Abstract
The combination of mechanical work by powder-in-tube processing and melt growth of YBa2Cu3O7-δ was investigated. During the heat treatment of Ag-sheathed YBa2Cu3O7-δ wire above the melting point of Ag, the sheath was melted and removed from the superconducting wire, but a small portion of Ag infiltrated into the core. Mechanical working before the heat treatment is beneficial for improvingJ c. Heat treatments above 1015°C resulted in higherJ c values for drawn wires than the samples without mechanical working. A proper combination of mechanical working and melt growth appears very promising for making high-J c wire with good strength.
Similar content being viewed by others
References
P. CHAUDHARI, J. MANNHART, D. DIMOS, C. C. TSUEI, J. CHI, M. M. OPRYSKO and M. SCHEUERMANN,Phys. Rev. Lett. 60 (1988) 1653.
D. DIMOS, P. CHAUDHARI, J. MANNHART and F. K. LeGOUES, ibid.61 (1988) 219.
S. JIN, T. H. TIEFEL, R. C. SHERWOOD, M. E. DAVIS, R. B. VAN DOVER, G. W. KAMMLOTT, R. H. FASTNACHT and H. D. KEITH,Appl. Phys. Lett. 52 (1988) 2074.
K. SALAMA, V. SELVAMANICKAM, L. GAO and K. SUN, ibid.54 (1989) 2352.
T. H. TIEFEL, S. JIN, R. C. SHERWOOD, M. E. DAVIS, G. W. KAMMLOTT, P. K. GALLAGER, D. W. JOHNSON, Jr, R. A. FASTNACHT and W. W. RHODES,Mater. Lett. 7 (11) (1989) 363.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Ahn, JH., Ha, KH. & Chung, H. Combined processing of YBa2Cu3O7-δ superconducting wire by mechanical work and melt growth technique. J Mater Sci: Mater Electron 2, 94–97 (1991). https://doi.org/10.1007/BF00694758
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00694758