.0 and 9.0; for preparing fluorocarbon polymer emulsion, the added amount of oligmer[P(BA/MANa)] is 6%; mass ratio of BA to MMA is 40: 60; the added amount of self-crosslinked monomer is 2%, the added amount of HFBA is 15%; reaction temperature is 80 °C; the mixture of potassium persulfate and sodium bisulfite is used as the initiator. The film-forming stability of the fluorocarbon polymer emulsion and the performance of the latex film, which is prepared with the soap-free emulsion polymerization, are better than that prepared with the conventional emulsion polymerization.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
BARRY R. New Technology Offers a Green Light to Develop Better Coatings[J]. Paint & Coatings Industry, 2002, 18(11): 68–72
YAMAUCHI M, HIRONO J, KODAMA S. The Evaluation of New Fluoropolymer Emulsion for Exterior Paint Use [J]. Surface Coatings International, 1996, 79(7): 312–318
CAO Xue-qin, LI Zhan-xiong, CHEN Guo-qiang. Preparation and Application on Fabrics of Fluorinated Acrylic Copolymer Emulsion[J]. Fine Chemicals, 2006, 23(12): 1194–1197(in Chinese)
ALESSANDRINI G, AGLIETTO M, CASTELVETRO V, et al. Comparative Evaluation of Fluorinated and Unfluorinated Acrylic Copolymers as Water-repellent Coating Materials for Stone[J]. Journal of Applied Polymer Science, 2000, 76(6): 962–977
ZHOU Yu-ming, XU Qun-hua, HUANG **g-yan. Preparation and Surface Properties of Perfluoroalkylethyl Acrylate Copolymer [J]. Chemical Journal of Chinese Universities, 2001, 22(12): 2126–2127(in Chinese)
CHENG Shi-yuan, CHEN Yan-jun, WANG Kang-li. The Study of the Acrylate Copolymer Emulsion Containing Fluorine[J]. Acta Polymerica Sinica, 2002(5): 560–565(in Chinese)
ZHAO **ng-shun, DING **ao-bin, ZHANG Jun-hua, et al. Preparation and Surface Properties of Acrylate Copolymer Latex Containing Fluorine[J]. Aata Polymerica Sinica, 2004 (2): 196–200 (in Chinese)
GAO **-zhang, WANG Xue-mei, WEI Yun-xia, et al. Synthesis and Characterization of a Novel Fluorine-containing Polymer Emulsion with Core/shell Structure [J]. Journal of Fluorine Chemistry, 2006, 127: 282–286
KANG Kai, KAN Cheng-you, DU Yi, et al. Synthesis and Properties of Soap-free Poly(methyl methacrylate-ethyl acrylate-methacrylic acid) Latex Particles Prepared by Seeded Emulsion Polymerization[J]. European Polymer Journal, 2005, 41(3): 439–445
GUO Lin-hui, MA Cheng-yin, CHEN Hong-mei. Emulsifier-free Emulsion Polymerization Theoretical Research, Preparation Methods and Application[J]. Chemical Word, 2003, (1): 49–52(in Chinese)
WANG **-gang, ZHU **ao-li, ZHANG Zhi-guo, et al. Soap-free Emulsion Copolymerization of Methyl Methacrylate Butyl Acrylate with Sodium A-olefinsulfonates Functional Monomer[J]. Acta Polymerica Sinica, 2006, (7): 903–907(in Chinese)
YUE Qing-lei, ZHOU Wen-hua, PAN Zhan-chang. Research Progress in Soap-free Emulsion Polymerization[J]. Fine Chemicals, 2003, 20(12): 766–768(in Chinese)
TONG Guo-zhong. Modern Coatings Instrument Analysis [M]. Bei**g: Chemical Industry Press, 2006: 139–144(in Chinese)
HONG **ao-yin, FENG Han-bao. Chemistry of Coatings [M]. 2nd Edition. Bei**g: Science Press, 2005: 15–22 (in Chinese)
HA J W, PARK I J, KIM D K, et al. Surface Properties of Core-shell Particles Containing Perfluoroalkyl Acrylate in Shell[J]. Surface Science, 2003, 532–535: 228–233
CAO Tong-yu, LIU Qing-pu, HU **-sheng. Synthetic Mechanism, Performance and Application of Polymer Latex [M]. Bei**g: Chemical Industry Press, 1997: 225–227(in Chinese)
LI Zheng-min, YANG **g-he, YU Yuang-zhang, et al. Morphological Characterization of the Core-shell Latex Particle by Transmission Electron Microscopy and Image Analysis[J]. Journal of Applied Polymer Science, 2003, 89(3): 855–861